⏱️ 0.0 years remaining
Dual cure cathodic electrocoating
Assignee: SCM Corp
•
Filing: 1976-05-24
•
Granted: 1977-07-12
•
Expires: 1996-05-24
Abstract
Abstract An electrocoating composition containing a polymer having pendant tertiary amine groups, a polymer containing pendant mercaptan groups, an alpha-,beta-ethylenically unsaturated carbonyl cross-linking agent, and a photosensitizer can be electrodeposited onto a cathode substrate disposed within an aqueous electrocoating bath. Full cure of the electrodeposited coating on the cathode substrate is obtained by the combination of heat curing and ultraviolet radiation curing. In a specific embodiment of the present invention, a single polymer contains both the pendant tertiary amine groups and pendant mercaptan groups.
Inventors
- 👤 Vincent Daniel McGinniss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:35
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4473; C09D5/4488; Y; Y10; Y10S; Y10S522/00; Y10S522/904; Y10S524/00; Y10S524/901; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31529; Y10T428/31678
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
226 words
A process for electrodeposition of an electrocoating composition dispersed within an aqueous electrocoating bath onto a cathode substrate dispersed within said bath to form a curable electrodeposited coating on said cathode substrate, which comprises: cathodically electrodepositing said electrocoating composition onto said cathode substrate under cathodic electrocoating conditions, said electrocoating composition comprising comprising: (a) a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups; (b) a water-dispersed electrocoating polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer; (c) at least about 5% by weight of said polymers of an alpha-,beta-ethylenically unsaturated carbonyl cross-linking agent having at least two alpha-,beta-ethylenically unsaturated carbonyl groups; and (d) at least about 0.5% ultraviolet photosensitizer by weight of said polymers, said pendant tertiary amine groups and said pendant mercaptan groups together comprising at least about 5% by weight of both said polymers; and curing said electrodeposited coating on said cathode substrate by heating said electrodeposited coating on said cathode substrate to cross-link said polymer having pendant mercaptan groups with said cross-linking agent to partially cure said coating, followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon of said polymer having pendant amine groups with said cross-linking agent to fully cure said coating on said cathode substrate.
Claim 2
Dependent Claim
226 words
A process for electrodeposition of an electrocoating composition dispersed within an aqueous electrocoating bath onto a cathode substrate dispersed within said bath to form a curable electrodeposited coating on said cathode substrate, which comprises: cathodically electrodepositing said electrocoating composition onto said cathode substrate under cathodic electrocoating conditions, said electrocoating composition comprising comprising: (a) a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups; (b) a water-dispersed electrocoating polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer; (c) at least about 5% by weight of said polymers of an alpha-,beta-ethylenically unsaturated carbonyl cross-linking agent having at least two alpha-,beta-ethylenically unsaturated carbonyl groups; and (d) at least about 0.5% ultraviolet photosensitizer by weight of said polymers, said pendant tertiary amine groups and said pendant mercaptan groups together comprising at least about 5% by weight of both said polymers; and curing said electrodeposited coating on said cathode substrate by heating said electrodeposited coating on said cathode substrate to cross-link said polymer having pendant mercaptan groups with said cross-linking agent to partially cure said coating, followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon of said polymer having pendant amine groups with said cross-linking agent to fully cure said coating on said cathode substrate.
Claim 3
Dependent Claim
46 words
The electrodeposition process of claim 1 wherein said polymer having pendant amine groups is dispersed in said bath by protonating said amine groups with proton-donating acid, said protonated amine groups becoming deprotonated upon electrodeposition of said polymer having said protonated amine groups onto said cathode substrate.
Claim 4
Dependent Claim
37 words
The electrodeposition process of claim 1 wherein said polymer having pendant mercaptan groups is dispersed in said bath by the addition of alkyl halide or halogen thereto to form pendant sulfonium ion groups from said mercaptan groups.
Claim 5
Dependent Claim
30 words
The electrodeposition process of claim 1 wherein said polymer having pendant mercaptan groups contains between about 1% and about 4% by weight of said polymer of said pendant mercaptan groups.
Claim 6
Dependent Claim
22 words
The electrodeposition process of claim 1 wherein said electrocoating composition additionally contains an ethylenically unsaturated compound having a multiplicity of ethylenic unsaturation.
Claim 7
Dependent Claim
22 words
The electrodeposition process of claim 1 wherein said cross-linking agent is an acrylate cross-linking agent having at least two pendant acrylate groups.
Claim 8
Dependent Claim
22 words
The electrodeposition process of claim 1 wherein said cross-linking agent is an acrylamide cross-linking agent having at least two pendant acrylamide groups.
Claim 9
Dependent Claim
33 words
A cathode substrate having thereon an electrodeposited coating from the electrocoating process of claim 1, said coating having been cured by heating followed by ultraviolet irradiation of said coating on said cathode substrate.
Claim 10
Dependent Claim
210 words
A process for electrodeposition of an electrocoating composition dispersed within an aqueous electrocoating bath onto a cathode substrate dispersed within said bath to form a curable electrodeposited coating on said cathode substrate, which comprises: cathodically electrodepositing said electrocoating composition onto said cathode substrate under cathodic electrocoating conditions, said electrocoating composition comprising: (a) a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups and said polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer, the total proportion of both said amine groups and said mercaptan groups being at least about 5% by weight of said polymer; (b) at least about 5% by weight of said polymers of an alpha-,beta-ethylenically unsaturated carbonyl cross-linking agent having at least two alpha-,beta-ethylenically unsaturated carbonyl groups; and (c) at least about 0.5% ultraviolet photosensitizer by weight of said polymer; and curing said electrodeposited coating on said cathode substrate by heating said electrodeposited coating to cross-link said pendant mercaptan groups with said cross-linking agent to partially cure said coating, followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon with said cross-linking agent to fully cure said coating on said cathode substrate.
Claim 11
Dependent Claim
210 words
A process for electrodeposition of an electrocoating composition dispersed within an aqueous electrocoating bath onto a cathode substrate dispersed within said bath to form a curable electrodeposited coating on said cathode substrate, which comprises: cathodically electrodepositing said electrocoating composition onto said cathode substrate under cathodic electrocoating conditions, said electrocoating composition comprising: (a) a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups and said polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer, the total proportion of both said amine groups and said mercaptan groups being at least about 5% by weight of said polymer; (b) at least about 5% by weight of said polymers of an alpha-,beta-ethylenically unsaturated carbonyl cross-linking agent having at least two alpha-,beta-ethylenically unsaturated carbonyl groups; and (c) at least about 0.5% ultraviolet photosensitizer by weight of said polymer; and curing said electrodeposited coating on said cathode substrate by heating said electrodeposited coating to cross-link said pendant mercaptan groups with said cross-linking agent to partially cure said coating, followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon with said cross-linking agent to fully cure said coating on said cathode substrate.
Claim 12
Dependent Claim
22 words
The electrodeposition process of claim 9 wherein said cross-linking agent is an acrylate cross-linking agent having at least two pendant acrylate groups.
Claim 13
Dependent Claim
22 words
The electrodeposition process of claim 9 wherein said cross-linking agent is an acrylamide cross-linking agent having at least two pendant acrylamide groups.
Claim 14
Dependent Claim
33 words
A cathode substrate having thereon an electrodeposited coating from the electrocoating process of claim 9, said coating having been cured by heating followed by ultraviolet irradiation of said coating on said cathode substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-11 | 1981-01-10 | 1981-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-11 | 1985-01-10 | 1985-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-11 | 1989-01-10 | 1989-07-12 | $7700.00 | Window Closed / Lapsed |