Process for isomerizing alkenes
Assignee: SnamProgetti SpA
•
Filing: 1975-08-01
•
Granted: 1977-07-26
•
Expires: 1995-08-01
Abstract
Abstract The invention relates to the skeleton isomerization of alkenes and, more particularly, to the catalyst for the isomerization reaction, the catalyst being prepared by treating an oxide of a metal of the group comprising aluminium, titanium, magnesium, silicon, chrome, zirconium, iron and their mixtures, preferably an active alumina, with a silicon compound, preferably an alkyl ester of the orthosilicic acid, and then subjecting the thus treated oxide to drying and to a controlled oxidation. Thus catalyst is obtained which permits higher yields and selectivity of the isomerization reaction to be achieved, as well as a longer operative life of the catalyst before the regeneration thereof.
Inventors
- 👤 Giovanni Manara
- 👤 Vittorio Fattore
- 👤 Bruno Notari
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 03:40
CPC Classifications
C; C07; C07C; C07C5/00; C07C5/22; C07C5/2206; C07C5/2213; B; B01; B01J; B01J37/00; B01J37/08; B01J37/082; B01J21/00; B01J21/12; B01J37/02; B01J37/0201; B01J37/0209; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/584; Y10; Y10S; Y10S585/00; Y10S585/8995; Y10S585/906
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
106 words
A process for the skeleton isomerization of alkenes which comprises contacting an alkene having at least four carbon atoms or a mixture of alkenes having at least four carbon atoms with a catalyst consisting essentially of alumina previously treated with a silicon compound having the formula ##STR2## wherein X, Y, Z and W are selected from the group of --R, --OR, --Cl, --Br, --SiH 3 , --COOR, --SiH n Cl m , R being either hydrogen or an alkyl, cycloalkyl, aromatic, alkyl-aromatic or alkyl-cycloalkyl radical having from 1 to 30 carbon atoms, n and m being whole numbers in the range of from 1 to 3.
Claim 2
Dependent Claim
106 words
A process for the skeleton isomerization of alkenes which comprises contacting an alkene having at least four carbon atoms or a mixture of alkenes having at least four carbon atoms with a catalyst consisting essentially of alumina previously treated with a silicon compound having the formula ##STR2## wherein X, Y, Z and W are selected from the group of --R, --OR, --Cl, --Br, --SiH 3 , --COOR, --SiH n Cl m , R being either hydrogen or an alkyl, cycloalkyl, aromatic, alkyl-aromatic or alkyl-cycloalkyl radical having from 1 to 30 carbon atoms, n and m being whole numbers in the range of from 1 to 3.
Claim 3
Dependent Claim
23 words
The process of claim 1 wherein R is a methyl, ethyl, isopropyl, n-propyl, n-butyl, isobutyl, cyclohexyl, cyclopentyl, phenyl, phenyl cyclohexyl or alkylphenyl radical.
Claim 4
Dependent Claim
17 words
The process of claim 2 wherein R is a methyl, ethyl, n-propyl, isopropyl, isobutyl or n-butyl radical.
Claim 5
Dependent Claim
24 words
The process of claim 1 wherein the silicon compound is selected from the group of the methyl, ethyl, n-propyl, isopropyl, isobutyl and n-butyl tetrasilicates.
Claim 6
Dependent Claim
11 words
The process of claim 4 wherein the silicon compound is tetraethylorthosilicate.
Claim 7
Dependent Claim
25 words
The process of claim 1 wherein the alumina has deposited thereon from 0.5 to 12% of silica, based on the total weight of the catalyst.
Claim 8
Dependent Claim
25 words
A process of claim 6 wherein the alumina has deposited thereon from 1 to 7% of silica, based on the total weight of the catalyst.
Claim 9
Dependent Claim
22 words
The process of claim 1 wherein the process is carried out at temperatures in the range of from 300° to 600° C.
Claim 10
Dependent Claim
21 words
The process of claim 8 wherein the process is carried out at temperatures in the range of 400° to 550° C.
Claim 11
Dependent Claim
20 words
The process of claim 1 wherein the process is carried out at a pressure ranging from one to ten atmospheres.
Claim 12
Dependent Claim
21 words
The process of claim 1 wherein the process is carried out at a feeding space velocity ranging from 0.1 to 20.
Claim 13
Dependent Claim
21 words
The process of claim 11 wherein the process is carried out at a feeding space velocity ranging from 0.2 to 10.
Claim 14
Dependent Claim
18 words
The process of claim 1 wherein the alkene is butene, in a gas mixture consisting essentially of butene.
Claim 15
Dependent Claim
18 words
The process of claim 1 wherein the alkene is pentene, in a gas mixture consisting essentially of pentane.
Claim 16
Dependent Claim
113 words
A process for the skeleton isomerization of alkenes which comprises contacting an alkene having at least four carbon atoms or a mixture of alkenes having at least four carbon atoms with a catalyst consisting essentially of alumina previously treated with a silicon compound having the formula ##STR3## wherein X, Y, Z and W are selected from the group of --R, --OR, --Cl, --Br, --SiH 3 , -- COOR, --SiH n Cl m , R being either hydrogen or a methyl, ethyl, isopropyl, n-propyl, n-butyl, isobutyl, cyclohexyl, cyclopentyl, phenyl, phenyl cyclohexyl or alkylphenyl radical having up to 30 carbon atoms, n and m being whole numbers in the range of from 1 to 3.
Claim 17
Dependent Claim
113 words
A process for the skeleton isomerization of alkenes which comprises contacting an alkene having at least four carbon atoms or a mixture of alkenes having at least four carbon atoms with a catalyst consisting essentially of alumina previously treated with a silicon compound having the formula ##STR3## wherein X, Y, Z and W are selected from the group of --R, --OR, --Cl, --Br, --SiH 3 , -- COOR, --SiH n Cl m , R being either hydrogen or a methyl, ethyl, isopropyl, n-propyl, n-butyl, isobutyl, cyclohexyl, cyclopentyl, phenyl, phenyl cyclohexyl or alkylphenyl radical having up to 30 carbon atoms, n and m being whole numbers in the range of from 1 to 3.
Claim 18
Dependent Claim
59 words
A process for producing isobutene which comprises contacting butene at temperatures of from 300° to 600° C. and at a pressure of from one to ten atmospheres with a catalyst consisting essentially of alumina previously treated with tetraethylorthosilicate to deposit thereon silica in an amount of from 0.5 to 12% by weight based on the weight of the catalyst.
Claim 19
Dependent Claim
59 words
A process for producing isobutene which comprises contacting butene at temperatures of from 300° to 600° C. and at a pressure of from one to ten atmospheres with a catalyst consisting essentially of alumina previously treated with tetraethylorthosilicate to deposit thereon silica in an amount of from 0.5 to 12% by weight based on the weight of the catalyst.
Claim 20
Dependent Claim
28 words
The process of claim 16 wherein the silica is deposited in an amount of from 1 to 7% by weight based on the total weight of the catalyst.
Claim 21
Dependent Claim
61 words
A process for producing linear butenes which comprises contacting isobutene at a temperature of from 300° to 600° C. and at a pressure of from one to ten atmospheres with a catalyst consisting essentially of alumina previously treated with tetraethylorthosilicate to deposit thereon silica in an amount of from 0.5 to 12% by weight based on the weight of the catalyst.
Claim 22
Dependent Claim
61 words
A process for producing linear butenes which comprises contacting isobutene at a temperature of from 300° to 600° C. and at a pressure of from one to ten atmospheres with a catalyst consisting essentially of alumina previously treated with tetraethylorthosilicate to deposit thereon silica in an amount of from 0.5 to 12% by weight based on the weight of the catalyst.
Claim 23
Dependent Claim
28 words
The process of claim 18 wherein the silica is deposited in an amount of from 1 to 7% by weight based on the total weight of the catalyst.
Claim 24
Dependent Claim
60 words
A process for producing isopentenes which comprises contacting pentene at a temperature of from 300° to 600° C. and at a pressure of from one to ten atmospheres with a catalyst consisting essentially of alumina previously treated with tetraethylorthosilicate to deposit thereon silica in an amount of from 0.5 to 12% by weight based on the weight of the catalyst.
Claim 25
Dependent Claim
60 words
A process for producing isopentenes which comprises contacting pentene at a temperature of from 300° to 600° C. and at a pressure of from one to ten atmospheres with a catalyst consisting essentially of alumina previously treated with tetraethylorthosilicate to deposit thereon silica in an amount of from 0.5 to 12% by weight based on the weight of the catalyst.
Claim 26
Dependent Claim
28 words
The process of claim 20 wherein the silica is deposited in an amount of from 1 to 7% by weight based on the total weight of the catalyst.
References Cited (Backward Citations)
US2242387A
Cited
US2328753A
Cited
US2280054A
Cited
US2300151A
Cited
US2322622A
Cited
US2483131A
Cited
US3213156A
Cited
US3345428A
Cited
US3698157A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |