High temperature alloys and members thereof
Assignee: Westinghouse Electric Corp
•
Filing: 1974-07-02
•
Granted: 1977-08-09
•
Expires: 1994-07-02
Abstract
Abstract An alloy consisting essentially of from about 14% to 19% chromium, from 25 to 35% of nickel, from about 2% to 3% molybdenum, from about 0.1% to 1% of silicon, up to 0.5% of manganese, from about 0.03 to 0.05% carbon, up to about 0.01% sulfur, up to about 0.01% of phosphorus, up to 0.01% boron, up to about 0.01% oxygen, up to about 0.02% nitrogen, small amounts of incidental impurities, and the balance being iron, the alloy having an Nv (average electron vacancy number) value of between 1.6 and 2.8, has an unexpected combination of properties enabling it to be formed by hot and cold working and heat treatment into components and members particularly suitable for use in nuclear reactors wherein the components are subjected to molten sodium, where the corrosion of the surface of the alloy is not in excess of the order of 1 to 2 mils per year, and the alloy exhibits low swelling when exposed to intense radiation, while exhibiting good physical properties at temperatures of up to 1325 DEG F. Worked and heat treated alloy members are usable as fuel cladding, grid supports, ducts and other sodium contacting in-core components that may be spaced in close predetermined relationship to ensure high reactor performance, particularly in breeder reactors, for the desired useful life thereof.
Inventors
- 👤 Melvin L. Bleiberg
- 👤 Sidney Diamond
- 👤 Arthur F. Rowcliffe
- 👤 John A. Spitznagel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 18:48
CPC Classifications
G; G21; G21C; G21C3/00; G21C3/02; G21C3/04; G21C3/06; G21C3/07; C; C22; C22C; C22C38/00; C22C38/18; C22C38/40; C22C38/44; Y; Y02; Y02E; Y02E30/00; Y02E30/30; Y10; Y10S; Y10S376/00; Y10S376/90
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
214 words
A shaped alloy member suitable for use in a nuclear reactor incorporating sodium wherein the member is in contact with the molten sodium at temperatures up to about 1325° F. and subject to high neutron flux, the alloy comprising said member consisting essentially of from about 14% to 19% chromium, from about 25% to 35% nickel, from about 2% to 3% molybdenum, from about 0.1% to 1% silicon, up to about 0.5% manganese, from about 0.03% to 0.05% carbon, up to about 0.01% sulphur, up to about 0.01% phosphorus, up to about 0.003% boron, up to about 0.01% oxygen, up to about 0.02% nitrogen, the balance being essentially iron with trace impurities with the N v value thereof being between 1.6 and 2.8, said alloy characterized by a low corrosion rate not in excess of from about 1 to 2 mils per year for the surfaces in contact with the sodium and further characterized by a low swelling not exceeding about 5% after exposure to 3 × 10 23 nvt, said shaped alloy member having been worked equivalent to from about 20% to 30% of cold working and heat treated to solution harden it and to develop high creep rupture strength and high yield strength at the temperatures of use in the nuclear reactor.
Claim 2
Dependent Claim
214 words
A shaped alloy member suitable for use in a nuclear reactor incorporating sodium wherein the member is in contact with the molten sodium at temperatures up to about 1325° F. and subject to high neutron flux, the alloy comprising said member consisting essentially of from about 14% to 19% chromium, from about 25% to 35% nickel, from about 2% to 3% molybdenum, from about 0.1% to 1% silicon, up to about 0.5% manganese, from about 0.03% to 0.05% carbon, up to about 0.01% sulphur, up to about 0.01% phosphorus, up to about 0.003% boron, up to about 0.01% oxygen, up to about 0.02% nitrogen, the balance being essentially iron with trace impurities with the N v value thereof being between 1.6 and 2.8, said alloy characterized by a low corrosion rate not in excess of from about 1 to 2 mils per year for the surfaces in contact with the sodium and further characterized by a low swelling not exceeding about 5% after exposure to 3 × 10 23 nvt, said shaped alloy member having been worked equivalent to from about 20% to 30% of cold working and heat treated to solution harden it and to develop high creep rupture strength and high yield strength at the temperatures of use in the nuclear reactor.
Claim 3
Dependent Claim
178 words
A metal member suitable for use as a component in a nuclear reactor imcorporating molten sodium as a medium in contact with the component during operation of the reactor, the member comprising an alloy worked to the equivalent of from about 20% to 30% cold working and solution hardened heat treated, the alloy being characterized by good creep rupture and high yield strength physical properties at elevated temperatures of up to 1325° F., low corrosion in molten sodium, and low swelling when subjected to nuclear irradiation, the alloy consisting essentially of from about 15% to 18% of chromium, from 25% to 35% of nickel, from about 2% to 3% of molybdenum as the solution hardener, from about 0.1% to 1% of silicon, from about 0.25% to 0.5% of manganese, from about 0.03 to 0.05% carbon, up to about 0.01% sulfur, up to about 0.01% phosphorus, up to 0.01% boron, up to about 0.01% oxygen, up to 0.02% nitrogen, small amounts of incidental impurities, and the balance being iron, with the N v value being between 1.6 and 2.8.
Claim 4
Dependent Claim
178 words
A metal member suitable for use as a component in a nuclear reactor imcorporating molten sodium as a medium in contact with the component during operation of the reactor, the member comprising an alloy worked to the equivalent of from about 20% to 30% cold working and solution hardened heat treated, the alloy being characterized by good creep rupture and high yield strength physical properties at elevated temperatures of up to 1325° F., low corrosion in molten sodium, and low swelling when subjected to nuclear irradiation, the alloy consisting essentially of from about 15% to 18% of chromium, from 25% to 35% of nickel, from about 2% to 3% of molybdenum as the solution hardener, from about 0.1% to 1% of silicon, from about 0.25% to 0.5% of manganese, from about 0.03 to 0.05% carbon, up to about 0.01% sulfur, up to about 0.01% phosphorus, up to 0.01% boron, up to about 0.01% oxygen, up to 0.02% nitrogen, small amounts of incidental impurities, and the balance being iron, with the N v value being between 1.6 and 2.8.
References Cited (Backward Citations)
US2403128A
Cited
US2879194A
Cited
US3065067A
Cited
US3199978A
Cited
US3592632A
Cited
US3582318A
Cited
US3837846A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |