Method for preparing improved expanded polystyrene sheet
Assignee: Lyondell Chemical Technology LP
•
Filing: 1975-12-31
•
Granted: 1977-09-13
•
Expires: 1995-12-31
Abstract
Abstract Expanded styrene polymer sheet material is produced by extruding expandable and/or general purpose styrene polymer with a conventional blowing agent, a nucleating system and small amounts of finely divided hydrophilic silicon dioxide and alkaline earth metal oxide. The resulting product has very fine, uniformly sized pores and improved flexibility.
Inventors
- 👤 John P. Spicuzza, Jr.
- 👤 Joseph M. Sutej
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:15
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0066; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/34; C08K3/36; C08J2325/00; C08J2325/02; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/13; Y10S264/17
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
90 words
In a process for producing microcellular expanded styrene polymer sheet by extruding a mixture containing styrene polymer, a blowing agent and a nucleating system, the improvement comprising extruding with said mixture about 0.002 to 2% of a hydrophilic silica and about 0.002 to 2% of an alkaline earth metal oxide, the percentages of hydrophilic silica and alkaline earth metal oxide being based on the total weight of styrene polymer and said hydrophilic silica and alkaline earth metal oxide being uniformly distributed throughout said mixture whereby said sheet has improved flexibility.
Claim 2
Dependent Claim
90 words
In a process for producing microcellular expanded styrene polymer sheet by extruding a mixture containing styrene polymer, a blowing agent and a nucleating system, the improvement comprising extruding with said mixture about 0.002 to 2% of a hydrophilic silica and about 0.002 to 2% of an alkaline earth metal oxide, the percentages of hydrophilic silica and alkaline earth metal oxide being based on the total weight of styrene polymer and said hydrophilic silica and alkaline earth metal oxide being uniformly distributed throughout said mixture whereby said sheet has improved flexibility.
Claim 3
Dependent Claim
29 words
The improved process of claim 1 wherein the alkaline earth metal oxide is selected from the group consisting of magnesium oxide, calcium oxide, barium oxide, and mixtures of these.
Claim 4
Dependent Claim
28 words
The improved process of claim 2 wherein said hydrophilic silica and alkaline earth metal oxide are blended with the styrene polymer before it is fed into the extruder.
Claim 5
Dependent Claim
27 words
The improved process of claim 2 wherein said hydrophilic silica and alkaline earth metal oxide are added to the styrene polymer in the barrel of the extruder.
Claim 6
Dependent Claim
34 words
The improved process of claim 2 wherein the amounts of hydrophilic silica and alkaline earth metal oxide extruded with said mixture are about 0.01 to 0.5%, based on the total weight of styrene polymer.
Claim 7
Dependent Claim
16 words
The improved process of claim 1 wherein expandable polystyrene materials are used in forming said mixture.
Claim 8
Dependent Claim
39 words
The improved process of claim 2 wherein a portion of the styrene polymer is general purpose polystyrene and a portion of the blowing agent is injected into the molten polymer while it is in the barrel of the extruder.
Claim 9
Dependent Claim
33 words
The improved process of claim 2 wherein the styrene polymer is general purpose polystyrene and the blowing agent is injected into the molten polymer while it is in the barrel of the extruder.
Claim 10
Dependent Claim
15 words
The improved process of claim 2 wherein the alkaline earth metal oxide is magnesium oxide.
Claim 11
Dependent Claim
95 words
A process of extruding expanded styrene polymer sheet having a small and uniform cell size from styrene polymer feedstock comprising extruding a mixture comprised of the styrene polymer, about 3-10% blowing agent, about 0.01 to 5% nucleating system, about 0.002 to 2% hydrophilic silica having an average particle size of about 1 to 100 millimicrons, and about 0.002 to 2% of an alkaline earth metal oxide selected from the group consisting of magnesium oxide, calcium oxide, barium oxide, and mixtures of these, said percentages being based on the total weight of styrene polymer being extruded.
Claim 12
Dependent Claim
95 words
A process of extruding expanded styrene polymer sheet having a small and uniform cell size from styrene polymer feedstock comprising extruding a mixture comprised of the styrene polymer, about 3-10% blowing agent, about 0.01 to 5% nucleating system, about 0.002 to 2% hydrophilic silica having an average particle size of about 1 to 100 millimicrons, and about 0.002 to 2% of an alkaline earth metal oxide selected from the group consisting of magnesium oxide, calcium oxide, barium oxide, and mixtures of these, said percentages being based on the total weight of styrene polymer being extruded.
Claim 13
Dependent Claim
64 words
The process of claim 10 wherein said blowing agent, nucleating system, hydrophilic silica and alkaline earth metal oxide are present in amounts of about 5 to 7%, about 0.05 to 3%, about 0.01 to 0.5% and about 0.01 to 0.5%, respectively, based on the total weight of styrene polymer and said hydrophilic silica has an average particle size of about 2 to 50 millimicrons.
Claim 14
Dependent Claim
40 words
The process of claim 11 wherein the styrene polymer is polystyrene, the blowing agent is pentane, the nucleating system is comprised of an organic acid and alkali or alkaline earth metal carbonate, and the hydrophilic silica is hydrophilic fumed silica.
Claim 15
Dependent Claim
17 words
The process of claim 12 wherein the nucleating system is comprised of citric acid and sodium bicarbonate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-12 | 1981-03-14 | 1981-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-12 | 1985-03-14 | 1985-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-12 | 1989-03-14 | 1989-09-13 | $7700.00 | Window Closed / Lapsed |