Method of patterning Cr-Pt-Au metallization for silicon devices

Assignee: Texas Instruments Inc
•
Filing: 1976-11-01
•
Granted: 1977-07-12
•
Expires: 1996-11-01
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract The disclosure relates to patterning of platinum effectively and then removing the mask from the platinum without attacking the chromium metal beneath the platinum. If tantalum is used on top, which metal can be patterned with CF 4 , the tantalum can be patterned and the platinum can then be patterned quite readily and the tantalum can then be removed with the CF 4 again and then the gold can be plated up onto the platinum patterns and the chromium can then be etched out using conventional chromium etch which will not attack any of the other metals. This solves the problem of high yield patterning with a metal mask and process for patterning and removal of that metal mask that is compatible with the chromium-platinum metal system. The advantage of the chromium-platinum system over the titanium-platinum system is the resistance of the chromium to silicon etch. Therefore, the principal application of this invention would be in the fabrication of mesa devices.

Inventors

  • 👤 Clyde Rhea Fuller
  • 👤 Barry William Battershall

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-05 11:43
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/60; H10P50/66; H10P50/663; H10P50/667; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H10W20/40; H10W20/41; H10W20/44; H10W20/4403

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 98 words
A method of forming a patterned platinum layer over a chromium layer which comprises the steps of: (a) forming a layer of platinum over said chromium layer, (b) forming a layer of tantalum over said platinum, (c) patterning said tantalum by a plasma-vapor etch to form a mask over said platinum, (d) patterning said platinum through said tantalum mask, (e) removing the remaining tantalum by a CF 4 plasmavapor etch, whereby the initial chromium layer is left intact due to the selectivity of the CF 4 plasma-vapor etch for tantalum, and (f) selectively plating gold onto the platinum.
Claim 2
Independent Claim 98 words
A method of forming a patterned platinum layer over a chromium layer which comprises the steps of: (a) forming a layer of platinum over said chromium layer, (b) forming a layer of tantalum over said platinum, (c) patterning said tantalum by a plasma-vapor etch to form a mask over said platinum, (d) patterning said platinum through said tantalum mask, (e) removing the remaining tantalum by a CF 4 plasmavapor etch, whereby the initial chromium layer is left intact due to the selectivity of the CF 4 plasma-vapor etch for tantalum, and (f) selectively plating gold onto the platinum.
Claim 3
Dependent Claim 17 words
A method as set forth in claim 1 wherein said layers are formed on a semiconductor slice.
Claim 4
Dependent Claim 19 words
A method as set forth in claim 2 wherein said tantalum layer is patterned using a CF 4 etch.
Claim 5
Dependent Claim 17 words
A method as set forth in claim 2 wherein said platinum layer is patterned using aqua regia.
Claim 6
Dependent Claim 17 words
A method as set forth in claim 3 wherein said platinum layer is patterned using aqua regia.
Claim 7
Dependent Claim 19 words
A method as set forth in claim 1 wherein said tantalum layer is patterned using a CF 4 etch.
Claim 8
Dependent Claim 17 words
A method as set forth in claim 6 wherein said platinum layer is patterned using aqua regia.
Claim 9
Dependent Claim 17 words
A method as set forth in claim 1 wherein said platinum layer is patterned using aqua regia.

References Cited (Backward Citations)

US3386894A Cited
US3657029A Cited
US3642548A Cited
US3795557A Cited
US3900944A Cited
US3951709A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1980-07-11 1981-01-10 1981-07-12 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1984-07-11 1985-01-10 1985-07-12 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1988-07-11 1989-01-10 1989-07-12 $7700.00 Window Closed / Lapsed