Amorphous precipitated siliceous pigments for cosmetic or dentrifice use and methods for their production
Assignee: JM Huber Corp
•
Filing: 1975-12-22
•
Granted: 1977-07-26
•
Expires: 1995-12-22
Abstract
Abstract A method for producing precipitated silicic acid pigments and silicates having a unique combination of physical and chemical properties is disclosed. The pigments are produced by acidulating alkali metal silicate solutions which contain a salt or electrolyte, such as sodium sulfate, which serves to pre-polymerize the said silicate solution. Pigments produced in accordance with the invention exhibit lower wet cake moisture (or higher percent solids) and are characterized by their low structure, low oil absorption, high abrasiveness and high pack density. The products can be used as abrasive and polishing agents in dentifrice compositions, in the production of molecular sieves, in paints and the like. In a particularly advantageous embodiment, an adduct material, such as aluminum, is added to control the refractive index of the precipitated pigment.
Inventors
- 👤 Satish K. Wason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:43
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/20; C01B33/36; C01B33/46; A; A61; A61K; A61K8/00; A61K8/18; A61K8/19; A61K8/25; A61Q; A61Q11/00; C01B33/113; C01B33/12; C01B33/18; C01B33/187; C01B33/193; C01B33/22; C01B33/24; C01B33/26; C01B33/38; C01B33/40; C01B33/42; C09; C09D; C09D7/00; C09D7/40; C09D7/42; A61K2800/00; A61K2800/40; A61K2800/42; A61K2800/43; C01P; C01P2002/00; C01P2002/02; C01P2004/00; C01P2004/51; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/19; C01P2006/80; C01P2006/82; C01P2006/90
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
99 words
A method for producing an amorphous precipitated silicic acid having improved chemical and physical properties including high abrasiveness and low wet cake moisture content prior to the drying thereof, said process comprising the steps of: 1. contacting an aqueous solution of an alkali metal silicate with an alkali or alkaline earth metal salt to prepolymerize said alkali metal silicate and form an aqueous solution of prepolymerized alkali metal silicate solution; 2. combining an acid with an adduct material selected from the group consisting of the water soluble salts of aluminum and alkaline earth metals to form an acidulating solution;
Claim 2
Independent Claim
99 words
A method for producing an amorphous precipitated silicic acid having improved chemical and physical properties including high abrasiveness and low wet cake moisture content prior to the drying thereof, said process comprising the steps of: 1. contacting an aqueous solution of an alkali metal silicate with an alkali or alkaline earth metal salt to prepolymerize said alkali metal silicate and form an aqueous solution of prepolymerized alkali metal silicate solution; 2. combining an acid with an adduct material selected from the group consisting of the water soluble salts of aluminum and alkaline earth metals to form an acidulating solution;
Claim 3
Dependent Claim
83 words
acidulating said prepolymerized aqueous alkali metal silicate solution with said acidulating solution by addition of the solution to said prepolymerized silicate solution; 4. continuing the addition of said acidulation solution to said aqueous silicate solution until the precipitation of said silicic acid is complete; and 5. separating and recovering the precipitated silicic acid; wherein said adduct material combined with said mineral acid is effective to control the refractive index of the precipitated silicic acid and form an alumino or alkaline earth metal silicate.
Claim 4
Dependent Claim
83 words
acidulating said prepolymerized aqueous alkali metal silicate solution with said acidulating solution by addition of the solution to said prepolymerized silicate solution; 4. continuing the addition of said acidulation solution to said aqueous silicate solution until the precipitation of said silicic acid is complete; and 5. separating and recovering the precipitated silicic acid; wherein said adduct material combined with said mineral acid is effective to control the refractive index of the precipitated silicic acid and form an alumino or alkaline earth metal silicate.
Claim 5
Dependent Claim
20 words
The method in accordance with claim 1, said method further comprising the steps of drying and disintegrating the precipitated material.
Claim 6
Dependent Claim
50 words
The method in accordance with claim 1 wherein said acid is a mineral acid selected from the group consisting of sulfuric acid, nitric acid and hydrochloric acid and said salt used to prepolymerize said silicate solution is a salt of the said sulfuric acid, nitric acid or hydrochloric acid, respectively.
Claim 7
Dependent Claim
26 words
The method in accordance with claim 3 wherein said alkali metal silicate is selected from the group consisting of sodium silicate, potassium silicate and lithium silicate.
Claim 8
Dependent Claim
43 words
The method in accordance with claim 4 wherein said alkali metal silicate has a SiO 2 /X 2 O mol ratio in the range of from about 1.0 to 3.0 wherein X is selected from the group consisting of sodium, potassium and lithium.
Claim 9
Dependent Claim
27 words
The method in accordance with claim 1 wherein said adduct material is selected from the group consisting of the water soluble salts of aluminum, magnesium and calcium.
Claim 10
Dependent Claim
21 words
The method in accordance with claim 6 wherein said adduct material is aluminum sulfate and said mineral acid is sulfuric acid.
Claim 11
Dependent Claim
9 words
The product produced by the process of claim 1.
Claim 12
Dependent Claim
9 words
The product produced by the process of claim 7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-25 | 1981-01-24 | 1981-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-25 | 1985-01-24 | 1985-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-25 | 1989-01-24 | 1989-07-26 | $7700.00 | Window Closed / Lapsed |