Control of physical properties of alumina extrudates
Assignee: WR Grace and Co
•
Filing: 1976-07-01
•
Granted: 1977-08-30
•
Expires: 1996-07-01
Abstract
Abstract A process for preparing extrudates of alumina monohydrate having densities, surface areas and pore volumes within a predetermined range by mixing the alumina with a sufficient quantity of water to prepare an extrudable product and aging this product for a period of 1/2 to 6 hours. The alumina is then extruded and the extrudates dried using conventional techniques. The alumina is primarily used as a base for auto exhaust conversion catalysts.
Inventors
- 👤 John Lawrence Warthen
- 👤 Warren Stanley Briggs
- 👤 Marvin Vernon Paggen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:01
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B01; B01J; B01J37/00; B01J37/0009; C04B35/00; C04B35/01; C04B35/10; C04B41/45; C04B41/50; C04B41/5007; C04B41/80; C04B41/81; C04B41/85
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
98 words
A process for preparing an auto exhaust conversion catalyst which consists essentially of the steps of: a. preparing an alpha alumina monohydrate in the 10 to 150 micron size range, b. adding a sufficient quantity of water to form an extrudable paste, c. aging said paste at ambient temperatures for 0.5 to 6 hours, d. extruding the alumina to form extrudates, e. drying and calcining the extrudates, f. contacting the extrudates with solutions of salts of metals having activity for conversion of the noxious components of exhaust gases to innocuous entities, g. drying, calcining and recovering the product.
Claim 2
Dependent Claim
98 words
A process for preparing an auto exhaust conversion catalyst which consists essentially of the steps of: a. preparing an alpha alumina monohydrate in the 10 to 150 micron size range, b. adding a sufficient quantity of water to form an extrudable paste, c. aging said paste at ambient temperatures for 0.5 to 6 hours, d. extruding the alumina to form extrudates, e. drying and calcining the extrudates, f. contacting the extrudates with solutions of salts of metals having activity for conversion of the noxious components of exhaust gases to innocuous entities, g. drying, calcining and recovering the product.
Claim 3
Dependent Claim
24 words
The process according to claim 1 wherein the extrudates have a large percentage of pores in the 200 to greater than 300A size range.
Claim 4
Dependent Claim
18 words
The process according to claim 1 wherein the extrudates are aged at temperature of 30° to 50° C.
Claim 5
Dependent Claim
27 words
The process according to claim 1 wherein the extrudates are dried in step (e) in a forced draft dryer at a temperature of 150° to 270° F.
Claim 6
Dependent Claim
26 words
The process according to claim 1 wherein the extrudates are calcined in step (g) at temperatures of 700° to 1400° F. for 1 to 6 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |