Process for preparing a gas desulfurization sorbent
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1976-06-08
•
Granted: 1977-08-30
•
Expires: 1996-06-08
Abstract
Abstract Hydrogen sulfide and its precursors can be selectively sorbed from gas streams containing the same by contacting the gas stream at elevated temperatures with a regenerable sorbent comprising a steam-treated support composited with a rare earth metal component. Presteaming the support lowers the amount of rare earth metal component needed to achieve a given activity level for hydrogen sulfide removal. Subsequent to sorption, the sorbent composite may be desorbed and regenerated by treatment with steam (desorption) and an oxidizing gas (regeneration). The sorbent capacity may be increased by the use of alkali or alkaline earth metal components as promoters. A preferred sorbent comprises lanthanum composited with presteamed alumina.
Inventors
- 👤 Kenneth S. Wheelock
- 👤 Geoffrey R. Say
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 01:44
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/02; B01D53/04; B01D53/34; B01D53/46; B01D53/48; B01D53/52; C; C10; C10K; C10K1/00; C10K1/20; B01D2257/00; B01D2257/30; B01D2257/304; B01D2257/308; B01D2259/00; B01D2259/40; B01D2259/402
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
84 words
A process for preparing a supported sorbent for removing at least a portion of acidic gases from a gaseous mixture containing an acidic gas selected from the group consisting of hydrogen sulfide, carbonyl sulfide and mixtures thereof, which process comprises: first steam treating an inorganic oxide support for a period of time sufficient to decrease the surface area thereof, subsequently impregnating the steam-treated support with a solution of a rare earth metal compound thermally decomposable to the oxide, drying and calcining said impregnated support.
Claim 2
Dependent Claim
84 words
A process for preparing a supported sorbent for removing at least a portion of acidic gases from a gaseous mixture containing an acidic gas selected from the group consisting of hydrogen sulfide, carbonyl sulfide and mixtures thereof, which process comprises: first steam treating an inorganic oxide support for a period of time sufficient to decrease the surface area thereof, subsequently impregnating the steam-treated support with a solution of a rare earth metal compound thermally decomposable to the oxide, drying and calcining said impregnated support.
Claim 3
Dependent Claim
36 words
The process of claim 1, wherein said inorganic oxide support is steam-treated at a temperature varying from about 700 to about 1,900° F. for a period of time ranging from about 60 to about 6,000 minutes.
Claim 4
Dependent Claim
22 words
The process of claim 1, wherein said steam treatment is conducted at a pressure varying from about atmospheric to about 200 psig.
Claim 5
Dependent Claim
28 words
The process of claim 1, wherein said rare earth metal component calculated as the oxide thereof, comprises from about 1 to about 50 weight percent of said support.
Claim 6
Dependent Claim
13 words
The process of claim 1, wherein said rare earth metal compound comprises lanthanum.
Claim 7
Dependent Claim
24 words
The process of claim 1, wherein said rare earth metal compound is a mixture of rare earth metal compounds comprising lanthanum, praseodymium, and neodymium.
Claim 8
Dependent Claim
16 words
The process of claim 1, wherein said sorbent comprises presteamed alumina impregnated with a lanthanum compound.
References Cited (Backward Citations)
US1900882A
Cited
US3864459A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |