Method for the manufacture of carbon-carbon composites
Assignee: Akzo NV
•
Filing: 1974-07-15
•
Granted: 1977-08-09
•
Expires: 1994-07-15
Abstract
Abstract A method for manufacturing carbon-carbon composite bodies consisting essentially exclusively of carbon, of about 20 to about 96 weight percent from carbon fiber, from 0 to about 72 weight percent from a carbonaceous flour, and from about 4 to about 15 weight percent from a carbonized resin, which consists in forming a mat by allowing a mixture of the solid ingredients to settle to equilibrium height by the force of gravity or by centrifugation in a solution of the resin and an appropriate solvent, then pressing the settled solids at up to about 100 psi and removing the excess liquid therefrom. Heating the formed and pressed mat to cure the resin, and then baking and optionally graphitizing the cured mat completes the process.
Inventors
- 👤 Michael F. Baud
- 👤 Jay A. Harvey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:08
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
202 words
A method for the manufacture of carbon mats consisting of carbon from about 20 to about 96 weight percent from carbon fiber, from 0 to about 72 weight percent from a carbonaceous flour, and from about 3 to about 15 weight percent from a carbonized resin which consists in: a. combining the appropriate quantities of carbon fibers of from 0.01 to 0.05 inches in length, a thermosetting resin and solvent therefor, and a carbonaceous flour so that the liquid to solid weight ratio is from about 50:1 to about 30:1, and the solvent to resin ratio is about 6:1 to about 20:1; b. allowing the solids to settle to equilibrium height in the liquid; c. pressing the settled solids at up to about 100 psi and removing the excess liquid therefrom by vacuum; d. heating the resulting mat to a sufficient temperature to cure the resin; and e. carbonizing the resulting mat by heating to a temperature between about 1000° C. to about 2800° C., to form a mat wherein the fibers are oriented randomly in the plane perpendicular to the direction of force used to settle the fibers and with no fibers oriented in the axis parallel to the settling force.
Claim 2
Independent Claim
202 words
A method for the manufacture of carbon mats consisting of carbon from about 20 to about 96 weight percent from carbon fiber, from 0 to about 72 weight percent from a carbonaceous flour, and from about 3 to about 15 weight percent from a carbonized resin which consists in: a. combining the appropriate quantities of carbon fibers of from 0.01 to 0.05 inches in length, a thermosetting resin and solvent therefor, and a carbonaceous flour so that the liquid to solid weight ratio is from about 50:1 to about 30:1, and the solvent to resin ratio is about 6:1 to about 20:1; b. allowing the solids to settle to equilibrium height in the liquid; c. pressing the settled solids at up to about 100 psi and removing the excess liquid therefrom by vacuum; d. heating the resulting mat to a sufficient temperature to cure the resin; and e. carbonizing the resulting mat by heating to a temperature between about 1000° C. to about 2800° C., to form a mat wherein the fibers are oriented randomly in the plane perpendicular to the direction of force used to settle the fibers and with no fibers oriented in the axis parallel to the settling force.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the carbonaceous flour component consists of thermatomic carbon.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the carbon fibers are of about 0.02 inches in length.
Claim 5
Dependent Claim
12 words
The method of claim 1 wherein the resin is a phenolic resin.
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein the settled mat is pressed at about 60 psi in step c).
Claim 7
Dependent Claim
18 words
The method of claim 1 wherein the settled mat is pressed at about 8 psi in step c).
Claim 8
Dependent Claim
15 words
The method of claim 1 wherein the solids are settled by the force of gravity.
Claim 9
Dependent Claim
15 words
The method of claim 1 wherein the solids are settled by the force of centrifugation.
References Cited (Backward Citations)
US3462289A
Cited
US3454691A
Cited
US3772115A
Cited
US3476703A
Cited
US3617437A
Cited
US3534803A
Cited
GB1232007A
Cited
US3573086A
Cited
US3790393A
Cited
US3720575A
Cited
US3671385A
Cited
US3708451A
Cited
US3793204A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |