Polyurethane precursors containing thixotropic agents
Assignee: Chevron USA Inc
•
Filing: 1973-09-10
•
Granted: 1977-07-19
•
Expires: 1993-09-10
Abstract
Abstract Polyurethane-forming compositions comprise (a) a polyurethane precursor, (b) a substantially inert, non-volatile extender, (c) a thixotropic agent formed by reacting a long chain primary or secondary monoamine and a polyisocyanate at a NCO/amine ratio of 0.1-1.05:1 and optionally (d) one or more inert fillers.
Inventors
- 👤 Arthur L. Meader, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 11:12
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/2805; C08G18/285; C08G18/2865; C08K; C08K5/00; C08K5/16; C08K5/17; C08K5/21
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
174 words
A composition comprising: A. 18 to 50 weight percent of a polyurethane precursor, said precursor comprising: 1. a polyol having a molecular weight of 1500 to 5000, and 2. a chain stiffener having a molecular weight of 62 to 300, wherein the mole ratio of the isocyanate-reactive groups of said low molecular weight chain stiffener to the isocyanate-reactive groups of said polyol is 0.5-4:1, B. 80 to 30 weight percent of a substantially inert, non-volatile extender, selected from the group consisting of cutback asphalts, mineral oils, and mixtures thereof, C. 0.1 to 8 weight percent of a thixotropic agent formed in situ by reacting a mixture of primary mono and diamines wherein the monoamine is a monofunctional monoamine containing 6 to 30 carbon atoms and the diamines are selected from the group consisting of a methyl imine bis(propylamine), ethylene diamine and mixtures thereof, wherein the mol ratio of monoamines to diamines is 20-1:1 diamines, and a polyisocyanate at an NCO/NH ratio of 0.10-1.3:1, and D. 0 to 20 weight percent of an inert filler.
Claim 2
Dependent Claim
174 words
A composition comprising: A. 18 to 50 weight percent of a polyurethane precursor, said precursor comprising: 1. a polyol having a molecular weight of 1500 to 5000, and 2. a chain stiffener having a molecular weight of 62 to 300, wherein the mole ratio of the isocyanate-reactive groups of said low molecular weight chain stiffener to the isocyanate-reactive groups of said polyol is 0.5-4:1, B. 80 to 30 weight percent of a substantially inert, non-volatile extender, selected from the group consisting of cutback asphalts, mineral oils, and mixtures thereof, C. 0.1 to 8 weight percent of a thixotropic agent formed in situ by reacting a mixture of primary mono and diamines wherein the monoamine is a monofunctional monoamine containing 6 to 30 carbon atoms and the diamines are selected from the group consisting of a methyl imine bis(propylamine), ethylene diamine and mixtures thereof, wherein the mol ratio of monoamines to diamines is 20-1:1 diamines, and a polyisocyanate at an NCO/NH ratio of 0.10-1.3:1, and D. 0 to 20 weight percent of an inert filler.
Claim 3
Dependent Claim
17 words
The composition of claim 1 wherein said mole ratio of said monoamines to said diamines is 10-5:1.
Claim 4
Dependent Claim
42 words
The composition of claim 2 containing 1 mole of isocyanate groups from said polyisocyanate per mole of isocyanate reactive amine groups and 0.5 to 2.3 moles of isocyanate groups from a polyisocyanate per mole of isocyanate reactive groups of said polyurethane precursor.
Claim 5
Dependent Claim
24 words
The composition of claim 1 wherein said monoamine is selected from tall oil fatty amine and dodecylaniline and said diamine is methyl imino bis(propylamine).
Claim 6
Dependent Claim
24 words
The composition of claim 1 wherein said monoamine is selected from tall oil fatty amine and dodecylaniline and wherein said diamine is ethylene diamine.
Claim 7
Dependent Claim
30 words
A composition comprising: A. 18 to 50 weight percent of a polyurethane precursor, said precursor comprising: 1. a high molecular weight polyol, and 2. a low molecular weight chain stiffener,
Claim 8
Dependent Claim
30 words
A composition comprising: A. 18 to 50 weight percent of a polyurethane precursor, said precursor comprising: 1. a high molecular weight polyol, and 2. a low molecular weight chain stiffener,
Claim 9
Dependent Claim
130 words
wherein the mole ratio of the isocyanate reactive groups of said low molecular weight chain stiffener to the isocyanate reactive groups of said high molecular weight polyol is 0.5-4:1, B. 80 to 30 weight percent of a substantially inert, non-volatile extender, selected from the group consisting of cutback asphalts, mineral oils, and mixtures thereof, C. 0.1 to 8 weight percent of a thixotropic agent formed in situ by reacting a mixture of (1) primary or secondary monofunctional monoamines containing 6 to 30 carbon atoms and (2) diamines selected from the group consisting of methyl imino bis(propylamine), ethylene diamine and mixtures thereof, and a polyisocyanate at a NCO/NH ratio of 0.10-1.3:1 and a monoamine to diamine mole ratio of 20-1:1, and D. 0 to 20 weight percent of an inert filler.
Claim 10
Dependent Claim
130 words
wherein the mole ratio of the isocyanate reactive groups of said low molecular weight chain stiffener to the isocyanate reactive groups of said high molecular weight polyol is 0.5-4:1, B. 80 to 30 weight percent of a substantially inert, non-volatile extender, selected from the group consisting of cutback asphalts, mineral oils, and mixtures thereof, C. 0.1 to 8 weight percent of a thixotropic agent formed in situ by reacting a mixture of (1) primary or secondary monofunctional monoamines containing 6 to 30 carbon atoms and (2) diamines selected from the group consisting of methyl imino bis(propylamine), ethylene diamine and mixtures thereof, and a polyisocyanate at a NCO/NH ratio of 0.10-1.3:1 and a monoamine to diamine mole ratio of 20-1:1, and D. 0 to 20 weight percent of an inert filler.
Claim 11
Dependent Claim
17 words
The composition of claim 6 wherein said high molecular weight polyol has a molecular weight of 1500-5000.
Claim 12
Dependent Claim
18 words
The composition of claim 7 wherein said low molecular weight chain stiffener has a molecular weight of 62-300.
Claim 13
Dependent Claim
18 words
The composition of claim 8 wherein said long chain primary or secondary monoamine contains from 12-30 carbon atoms.
Claim 14
Dependent Claim
27 words
The composition of claim 9 wherein said high molecular weight polyol is selected from polybutadiene diols, polyisoprene diols, polybutadiene-styrene diols, polybutadieneacrylonitrile diols, polypropylene glycols, and mixtures thereof.
Claim 15
Dependent Claim
14 words
The composition of claim 10 wherein said long chain monoamine is a primary monoamine.
References Cited (Backward Citations)
US2955056A
Cited
US3243372A
Cited
US3369000A
Cited
US3388100A
Cited
US3284357A
Cited
US3346497A
Cited
US3637558A
Cited
US3714110A
Cited
US3489723A
Cited
US3401027A
Cited
US3615802A
Cited
US3743617A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-18 | 1981-01-17 | 1981-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-18 | 1985-01-17 | 1985-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-18 | 1989-01-17 | 1989-07-19 | $7700.00 | Window Closed / Lapsed |