Cementitious sound absorbing panels and sound absorbing sprayed wall structures

Claim 2

An acoustical sound-absorbing cementitious product composed of hydraulic cement, selected from the group comprising portland cement, calcium aluminate cement, and gypsum cement, of lightweight aggregate and of foamed air cells, with a range of dry densities of 20-40 pounds per cubic foot, having an interior interconnecting cellular structure and an impervious surface with perforations providing open space accounting for at least 10% of the surface area, giving the sound waves access to the interior open cell structure.

Claim 3

A sound-absorbing product according to claim 1 in which the impervious surface is the natural tough skin of the cementitious material.

Claim 4

A sound-absorbing product according to claim 1 in which thin perforated sheeting selected from the group of materials comprising aluminum, steel, wood veneer, fiber hardboard, and plastic, is laminated to the surface of the low density cementitious composition.

Claim 5

A process for the production of cementitious sound-absorbing products having interior interconnected cellular structures, comprising the steps of mixing 100 parts by weight of hydraulic cement, selected from the group of portland cement, calcium aluminate cement, and gypsum cement, with the following ranges of other components, in parts by weight, water 55-120, pozzolonic fly ash 0-50, vermiculite or perlite 5-30, chopped fiber glass 0-10, guar gum 0-1, and preformed foam 5-30 parts, casting the mixed composition into forms, partially curing the cementitious product, perforating the impervious skin to provide at least 10% open space on the surface area to give access to the interior interconnected cellular structure and fully curing the product to a dry density of 20-40 pounds per cubic foot.

Claim 6

A process for the production of cementitious sound-absorbing products having interior interconnected cellular structures, comprising the steps of mixing 100 parts by weight of hydraulic cement, selected from the group of portland cement, calcium aluminate cement, and gypsum cement, with the following ranges of other components, in parts by weight, water 55-120, pozzolonic fly ash 0-50, vermiculite or perlite 5-30, chopped fiber glass 0-10, guar gum 0-1, and preformed foam 5-30 parts, casting the mixed composition into forms, partially curing the cementitious product, perforating the impervious skin to provide at least 10% open space on the surface area to give access to the interior interconnected cellular structure and fully curing the product to a dry density of 20-40 pounds per cubic foot.

Claim 7

A process according to claim 4 in which the cementitious composition without the foam is pumped to a spray gun provided with a static in-line mixer before the nozzle, the preformed foam is then conveyed pneumatically and introduced at the static in-line mixer there to be mixed with the cementitious slurry and sprayed under controlled density unto a substrate to form the interior cellular structure and the impervious skin, which is perforated for sound absorption characteristics.

Claim 8

A process according to claim 4 in which one or both impervious skin surfaces are skived off after partial curing to expose the interconnected cellular structure, the curing is completed and the panels are then formed into a sandwich construction by bonding thin perforated sheeting, selected from the group of materials comprising aluminum, steel, wood veneer, compressed fiber board, and plastics, to the low density skinless surfaces of the panels.

Claim 9

A process according to claim 4 in which the cast panels after partial curing are sliced into narrower panels of controlled width, the curing is then completed and the sliced panels are separated and bonded to perforated thin sheeting selected from the group of materials comprising aluminum, steel, wood veneer, compressed fiber board, and plastics.

Claim 10

A process according to claim 7 in which the sandwich construction with the thin sheeting is made with one side of the panel being bonded to perforated sheeting for absorption of sound waves while the other side of the panel is bonded to imperforated sheeting to reflect the sound waves.