Slimes treatment process
Assignee: Noranda Inc
•
Filing: 1975-06-13
•
Granted: 1977-09-13
•
Expires: 1995-06-13
Abstract
Abstract Slimes from electrolytic copper refinery are first treated by leaching them with dilute sulphuric acid under an oxygen partial pressure of up to 50 psi and an elevated temperature, until copper and tellurium present in the slimes are substantially dissolved, and effecting a liquid-solid separation of the leached slurry so produced to separate the leach liquor from the leach slimes. The leach liquor is then treated with metallic copper to cement the tellurium as copper telluride. The latter is separated from the remaining solution which is suitable for the production of copper sulphate. The leach slimes containing mainly selenium, lead, silver, gold and other impurities are dried, mixed with a binder and pelletized and the pellets are then roasted to remove selenium as selenium dioxide. Finally, the roasted pellets are smelted to remove the remaining impurities leaving a dore metal containing essentially silver and gold.
Inventors
- 👤 Bernard H. Morrison
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:48
CPC Classifications
C; C22; C22B; C22B11/00; C01; C01B; C01B19/00; C01B19/007; C01G; C01G3/00; C01G3/10; C22B1/00; C22B1/14; C22B1/24; C22B1/2406; C22B7/00; C22B7/001; C22B7/006; C22B7/007; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
113 words
A method of treating slimes from the electrolytic refining of copper comprising: a. leaching said slimes with dilute sulphuric acid under an oxygen partial pressure of up to 50 psi and at an elevated temperature between about 180° and 320° F until copper and tellurium in said slimes are substantially dissolved, thereby forming a leach slurry; b. effecting a liquid-solid separation on said leach slurry to separate leach liquor from the solid leach slimes; c. treating said leach liquor with metallic copper to cement the tellurium as copper telluride and form a remaining solution suitable for the production of copper sulphate; and d. separating the cemented copper telluride solids from said solution. gold.
Claim 2
Independent Claim
113 words
A method of treating slimes from the electrolytic refining of copper comprising: a. leaching said slimes with dilute sulphuric acid under an oxygen partial pressure of up to 50 psi and at an elevated temperature between about 180° and 320° F until copper and tellurium in said slimes are substantially dissolved, thereby forming a leach slurry; b. effecting a liquid-solid separation on said leach slurry to separate leach liquor from the solid leach slimes; c. treating said leach liquor with metallic copper to cement the tellurium as copper telluride and form a remaining solution suitable for the production of copper sulphate; and d. separating the cemented copper telluride solids from said solution. gold.
Claim 3
Dependent Claim
22 words
Method according to claim 1, wherein the oxygen partial pressure used during leaching of the slimes is between 20 and 50 psi.
Claim 4
Dependent Claim
23 words
Method according to claim 1, wherein the temperature used during the leaching of the slimes is between about 200 ° and 300° F.
Claim 5
Dependent Claim
25 words
Method according to claim 1, wherein the initial concentration of the sulphuric acid used for the leaching is between about 250 gpl and 300 gpl.
Claim 6
Dependent Claim
31 words
Method as claimed in claim 1, in which the liquid-solid if the leach slurry is effected by means of a filter press and the solids are further washed with warm water.
Claim 7
Dependent Claim
62 words
Method as claimed in claim 1, wherein the leach liquor resulting from the liquid-solid separation is treated with metallic copper in the form of fine copper shot in a rotating cylindrical horizontally disposed cementation reactor provided with internal baffles to achieve suitable intermixing of the copper shot with the leached liquor during treatment, said reactor being sligthly inclined toward its feed end.
Claim 8
Dependent Claim
22 words
Method according to claim 6, in which the cementation operation is carried out at a temperature of between 150° and 200° F.
Claim 9
Dependent Claim
67 words
The method of claim 1 wherein said leach slimes containing selenium, gold, silver and other impurities and are treated by: a. drying said leach slimes; b. mixing said leach slimes with a binder; c. pelletizing said binder containing leach slimes; d. roasting said pellets to remove selenium therefrom; and e. smelting said roasted pellets to remove remaining impurities to form dore metal, containing essentially silver and gold.
Claim 10
Dependent Claim
58 words
Method according to claim 8 wherein the leached wet slimes containing about 25% moisture are dried by means of a steam heated roller drierhaving two chromium plated stainless steel rollers positioned face to face so that the wet slimes being fed into the nip of said rollers are pressed thereby to produce substantially dry material suitable for pelletization.
Claim 11
Dependent Claim
23 words
Method according to claim 8, wherein the binder is bentonite and it is added in a proportion of between about 5 and 10%.
Claim 12
Dependent Claim
34 words
Method according to claim 8, wherein the pellets are roasted at a temperature of between 1,200°-1,500° F with an air flow of 30 to 60 cfm during a period of 1 to 2 hours.
References Cited (Backward Citations)
US2039256A
Cited
US3627486A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-12 | 1981-03-14 | 1981-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-12 | 1985-03-14 | 1985-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-12 | 1989-03-14 | 1989-09-13 | $7700.00 | Window Closed / Lapsed |