Method of and apparatus for bending relatively thin glass sheets
Assignee: Pilkington North America Inc
•
Filing: 1975-06-23
•
Granted: 1977-08-23
•
Expires: 1995-06-23
Abstract
Abstract A method of and apparatus for bending and tempering a relatively thin glass sheet comprising heating the glass sheet to its softening point in a heating chamber, rapidly conveying the sheet from the heating chamber to and between a pair of mold press members for immediate press shaping therebetween, and then quickly chilling the sheets below the annealing temperature range of the glass in a two-stage operation by applying a cooling medium successively under relatively high and low pressures to the opposite surfaces of the sheet.
Inventors
- 👤 Robert P. Bamford, deceased
- 👤 Richard A. Herrington
- 👤 Waldemar W. Oelke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:56
CPC Classifications
C; C03; C03B; C03B27/00; C03B27/04; C03B27/0404; C03B23/00; C03B23/02; C03B23/023; C03B23/03; C03B27/044; C03B27/0442; C03B40/00; C03B40/005; C03B2225/00; C03B2225/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
219 words
A method of bending and tempering relatively thin glass sheets comprising: heating a glass sheet to the softening point thereof in a furnace, transferring said heated sheet from said furnace onto a shaping surface of a press member, moving said press member toward a complemental shaping surface of a second press member to press said sheet therebetween and impart the desired curvature to said sheet, removing said sheet from between said press members and advancing said sheet to a primary tempering section immediately downstream from said press members, advancing said sheet through said primary tempering section while applying a cooling fluid at a rapid flow rate through a multiplicity of small diameter orifices under relatively high pressure but of relatively small volume against the opposite surfaces of said sheet to initiate tempering by creating a maximum temperature differential between the opposite surfaces of the glass sheet and the core thereof and maintaining said maximum temperature differential until said core of the sheet passes through the strain point of the glass, advancing said sheet from said primary tempering section to and through a secondary tempering section immediately downstream of said primary tempering section while applying a cooling fluid under relatively low pressure but of a relatively large volume against the opposite surfaces of said sheet to complete the tempering thereof.
Claim 2
Independent Claim
219 words
A method of bending and tempering relatively thin glass sheets comprising: heating a glass sheet to the softening point thereof in a furnace, transferring said heated sheet from said furnace onto a shaping surface of a press member, moving said press member toward a complemental shaping surface of a second press member to press said sheet therebetween and impart the desired curvature to said sheet, removing said sheet from between said press members and advancing said sheet to a primary tempering section immediately downstream from said press members, advancing said sheet through said primary tempering section while applying a cooling fluid at a rapid flow rate through a multiplicity of small diameter orifices under relatively high pressure but of relatively small volume against the opposite surfaces of said sheet to initiate tempering by creating a maximum temperature differential between the opposite surfaces of the glass sheet and the core thereof and maintaining said maximum temperature differential until said core of the sheet passes through the strain point of the glass, advancing said sheet from said primary tempering section to and through a secondary tempering section immediately downstream of said primary tempering section while applying a cooling fluid under relatively low pressure but of a relatively large volume against the opposite surfaces of said sheet to complete the tempering thereof.
Claim 3
Dependent Claim
54 words
A method according to claim 1, including moving said sheet through said heating chamber at a first preselected rate of speed and rapidly advancing said sheet out of said heating chamber to the region of said first mentioned press member at a second rate of speed substantially greater than said first rate of speed.
Claim 4
Dependent Claim
38 words
A method according to claim 1, wherein the pressure of said high pressure cooling fluid ranges from about 5 to 11 p.s.i. and the pressure of said low pressure cooling fluid ranges from about 1.2 to 1.5 p.s.i.
Claim 5
Dependent Claim
216 words
Apparatus for bending and tempering relatively thin glass sheets comprising: a conveyor for supporting and moving a thin glass sheet along a substantially horizontal path through a heating chamber, a bending area, and a tempering area including a primary tempering section and a secondary tempering section; means in said heating chamber for heating the sheet to substantially the softening point of glass; opposed press members mounted in said bending area for press shaping said heated sheet into the desired curvature; said press members located immediately adjacent the exit end of said heating chamber in a substantially juxtaposed relation thereto; said primary tempering section being mounted immediately downstream of said press members in substantially juxtaposed relation thereto and including a multiplicity of relatively small diameter orifices for directing a plurality of streams of cooling fluid under relatively high pressure but of relatively small volume against the opposite surfaces of said bent sheet to initiate rapid chilling and tempering of the same while minimizing blow back into the bending area; said secondary tempering section located immediately downstream of said primary tempering section and including relatively large diameter orifices for directing a plurality of streams of cooling fluid under relatively low pressure but of relatively large volume against the opposite surfaces of said sheet to complete the tempering thereof.
Claim 6
Dependent Claim
216 words
Apparatus for bending and tempering relatively thin glass sheets comprising: a conveyor for supporting and moving a thin glass sheet along a substantially horizontal path through a heating chamber, a bending area, and a tempering area including a primary tempering section and a secondary tempering section; means in said heating chamber for heating the sheet to substantially the softening point of glass; opposed press members mounted in said bending area for press shaping said heated sheet into the desired curvature; said press members located immediately adjacent the exit end of said heating chamber in a substantially juxtaposed relation thereto; said primary tempering section being mounted immediately downstream of said press members in substantially juxtaposed relation thereto and including a multiplicity of relatively small diameter orifices for directing a plurality of streams of cooling fluid under relatively high pressure but of relatively small volume against the opposite surfaces of said bent sheet to initiate rapid chilling and tempering of the same while minimizing blow back into the bending area; said secondary tempering section located immediately downstream of said primary tempering section and including relatively large diameter orifices for directing a plurality of streams of cooling fluid under relatively low pressure but of relatively large volume against the opposite surfaces of said sheet to complete the tempering thereof.
Claim 7
Dependent Claim
55 words
Apparatus according to claim 4, wherein said conveyor is operative at differential speeds to move said sheet through said heating chamber at a preselected first rate of speed and rapidly advance said sheet out of said heating chamber and into said bending area at a rate of speed greater than said first rate of speed.
Claim 8
Dependent Claim
26 words
A method according to claim 1, wherein the elapsed time between the heating and high pressure cooling of said sheet is no greater than 4 seconds.
Claim 9
Dependent Claim
24 words
A method according to claim 1, wherein the elapsed time between the heating and high pressure cooling of said sheet is about 3.5 seconds.
Claim 10
Dependent Claim
35 words
A method according to claim 2, wherein said first preselected speed ranges from about 180 to 280 inches per minute and said second rate of speed ranges from about 1400 to 1550 inches per minute.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |