Abrasion resistant coated abrasive pipe lining sheet
Assignee: CA ACQUISITION Co CHICAGO ILL A CORP OF
•
Filing: 1974-11-29
•
Granted: 1977-08-16
•
Expires: 1994-11-29
Abstract
Abstract A composite abrasion resistant, coated and abrasive containing pipe lining sheet comprises a pipe lining layer consisting from about 30 to about 70% by volume of abrasion resistant abrasive granules (preferably from about 45 to about 55% by volume of silicon carbide, alumina or alumina/zirconia granules of blocky shape, nonaligned orientation and diverse size) and from about 70 to about 30% by volume (preferably from about 55 to about 45% by volume) of a flexible organic resin binder, preferably phenolic, polyurethane, polybutadiene-acrylonitrile or epoxy resins. The pipe lining sheet can optionally be provided with a paper or textile backing bonded thereto, or with a backing of nonabsorbent, nonreactive film such as polyester, which can later be stripped off the abrasion resistant pipe lining material prior to use for lining pipes. The composite abrasion resistant pipe lining sheet can be bonded to the inner perimeter of the outer portion of a pipe by mechanical means, chemical means or a combination thereof. The abrasion resistant pipe lining sheet can be used as the innermost component for building a pipe; or it can be applied to the inside of a pre-existing pipe by adhesive means or, in the case of a metallic pipe and a composite abrasion resistant pipe lining sheet having a metallic flexible binder, by welding or brazing to the inner perimeter of the pre-existing metallic pipe.
Inventors
- 👤 Paul N. Abelson
- 👤 Halsey W. Buell
- 👤 William E. Hallatt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:23
CPC Classifications
B; B65; B65G; B65G53/00; B65G53/34; B65G53/52; B65G53/523; C; C08; C08K; C08K3/00; C08K7/00; F; F16; F16L; F16L57/00; F16L57/06; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24364; Y10T428/24372; Y10T428/24405; Y10T428/25; Y10T428/252; Y10T442/00; Y10T442/20; Y10T442/2041; Y10T442/2098; Y10T442/2107
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
246 words
An abrasion resistant, coated and abrasion containing, pipe lining sheet having a thickness of not less than about 0.75 mm, a backing side with a relatively uneven surface, and being sufficiently flexible to be wound backing side inward around a mandrel in building a pipe or within a pre-existing pipe, said sheet including a backing, and a composite layer on said backing and consisting essentially if: (1) from about 30 to about 70% by volume of abrasive granules selected from the group consisting of the refractory metal borides, carbides, nitrides, oxides, and mixtures thereof, and (2) from about 70 to about 30% by volume of an at least partially cured organic resin binder, said composite layer being formed by a first binder coat on said backing and forming said smooth surface, a coating of said abrasive granules deposited on said first binder coat in a non-aligned orientation and compacted in said first binder coat under pressure, and a second binder coat covering said granules, merging with said first binder coat and forming said uneven surface, said granules having a minimum particle size of about 50 microns with most of said granules being somewhat larger, a maximum dimension of not more than about twice their minimum dimension and somewhat smaller than the thickness of said sheet, and such diverse size that all of the largest 50% by weight of said granules have at least 30% greater maximum dimension than all of the smallest 10% by weight thereof.
Claim 2
Dependent Claim
246 words
An abrasion resistant, coated and abrasion containing, pipe lining sheet having a thickness of not less than about 0.75 mm, a backing side with a relatively uneven surface, and being sufficiently flexible to be wound backing side inward around a mandrel in building a pipe or within a pre-existing pipe, said sheet including a backing, and a composite layer on said backing and consisting essentially if: (1) from about 30 to about 70% by volume of abrasive granules selected from the group consisting of the refractory metal borides, carbides, nitrides, oxides, and mixtures thereof, and (2) from about 70 to about 30% by volume of an at least partially cured organic resin binder, said composite layer being formed by a first binder coat on said backing and forming said smooth surface, a coating of said abrasive granules deposited on said first binder coat in a non-aligned orientation and compacted in said first binder coat under pressure, and a second binder coat covering said granules, merging with said first binder coat and forming said uneven surface, said granules having a minimum particle size of about 50 microns with most of said granules being somewhat larger, a maximum dimension of not more than about twice their minimum dimension and somewhat smaller than the thickness of said sheet, and such diverse size that all of the largest 50% by weight of said granules have at least 30% greater maximum dimension than all of the smallest 10% by weight thereof.
Claim 3
Dependent Claim
27 words
The sheet of claim 1, wherein said backing is made of paper, textile or combinations thereof and is bonded to said smooth surface of said composite layer.
Claim 4
Dependent Claim
25 words
The sheet of claim 1, wherein said backing is made of non-absorbent, non-reactive film and is removable from said smooth surface of said composite layer.
Claim 5
Dependent Claim
17 words
The sheet of claim 1, including an adhesive layer on said uneven surface of said composite layer.
Claim 6
Dependent Claim
27 words
The sheet of claim 4, wherein said backing is made of paper, textiles or combinations thereof and is bonded to said smooth surface of said composite layer.
Claim 7
Dependent Claim
25 words
The sheet of claim 4 wherein said backing is made of non-absorbent, non-reactive film, and is removable from said smooth surface of said composite layer.
Claim 8
Dependent Claim
129 words
The sheet of claim 1 having a thickness of not more than about 3 cm, and wherein said composite layer consists essentially of: (1) from about 45 to about 55% by volume of said abrasive granules selected from the group consisting of silicon carbide, alumina, fused combinations of alumina and zirconia, and mixtures thereof, and (2) from about 55 to about 45% by volume of said organic resin binder selected from the group consisting of phenolic, polyurethane, polybutadiene-acrylonitrile, and epoxy resins, and said granules have a maximum dimension no more than about 1/2 the thickness of said sheet, and such diverse size that all of the largest 85% by weight of said granules have at least 50% greater maximum dimension than all of the smallest 10% by weight thereof.
Claim 9
Dependent Claim
27 words
The sheet of claim 7 wherein said backing is made of paper, textile or combinations thereof, and is bonded to said smooth surface of said composite layer.
Claim 10
Dependent Claim
26 words
The sheet of claim 7 wherein said backing is made of non-absorbent, non-reactive polyester film and is removable from said smooth surface of said composite layer.
Claim 11
Dependent Claim
17 words
The sheet of claim 7 including an adhesive layer on said uneven surface of said composite layer.
Claim 12
Dependent Claim
27 words
The sheet of claim 10 wherein said backing is made of paper, textiles, or combinations thereof and is bonded to said smooth surface of said composite layer.
Claim 13
Dependent Claim
25 words
The sheet of claim 10 wherein said backing is made of non-absorbent, non-reactive film and is removable from said smooth surface of said composite layer.
References Cited (Backward Citations)
US3360391A
Cited
US3295940A
Cited
US3306718A
Cited
US3498827A
Cited
US3846161A
Cited
US3787273A
Cited
US3876579A
Cited
US3864101A
Cited
US3836420A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-15 | 1981-02-14 | 1981-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-15 | 1985-02-14 | 1985-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-15 | 1989-02-14 | 1989-08-16 | $7700.00 | Window Closed / Lapsed |