Methods for reactivating zeolites
Assignee: Leuna Werke Walter Ulbright Germany VEB
•
Filing: 1975-02-03
•
Granted: 1977-08-23
•
Expires: 1995-02-03
Abstract
Abstract A zeolite of type 5A, which has been used to separate normal paraffins from a hydrocarbon mixture containing normal paraffins by bringing the hydrocarbon mixture into contact with the zeolite whereby the zeolite absorbs the normal paraffins and then desorbing the normal paraffins from the zeolite by contacting the zeolite with water-containing ammonia vapour, is reactivated by first contacting the zeolite with at least one of water, aqueous solutions and water-containing gases at a temperature below 350° C and then heating the zeolite to a temperature above 350° C.
Inventors
- 👤 Hans-Heinrich Reif
- 👤 Klaus Wehner
- 👤 Jurgen Welker
- 👤 Karl-Heinz Schmidt
- 👤 Waltraud Schnick
- 👤 Lutz Widmann
- 👤 Otto Schicker
- 👤 Gunter Seidel
- 👤 Karsten Kalb
- 👤 Wolfhard Dollase
- 👤 Helmut Furtig
- 👤 Werner Hose
- 👤 Wolfgang Roscher
- 👤 Udo Hadicke
- 👤 Herbert Knoll
- 👤 Rudiger Seidel
- 👤 Gunter Nemitz
- 👤 Edith Sturmer
- 👤 Manfred Kaiser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:25
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/30; B01J20/34; B01J20/3408; C; C10; C10G; C10G25/00; C10G25/12
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
136 words
A method for reactivating a zeolite whose absorptive capacity has been deactivated in a process of separating normal paraffins from a hydrocarbon mixture containing said paraffins by means of alternating adsorption onto said zeolite and desorption therefrom with water-containing ammonia vapor; which method comprises a first step of contacting said zeolite directly after said desorption step with water, or water-containing gases at a temperature of about 20°-250° C, the proportion by weight of water to zeolite being at least 1:10, and then contacting said zeolite in a second step with a stream of gas selected from the group consisting of air, hydrogen, oxygen, nitrogen and ammonia, at a temperature of about 400°-550° C, said gas having a water content of less than 5% by volume, until said zeolite is restored to substantially its original adsorption capacity.
Claim 2
Independent Claim
136 words
A method for reactivating a zeolite whose absorptive capacity has been deactivated in a process of separating normal paraffins from a hydrocarbon mixture containing said paraffins by means of alternating adsorption onto said zeolite and desorption therefrom with water-containing ammonia vapor; which method comprises a first step of contacting said zeolite directly after said desorption step with water, or water-containing gases at a temperature of about 20°-250° C, the proportion by weight of water to zeolite being at least 1:10, and then contacting said zeolite in a second step with a stream of gas selected from the group consisting of air, hydrogen, oxygen, nitrogen and ammonia, at a temperature of about 400°-550° C, said gas having a water content of less than 5% by volume, until said zeolite is restored to substantially its original adsorption capacity.
Claim 3
Dependent Claim
26 words
A method in accordance with claim 1, wherein the stream of gas used in the second step has a maximum water content of 0.5% by volume.
Claim 4
Dependent Claim
20 words
A method in accordance with claim 1, wherein the stream of gas in the second step is an oxygen-containing gas.
Claim 5
Dependent Claim
33 words
A method in accordance with claim 1, wherein water is used in the first step and a stream of hydrogen containing less than 0.01% water by volume is used in the second step.
Claim 6
Dependent Claim
35 words
A method in accordance with claim 1, wherein hydrogen having a water of content of 25% by volume is used in the first step and a stream of air is used in the second step.
Claim 7
Dependent Claim
42 words
A method in accordance with claim 1, wherein ammonia having a water content of 20% by volume is used in the first step and a stream of ammonia having a water content of 0.5% by volume is used in the second step.
Claim 8
Independent Claim
159 words
A method for reactivating a zeolite whose absorptive capacity has been deactivated in a process of separating normal paraffins from a hydrocarbon mixture containing said paraffins by means of alternating adsorption onto said zeolite and desorption therefrom with water-containing ammonia vapor; which method comprises a first step of contacting said zeolite directly after said desorption step with an aqueous solution of a salt of the bivalent metal of group IIA of the periodic system at a temperature below about 100° C, for a period of 1 to 72 hours, the amount of salt used being 0.1 to 1.0 mole per mole of zeolite; and then contacting said zeolite in a second step with a stream of gas selected from the group consisting of air, hydrogen, oxygen, nitrogen and ammonia, at a temperature of about 400°-550° C, said gas having a water content of less than 5% by volume, until said zeolite is restored to substantially its original adsorption capacity.
Claim 9
Independent Claim
159 words
A method for reactivating a zeolite whose absorptive capacity has been deactivated in a process of separating normal paraffins from a hydrocarbon mixture containing said paraffins by means of alternating adsorption onto said zeolite and desorption therefrom with water-containing ammonia vapor; which method comprises a first step of contacting said zeolite directly after said desorption step with an aqueous solution of a salt of the bivalent metal of group IIA of the periodic system at a temperature below about 100° C, for a period of 1 to 72 hours, the amount of salt used being 0.1 to 1.0 mole per mole of zeolite; and then contacting said zeolite in a second step with a stream of gas selected from the group consisting of air, hydrogen, oxygen, nitrogen and ammonia, at a temperature of about 400°-550° C, said gas having a water content of less than 5% by volume, until said zeolite is restored to substantially its original adsorption capacity.
Claim 10
Dependent Claim
36 words
A method in accordance with claim 7, wherein the aqueous solution of the bivalent metal salt is selected from the class consisting of magnesium sulfate, magnesium chloride, magnesium acetate, calcium sulfate, calcium chloride and calcium acetate.
Claim 11
Dependent Claim
30 words
A method in accordance with claim 7, wherein the salt treated zeolite is washed with water and dried prior to said second step of contacting with a stream of gas.
Claim 12
Independent Claim
183 words
A method for reactivating a zeolite whose absorptive capacity has been deactivated in a process of separating normal paraffins from a hydrocarbon mixture containing said paraffins by means of alternating adsorption onto said zeolite and desorption therefrom with water-containing ammonia vapor; which method comprises a first step of contacting said zeolite directly after said desorption step with an aqueous solution of a substance selected from the class consisting of urea and a nitrogen compound having the formula NR 1 R 2 R 3 , wherein R 1 and R 2 are independently H, CH 3 or C 2 H 5 and R 3 is CH 3 or C 2 H 5 , at a temperature below about 150° C, for a period of 1 to 72 hours, and then contacting said zeolite in a second step with a stream of gas selected from the group consisting of air, hydrogen, oxygen, nitrogen and ammonia, at a temperature of about 400°-550° C, said gas having a water content of less than 5% by volume, until said zeolite is restored to substantially its original adsorption capacity.
Claim 13
Independent Claim
183 words
A method for reactivating a zeolite whose absorptive capacity has been deactivated in a process of separating normal paraffins from a hydrocarbon mixture containing said paraffins by means of alternating adsorption onto said zeolite and desorption therefrom with water-containing ammonia vapor; which method comprises a first step of contacting said zeolite directly after said desorption step with an aqueous solution of a substance selected from the class consisting of urea and a nitrogen compound having the formula NR 1 R 2 R 3 , wherein R 1 and R 2 are independently H, CH 3 or C 2 H 5 and R 3 is CH 3 or C 2 H 5 , at a temperature below about 150° C, for a period of 1 to 72 hours, and then contacting said zeolite in a second step with a stream of gas selected from the group consisting of air, hydrogen, oxygen, nitrogen and ammonia, at a temperature of about 400°-550° C, said gas having a water content of less than 5% by volume, until said zeolite is restored to substantially its original adsorption capacity.
Claim 14
Dependent Claim
18 words
A method in accordance with claim 10, wherein the second step is conducted below about one atmosphere pressure.
Claim 15
Dependent Claim
18 words
A method in accordance with claim 10, wherein the second step is conducted below about 0.1 atmosphere pressure.
Claim 16
Dependent Claim
30 words
A method in accordance with claim 10, wherein an aqueous urea solution is used in the first step and a stream of hydrogen gas is used in the second step.
Claim 17
Dependent Claim
28 words
A method in accordance with claim 10, wherein the second step is conducted in the presence of a stream of gas at a maximum pressure of 15 atmospheres.
Claim 18
Dependent Claim
30 words
A method in accordance with claim 10, wherein an aqueous dimethyl amine solution is used in the first step, and a stream of air is used in the second step.
Claim 19
Dependent Claim
27 words
A method in accordance with claim 10, wherein aqueous dimethylamine is used in the first step and a stream of ammonia is used in the second step.
References Cited (Backward Citations)
US3075023A
Cited
US3347783A
Cited
US3422004A
Cited
US3420772A
Cited
US3437601A
Cited
US3405057A
Cited
US3531400A
Cited
US3622506A
Cited
US3836455A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |