Method for the conversion of crystalline silica raw materials into amorphous silica
Assignee: Individual
•
Filing: 1975-04-16
•
Granted: 1977-08-09
•
Expires: 1995-04-16
Abstract
Abstract The apparatus is a rotatable resistance heating furnace including a rotatable cylindrical body portion having an interior space in the form of a truncated cone. The base of the truncated cone forms a discharge opening for rapid discharge of the amorphous silica. The furnace is provided with a resistance heating element which extends into the furnace interior through a top opening. In one embodiment a slidable filling tube is provided for charging the furnace during rotation thereof. The process utilizes the above-described apparatus and involves heating the crystalline silica to a temperature sufficient to convert it to the amorphous state, evacuating the furnace during the conversion to draw off by-product gases, and rotating the furnace to a speed sufficient to bring about a separation between the silica charge and the resistance heating element.
Inventors
- 👤 Lothar Jung
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:18
CPC Classifications
C; C03; C03B; C03B5/00; C03B5/02; C03B5/033; C03B5/0338; H; H05; H05B; H05B3/00; H05B3/62; H05B3/64; Y; Y10; Y10S; Y10S65/00; Y10S65/08
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
178 words
In a process for the conversion of particulate crystalline silica into an amorphous silica mass by charging a furnace with the particulate crystalline silica and heating the charge to a temperature within the range of from about 1,728° to about 1,900° C. for a period of time sufficient to melt and convert the silica to the amorphous state while evacuating the furnace to draw off gaseous by-products and rotating the furnace at a speed sufficient to cause the silica charge to be forced against the furnace wall, wherein the furnace is a vertically mounted rotatable electric furnace provided with a central internal resistance heating element and with a cylindrical body portion having an interior surface defining an interior of a configuration approximating a truncated cone, the base of the cone defining a bottom discharge opening, the improvement comprising: cooling the amorphous silica mass within the furnace to a temperature within the range of 1,300°-1,400° C. to rigidify the mass and then rapidly discharging said cooled rigid mass through the furnace bottom by gravity to permit more rapid cooling.
Claim 2
Dependent Claim
178 words
In a process for the conversion of particulate crystalline silica into an amorphous silica mass by charging a furnace with the particulate crystalline silica and heating the charge to a temperature within the range of from about 1,728° to about 1,900° C. for a period of time sufficient to melt and convert the silica to the amorphous state while evacuating the furnace to draw off gaseous by-products and rotating the furnace at a speed sufficient to cause the silica charge to be forced against the furnace wall, wherein the furnace is a vertically mounted rotatable electric furnace provided with a central internal resistance heating element and with a cylindrical body portion having an interior surface defining an interior of a configuration approximating a truncated cone, the base of the cone defining a bottom discharge opening, the improvement comprising: cooling the amorphous silica mass within the furnace to a temperature within the range of 1,300°-1,400° C. to rigidify the mass and then rapidly discharging said cooled rigid mass through the furnace bottom by gravity to permit more rapid cooling.
Claim 3
Dependent Claim
63 words
The process of claim 1 wherein the furnace is filled with particulate silica and then heated to a temperature within the range of from about 1,728° to about 1,900° C. for a period of time sufficient to bring about a separation of the silica mass from the resistance heating element and wherein rotation is started at the end of said period of time.
Claim 4
Dependent Claim
63 words
The process of claim 1 utilizing a furnace additionally provided with an axially movable filling tube and wherein rotation of the furnace is started prior to charging the particulate silica through said filling tube, said process further comprising withdrawing the filling tube from the furnace during charging so as to deposit the particulate silica along the length of the interior of the furnace.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein the amorphous silica is discharged into a cooling tank.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |