Method of producing thin layer methanation reaction catalyst
Assignee: Hitachi Ltd
•
Filing: 1975-11-11
•
Granted: 1977-08-23
•
Expires: 1995-11-11
Abstract
Abstract A catalyst layer is formed on the metallic surface of a structure constructing a reactor by diffusing a developable metal into the structure by the pack cementation method and developing the diffused metal. The catalyst layer is metallurgically combined with the structure, so that it has excellent mechanical strength and heat conductivity. Thus, by using the structure having the catalyst layer as a heat exchanger type methanation reactor it is possible to obtain a methanation reactor enabling an extremely enhanced rate of reaction to be obtained with superior operability and at great savings.
Inventors
- 👤 Yutaka Fukui
- 👤 Fumio Hataya
- 👤 Ryoichi Sasaki
- 👤 Fumito Nakajima
- 👤 Shimpei Matsuda
- 👤 Munehiko Tonami
- 👤 Ryo Hiraga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:46
CPC Classifications
B; B01; B01J; B01J19/00; B01J19/0006; B01J19/0013; B01J25/00; B01J25/02; B01J35/00; B01J35/30; B01J35/391; B01J35/395; C; C07; C07C; C07C1/00; C07C1/02; C07C1/04; C07C1/0425; C07C1/0445; B01J2219/00; B01J2219/00049; B01J2219/00051; B01J2219/00074; B01J2219/00076; B01J2219/00085; B01J2219/00159; B01J2219/00177; B01J2219/00186; B01J2235/00; B01J35/34; B01J35/36; C07C2521/00; C07C2521/02; C07C2521/04
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
113 words
A method of producing a methanation reaction catalyst comprising forming an aluminum diffusion layer on the inner surface of a tube of an alloy containing at least 45% by weight nickel and having a tensile strength of at least 35 kg/mm 2 and an elongation of at least 20% at 500° C. by heating said tube together with a powdery pack comprising an aluminum powder in an amount of 1 to 50 percent by weight, ammonium chloride as an active agent and a heat-resistant inactive carrier for preventing agglomeration of said aluminum powder, said pack being charged into the interior of said tube, and developing said aluminum diffusion layer with an alkaline solution.
Claim 2
Independent Claim
113 words
A method of producing a methanation reaction catalyst comprising forming an aluminum diffusion layer on the inner surface of a tube of an alloy containing at least 45% by weight nickel and having a tensile strength of at least 35 kg/mm 2 and an elongation of at least 20% at 500° C. by heating said tube together with a powdery pack comprising an aluminum powder in an amount of 1 to 50 percent by weight, ammonium chloride as an active agent and a heat-resistant inactive carrier for preventing agglomeration of said aluminum powder, said pack being charged into the interior of said tube, and developing said aluminum diffusion layer with an alkaline solution.
Claim 3
Dependent Claim
22 words
The method according to claim 1, wherein said inactive carrier is alumina, and said charged tube is heated in a non-oxidizing atmosphere.
Claim 4
Dependent Claim
32 words
The method according to claim 2, wherein the powdery pack comprises 40% aluminum, 1% ammonium chloride, and a balance of alumina, said charged tube being heated for 120 minutes at 900° C.
Claim 5
Dependent Claim
32 words
The method according to claim 3, wherein the powdery pack comprises 20% aluminum, 1% ammonium chloride, and a balance of alumina, said charged tube being heated for 120 minutes at 900° C.
Claim 6
Dependent Claim
32 words
The method according to claim 3, wherein the powdery pack comprises 20% aluminum, 0.5% ammonium chloride, and a balance of alumina, said charged tube being heated for 60 minutes at 800° C.
Claim 7
Dependent Claim
32 words
The method according to claim 3, wherein the powdery pack comprises 20% aluminum, 0.5% ammonium chloride, and a balance of alumina, said charged tube being heated for 120 minutes at 600° C.
Claim 8
Dependent Claim
32 words
The method according to claim 3, wherein the powdery pack comprises 5% aluminum, 1% ammonium chloride, and a balance of alumina, said charged tube being heated for 120 minutes at 900° C.
Claim 9
Dependent Claim
32 words
The method according to claim 3, wherein the powdery pack comprises 5% aluminum, 1% ammonium chloride, and a balance of alumina, said charged tube being heated for 120 minutes at 1,000° C.
Claim 10
Dependent Claim
32 words
The method according to claim 3, wherein the powdery pack comprises 1% aluminum, 1% ammonium chloride, and a balance of alumina, said charged tube being heated for 120 minutes at 800° C.
Claim 11
Dependent Claim
26 words
The method according to claim 2, wherein the alkaline solution is an aqueous solution of caustic soda at a temperature of from 50° to 80° C.
Claim 12
Dependent Claim
22 words
The method according to claim 1, wherein said aluminum diffusion layer has an aluminum to nickel atomic ratio of at least 0.3.
Claim 13
Independent Claim
157 words
A method of producing a methanation reaction catalyst comprising a step of forming an aluminum diffusion layer on the inner surface of a tube containing at least 45% by weight of nickel and exhibiting a tensile strength of not less than 35 kg/mm 2 and an elongation of not less than 20 percent at 500° C., by heating said tube together with a powdery pack comprising 1 to 50 percent by weight of aluminum, an aluminum oxide as an inactive component and ammonium chloride as an active component, said powdery pack being charged into the interior of said tube, a step of developing said aluminum diffusion layer with an alkaline solution to form an active catalyst layer of 1 to 500 microns thickness, and a step of oxidizing the surface of said active catalyst layer in a nitrogen atmosphere containing oxygen whereby the oxidized surface of the active catalyst layer is easily reduced in an operating atmosphere.
Claim 14
Independent Claim
157 words
A method of producing a methanation reaction catalyst comprising a step of forming an aluminum diffusion layer on the inner surface of a tube containing at least 45% by weight of nickel and exhibiting a tensile strength of not less than 35 kg/mm 2 and an elongation of not less than 20 percent at 500° C., by heating said tube together with a powdery pack comprising 1 to 50 percent by weight of aluminum, an aluminum oxide as an inactive component and ammonium chloride as an active component, said powdery pack being charged into the interior of said tube, a step of developing said aluminum diffusion layer with an alkaline solution to form an active catalyst layer of 1 to 500 microns thickness, and a step of oxidizing the surface of said active catalyst layer in a nitrogen atmosphere containing oxygen whereby the oxidized surface of the active catalyst layer is easily reduced in an operating atmosphere.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |