Method of compounding thermo-plastic polymeric materials and fillers
Assignee: Vulkor Inc
•
Filing: 1974-07-29
•
Granted: 1977-08-30
•
Expires: 1994-07-29
Abstract
Abstract A method of compounding thermoplastic polymeric material and fillers, including additives and agents, and unique compounded products. The compounding method comprises mixing the thermoplastic polymeric material in particulate form with particulate filler, and in progressive sequence melting the surface portion of the thermoplastic particles, blending the filler with said molten surface portion of the thermoplastic particles and removing the resultant blended melt and filler from the surface of the thermoplastic particles. The mixing and melting, and the blending and removing, are continued until the filler is substantially assimilated into the polymeric material and the thermoplastic particles become substantially diminished by melting and blending, or the method can be carried further if desired. The compounded product thus prepared is characterized by a distinctive stratified consistency.
Inventors
- 👤 Ray C. Lever
- 👤 Edward V. Wilkus
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:40
CPC Classifications
B; B29; B29B; B29B9/00; B29B9/02; B29B7/00; B29B7/80; B29B7/88; B29B7/90; B29B9/12; C; C08; C08J; C08J3/00; C08J3/20; C08J3/203; C08K; C08K9/00; C08K9/10; B29C; B29C2791/00; B29C2791/001; B29K; B29K2105/00; B29K2105/06; B29K2105/16
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
250 words
The method of compounding thermoplastic polymeric material and filler, comprising the steps of: a. mixing particles of thermoplastic polymeric material with particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the polymeric material while melting surface portions of the particles of polymeric material, whereby the filler is blended with the melting surface portions of said polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the polymeric particles by the mixing action; and, b. continuing both the mixing of the particles of thermoplastic polymeric material with the filler and the melting of surface portions of said particles with the resulting blending of the melting surface portions and filler and the removal of the resultant blend of melted polymeric material and filler from said particles of polymeric material to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polyeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of filler adhesively embraced by a film-like mass of polymeric material.
Claim 2
Independent Claim
250 words
The method of compounding thermoplastic polymeric material and filler, comprising the steps of: a. mixing particles of thermoplastic polymeric material with particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the polymeric material while melting surface portions of the particles of polymeric material, whereby the filler is blended with the melting surface portions of said polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the polymeric particles by the mixing action; and, b. continuing both the mixing of the particles of thermoplastic polymeric material with the filler and the melting of surface portions of said particles with the resulting blending of the melting surface portions and filler and the removal of the resultant blend of melted polymeric material and filler from said particles of polymeric material to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polyeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of filler adhesively embraced by a film-like mass of polymeric material.
Claim 3
Dependent Claim
31 words
The method of compounding thermoplastic polymeric material and filler of claim 1, wherein the filler mixed with the polymeric material is of a relatively smaller particle size than the polymeric material.
Claim 4
Dependent Claim
40 words
The method of compounding thermoplastic polymeric material and filler of claim 1, wherein the amount of filler mixed with the polymeric material is approximately 25 to approximately 200 parts by weight per 100 parts by weight of the polymeric material.
Claim 5
Dependent Claim
19 words
The method of compounding thermoplastic polymeric material and filler of claim 2, wherein the filler is finely divided powder.
Claim 6
Dependent Claim
54 words
The method of compounding thermoplastic polymeric material and filler of claim 4, wherein the particles of polymeric material are sized substantially within the range of approximately 2 to approximately 8 millimeters in diameter and the particles of filler are sized substantially within the range of approximately 149 microns to approximately 37 microns in diameter.
Claim 7
Dependent Claim
40 words
The method of compounding thermoplastic polymeric material and filler of claim 1, wherein the mixing of the polymeric material and filler is continued until the mix thereof coalesces into a soft mass which upon cooling hardens into a friable mass.
Claim 8
Dependent Claim
29 words
The method of compounding thermoplastic polymeric material and filler of claim 6, wherein the coalesced and cooled friable mass of mixed polymeric material and filler is broken into particles.
Claim 9
Dependent Claim
61 words
The method of compounding thermoplastic polymeric material and filler of claim 7, wherein the steps of mixing until the polymeric material and filler coalesces into a soft mass and cooling to a friable mass and then breaking the coalesced and cooled friable mass into particles of compound, are repeated until the resultant compound of polymeric material and filler is substantially homogeneous.
Claim 10
Dependent Claim
35 words
The method of compounding thermoplastic polymeric material and filler of claim 1, wherein the compound of polymeric material and filler is cooled, and a cross-linking curing agent is added to and dispersed throughout the compound.
Claim 11
Dependent Claim
20 words
The method of compounding thermoplastic polymeric material and filler of claim 9, wherein the cross-linking curing agent is a peroxide.
Claim 12
Independent Claim
277 words
The method of compounding thermoplastic polymeric material with filler, comprising the steps of: a. mixing with high energy and high velocity particles of thermoplastic polymeric material and particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the polymeric material, and heating the surface portions of the particles of polymeric material to at least approximately the melting temperature of the polymeric material and thereby melting said surface portions of the polymeric particles whereby the filler is blended with the melting surface portions of the polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the particles by the attrition effects of the mixing action; and, b. continuing the high energy and high velocity mixing action with the heating and melting surface portions of said particles of polymeric material and the resulting blending of the melted surface portions and filler and the removal of the resultant blend of melted polymeric material and filler to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and at least a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polymeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 13
Independent Claim
277 words
The method of compounding thermoplastic polymeric material with filler, comprising the steps of: a. mixing with high energy and high velocity particles of thermoplastic polymeric material and particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the polymeric material, and heating the surface portions of the particles of polymeric material to at least approximately the melting temperature of the polymeric material and thereby melting said surface portions of the polymeric particles whereby the filler is blended with the melting surface portions of the polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the particles by the attrition effects of the mixing action; and, b. continuing the high energy and high velocity mixing action with the heating and melting surface portions of said particles of polymeric material and the resulting blending of the melted surface portions and filler and the removal of the resultant blend of melted polymeric material and filler to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and at least a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polymeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 14
Dependent Claim
32 words
The method of compounding thermoplastic polymeric material and filler of claim 1, wherein the filler mixed with the polymeric material is of a relatively smaller average particle size than the polymeric material.
Claim 15
Dependent Claim
40 words
The method of compounding thermoplastic polymeric material and filler of claim 1, wherein the amount of filler mixed with the polymeric material is approximately 25 to approximately 200 parts by weight per 100 parts by weight of the polymeric material.
Claim 16
Dependent Claim
20 words
The method of compounding thermoplastic polymeric material and filler of claim 12, wherein the filler is a finely divided powder.
Claim 17
Dependent Claim
54 words
The method of compounding thermoplastic polymeric material and filler of claim 14, wherein the particles of polymeric material are sized substantially within the range of approximately 2 to approximately 8 millimeters in diameter and the particles of filler are sized substantially within the range of approximately 149 microns to approximately 37 microns in diameter.
Claim 18
Dependent Claim
50 words
The method of compounding thermoplastic polymeric material and filler of claim 11, wherein the heating of the surface portions of the particles of polymeric material is at least partially effected by the heat generated by the attrition of particles of polymeric material and filler mixing at high energy and velocity.
Claim 19
Dependent Claim
46 words
The method of compounding thermoplastic polymeric material and filler of claim 16, wherein heat from an external source is applied to the mixing particles of polymeric material and filler to augment the heat generated by the attrition of the mixing particles of polymeric material and filler.
Claim 20
Independent Claim
282 words
The method of compounding thermoplastic polyolefin polymeric material and filler, comprising the steps of: a. mixing particulate thermoplastic ethylene polymeric material of at least one member selected from the group consisting of polyethylene, blends of polyethylene and other polymers, and copolymers of ethylene and other polymerizable materials, and particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the ethylene polymeric material while melting surface portions of the particles of ethylene polymeric material, whereby the filler is blended with the melting surface portions of said particles of ethylene polymeric material and the resultant blend of the melted material and filler is removed from the remaining portions of the particles of ethylene polymeric material by the mixing action; and, b. continuing the mixing of the particulate thermoplastic ethylene polymeric material with the filler and the melting of surface portions of said particles with the resulting blending of the melting surface portions and filler and the removing of the resultant blend of melted material and filler to effect a progressive melting and diminution of the said particles of ethylene polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and at least a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said ethylene polymeric material and filler are substantially completely compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polymeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 21
Independent Claim
282 words
The method of compounding thermoplastic polyolefin polymeric material and filler, comprising the steps of: a. mixing particulate thermoplastic ethylene polymeric material of at least one member selected from the group consisting of polyethylene, blends of polyethylene and other polymers, and copolymers of ethylene and other polymerizable materials, and particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the ethylene polymeric material while melting surface portions of the particles of ethylene polymeric material, whereby the filler is blended with the melting surface portions of said particles of ethylene polymeric material and the resultant blend of the melted material and filler is removed from the remaining portions of the particles of ethylene polymeric material by the mixing action; and, b. continuing the mixing of the particulate thermoplastic ethylene polymeric material with the filler and the melting of surface portions of said particles with the resulting blending of the melting surface portions and filler and the removing of the resultant blend of melted material and filler to effect a progressive melting and diminution of the said particles of ethylene polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and at least a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said ethylene polymeric material and filler are substantially completely compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polymeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 22
Dependent Claim
70 words
The method of compounding thermoplastic ethylene polymeric material with filler of claim 18, wherein the mixing of the particulate thermoplastic ethylene polymeric material and filler is effected with a high energy and high velocity mixing action whereby the melting of the surface portions of the particles of ethylene polymeric material is at least partially effected by the heat generated by the attrition of particles of ethylene polymeric material and filler.
Claim 23
Dependent Claim
48 words
The method of compounding thermoplastic ethylene polymeric material with filler of claim 19, wherein heat from an external source is applied to the mixing particles of ethylene polymeric material and filler to augment the heat generated by the attrition of mixing particles of ethylene polymeric material and filler.
Claim 24
Dependent Claim
31 words
The method of compounding thermoplastic polymeric material and filler of claim 20, wherein the filler mixed with the polymeric material is of a relatively smaller particle size than the polymeric material.
Claim 25
Dependent Claim
40 words
The method of compounding thermoplastic polymeric material and filler of claim 20, wherein the amount of filler mixed with the polymeric material is approximately 25 to approximately 200 parts by weight per 100 parts by weight of the polymeric material.
Claim 26
Dependent Claim
20 words
The method of compounding thermoplastic polymeric material and filler of claim 21, wherein the filler is a finely divided powder.
Claim 27
Dependent Claim
54 words
The method of compounding thermoplastic polymeric material and filler of claim 23, wherein the particles of polymeric material are sized substantially within the ranges of approximately 2 to approximately 8 millimeters in diameter and the particles of filler are sized substantially within the range of approximately 149 microns to approximately 37 microns in diameter.
Claim 28
Dependent Claim
35 words
The method of compounding thermoplastic polymeric material and filler of claim 23, wherein the compound of polymeric material and filler is cooled and a cross-linking curing agent is added to and dispersed through the compound.
Claim 29
Dependent Claim
19 words
The method of compounding thermoplastic polymeric material and filler of claim 25, wherein the cross-linking curing agent is peroxide.
Claim 30
Independent Claim
247 words
The method of compounding thermoplastic polymeric material and filler, comprising the steps of: a. mixing particles of thermoplastic polymeric material with particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the polymeric material in a high velocity impeller mixer while melting surface portions of the particles of polymer material, whereby the filler is blended with the melting surface portions of said polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the polymeric particles by the mixing action; and, b. continuing both the mixing of the particles of thermoplastic polymeric material with the filler in the high velocity impeller mixer and the melting of the surface portions of said particles with the resulting blending of the melting surface portions and filler and the removal of the resultant blend of the melted polymeric material and filler from said particles of polymeric material to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded with said compound comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 31
Independent Claim
247 words
The method of compounding thermoplastic polymeric material and filler, comprising the steps of: a. mixing particles of thermoplastic polymeric material with particulate filler proportioned in amounts ranging from at least 5 to about 200 parts by weight of the filler per 100 parts by weight of the polymeric material in a high velocity impeller mixer while melting surface portions of the particles of polymer material, whereby the filler is blended with the melting surface portions of said polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the polymeric particles by the mixing action; and, b. continuing both the mixing of the particles of thermoplastic polymeric material with the filler in the high velocity impeller mixer and the melting of the surface portions of said particles with the resulting blending of the melting surface portions and filler and the removal of the resultant blend of the melted polymeric material and filler from said particles of polymeric material to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded with said compound comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 32
Dependent Claim
43 words
The method of compounding thermoplastic polymeric material and filler of claim 27, wherein the proportion of filler to polymeric material is in amounts ranging from about 25 to about 200 parts by weight of filler per 100 parts by weight of polymeric material.
Claim 33
Dependent Claim
40 words
The method of compounding thermoplastic polymeric material and filler of claim 28, wherein the filler is of relatively smaller average particle size than the original average size of the particles of polymeric material, and the polymeric material comprises a polyolefin.
Claim 34
Independent Claim
352 words
The method of compounding thermoplastic ethylene-containing polymeric material and filler, comprising the steps of: a. mixing with high energy and high velocity particles of ethylene-containing polymeric material of at least one member selected from the group consisting of polyethylene, blends of polyethylene and other polymers, and copolymers of ethylene and other polymerizable materials sized substantially within the range of approximately 2 to approximately 8 millimeters in diameter with particulate filler sized substantially within the range of approximately 149 microns to approximately 37 microns in diameter, said particles of polymeric material and filler being proportioned in amounts ranging from about 25 to about 200 parts by weight of filler per 100 parts by weight of polymeric material, in a high velocity impeller mixer, and heating the surface portions of the particles of ethylene-containing polymeric material to at least approximately the melting temperature of the polymeric material and thereby melting said surface portions of the polymeric particles whereby the filler is blended with the melting surface portions of the polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the particles by the attrition effects of the mixing action; and, b. continuing the high energy and high velocity mixing action in the high velocity impeller mixer with the heating and melting of surface portions of said particles of polymeric material and the resulting blending of the melted surface portions and filler and the removal of the resultant blend of melted polymeric material and filler to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and at least a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polymeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
Claim 35
Independent Claim
352 words
The method of compounding thermoplastic ethylene-containing polymeric material and filler, comprising the steps of: a. mixing with high energy and high velocity particles of ethylene-containing polymeric material of at least one member selected from the group consisting of polyethylene, blends of polyethylene and other polymers, and copolymers of ethylene and other polymerizable materials sized substantially within the range of approximately 2 to approximately 8 millimeters in diameter with particulate filler sized substantially within the range of approximately 149 microns to approximately 37 microns in diameter, said particles of polymeric material and filler being proportioned in amounts ranging from about 25 to about 200 parts by weight of filler per 100 parts by weight of polymeric material, in a high velocity impeller mixer, and heating the surface portions of the particles of ethylene-containing polymeric material to at least approximately the melting temperature of the polymeric material and thereby melting said surface portions of the polymeric particles whereby the filler is blended with the melting surface portions of the polymeric particles and the resultant blend of the melted polymeric material and filler is removed from the remaining portion of the particles by the attrition effects of the mixing action; and, b. continuing the high energy and high velocity mixing action in the high velocity impeller mixer with the heating and melting of surface portions of said particles of polymeric material and the resulting blending of the melted surface portions and filler and the removal of the resultant blend of melted polymeric material and filler to effect a progressive melting and diminution of the said particles of polymeric material until greater than 50% of the particulate polymeric material has become expended by melting and at least a majority of greater than 50% of the filler has become substantially assimilated into the polymeric material whereby said polymeric material and filler are substantially compounded to a free flowing particulate form comprising discrete particles of the compounded blend of polymeric material and filler with said blend comprising fundamental units predominantly structured essentially of a stratified layer of the filler adhesively embraced by a film-like mass of polymeric material.
References Cited (Backward Citations)
US3148169A
Cited
US3372139A
Cited
US3567669A
Cited
US3736173A
Cited
FR2047362A5
Cited
US3824208A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |