Stress-crack resistant ethylene-perhaloethylene terpolymers

Claim 2

Terpolymers of from about 40 to 60 mol percent ethylene, from about 60 to about 40 mol percent of a halogenated comonomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene and mixtures thereof and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, a vinyl monomer selected from the group consisting of fluorinated alpha-monoolefins, and monomers of the formula R-- CF=CF 2 ; ROCF=CF 2 ; CF 3 (CF 2 ) m CH 2 OCF=CF 2 ; CH 3 (CH 2 ) n OCF=CF 2 ; R'CH 2 (X)=CH 2 and R 2 OCH 2 C(X)=CH 2 , wherein R is an organic group containing 2 to 8 carbon atoms, R' is a perfluorinated or chlorofluoroalkyl group of 1 to 7 carbon atoms or a secondary or tertiary halo-alcohol group, R 2 is a perfluorinated or chlorofluoroalkyl of 1 to 7 carbon atoms, X is H or CH 3 , m is an integer of 0 to 6 and n is an integer of 1 to 7, and mixtures thereof, and containing high and low molecular weight components of said terpolymers such that equations (1) and (2) are satisfied: ##EQU11## wherein X i represents the weight fraction of each high molecular weight component, Mw represents the weight-average molecular weight of the terpolymer, Mw i represents the weight-average molecular weight of each component i, ##EQU12## wherein X j represents the weight fraction of each low molecular weight component, Mw j represents the weight-average molecular weight of each component j, and

Claim 3

1≦ f≦ 0.95, the high molecular components having a weight-average molecular weight, expressed in terms of melt index of from about 0.0001 to 1.0 and the low molecular weight components having a weight-average molecular weight, expressed in terms of melt index of from about 3 to 3000 and therefore wherein said terpolymers contain from 0.2 to 57 weight percent of said high molecular weight components and from 99.8 to 43 weight percent of said low molecular weight components.

Claim 4

1≦ f≦ 0.95, the high molecular components having a weight-average molecular weight, expressed in terms of melt index of from about 0.0001 to 1.0 and the low molecular weight components having a weight-average molecular weight, expressed in terms of melt index of from about 3 to 3000 and therefore wherein said terpolymers contain from 0.2 to 57 weight percent of said high molecular weight components and from 99.8 to 43 weight percent of said low molecular weight components.

Claim 5

Terpolymers in accordance with claim 1 wherein said halogenated comonomer is chlorotrifluoroethylene.

Claim 6

Terpolymers in accordance with claim 2 containing from about 5 to about 50 weight percent of a high molecular weight component which has a melt index of from about 0.005 to about 0.5.

Claim 7

Terpolymers in accordance with claim 3 wherein said high molecular weight component has a melt index in the range of about 0.005 to about 0.2.

Claim 8

Terpolymers in accordance with claim 4 containing from about 45 to about 55 mol percent of ethylene, from about 55 to about 45 mol percent of chlorotrifluoroethylene and wherein said termonomer is 3,3,3-trifluoro-2-trifluoromethyl propene.

Claim 9

Terpolymers in accordance with claim 5 wherein said termonomer is present in an amount of about 0.5 to 5 mol percent.

Claim 10

Terpolymers in accordance with claim 1 wherein ##EQU13##

Claim 11

Terpolymers of from about 40 to 60 mol percent ethylene and from about 60 to 40 mol percent of a halogenated comonomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene and mixtures thereof and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, a vinyl monomer selected from the group consisting of fluorinated alphamonoolefins, and monomers of the formula R--CF=CF 2 ; ROCF=CF 2 ; CF 3 (CF 2 ) m CH 2 OCF=CF 2 ; CH 3 (CH 2 ) n OCF=CF 2 ; R'CH 2 (X)=CH 2 and R 2 OCH 2 C(X)=CH 2 , wherein R is an organic group containing 2 to 8 carbon atoms, R' is a perfluorinated or chlorofluoroalkyl group of 1 to 7 carbon atoms or a secondary or tertiary halo-alcohol group, R 2 is a perfluorinated or chlorofluoroalkyl of 1 to 7 carbon atoms, X is H or CH 3 , m is an integer of 0 to 6 and n is an integer of 1 to 7, and mixtures thereof, and containing from about 0.5 to about 60 weight percent of a high molecular weight fraction which has a melt index of from about 0.0001 to 1.0 and from about 40 to about 99.5 weight percent of a low molecular weight fraction having a melt index of from about 3 to 3000.

Claim 12

Terpolymers of from about 40 to 60 mol percent ethylene and from about 60 to 40 mol percent of a halogenated comonomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene and mixtures thereof and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, a vinyl monomer selected from the group consisting of fluorinated alphamonoolefins, and monomers of the formula R--CF=CF 2 ; ROCF=CF 2 ; CF 3 (CF 2 ) m CH 2 OCF=CF 2 ; CH 3 (CH 2 ) n OCF=CF 2 ; R'CH 2 (X)=CH 2 and R 2 OCH 2 C(X)=CH 2 , wherein R is an organic group containing 2 to 8 carbon atoms, R' is a perfluorinated or chlorofluoroalkyl group of 1 to 7 carbon atoms or a secondary or tertiary halo-alcohol group, R 2 is a perfluorinated or chlorofluoroalkyl of 1 to 7 carbon atoms, X is H or CH 3 , m is an integer of 0 to 6 and n is an integer of 1 to 7, and mixtures thereof, and containing from about 0.5 to about 60 weight percent of a high molecular weight fraction which has a melt index of from about 0.0001 to 1.0 and from about 40 to about 99.5 weight percent of a low molecular weight fraction having a melt index of from about 3 to 3000.

Claim 13

Terpolymers in accordance with claim 8 wherein said halogenated comonomer is chlorotrifluoroethylene.

Claim 14

Terpolymers in accordance with claim 9 containing from about 5 to about 50 weight percent of a high molecular weight fraction which has a melt index of from about 0.005 to about 0.5.

Claim 15

Terpolymers in accordance with claim 10 in which said high molecular weight fraction has a melt index in the range of about 0.005 to about 0.2 and said low molecular weight fraction has a melt index of about 5 to 100.

Claim 16

Terpolymers in accordance with claim 11 containing from about 45 to about 55 mol percent of ethylene and correspondingly from about 55 to about 45 mol percent of chlorotrifluoroethylene.

Claim 17

Terpolymers in accordance with claim 12 containing from about 0.5 to 5 mol percent of 3,3,3-trifluoro-2-trifluoromethyl propene.

Claim 18

Terpolymers in accordance with claim 8 wherein said halogenated comonomer is chlorotrifluoroethylene.

Claim 19

Terpolymers in accordance with claim 14 containing from about 5 to about 50 weight percent of a high molecular weight fraction having a melt index in the range of about 0.005 to about 0.5.

Claim 20

Terpolymers in accordance with claim 8 wherein said halogenated comonomer is tetrafluoroethylene.

Claim 21

A process of preparing stress-crack resistant terpolymers of from about 40 to about 60 mol percent ethylene, from about 60 to about 40 mol percent of a halogenated comonomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene and mixtures thereof, and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, a vinyl monomer selected from the group consisting of fluorinated alpha-monoolefins, and monomers of the formula R--CF=CF 2 ; ROCF=CF 2 ; CF 3 (CF 2 ) m CH 2 OCF=CF 2 ; CH 3 (CH 2 ) n OCF=CF 2 ; R'CH 2 (X)=CH 2 and R 2 OCH 2 C(X)=CH 2 , wherein R is an organic group containing 2 to 8 carbon atoms, R' is a perfluorinated or chlorofluoroalkyl group of 1 to 7 carbon atoms or a secondary or tertiary halo-alcohol group, R 2 is a perfluorinated or chlorofluoroalkyl of 1 to 7 carbon atoms, X is H or CH 3 , m is an integer of 0 to 6 and n is an integer of 1 to 7, and mixtures thereof, said process comprising forming a terpolymer containing a high molecular weight component present in a desired weight fraction and having a melt index in the range of about 0.0001 to 1.0 and a low molecular weight component having a melt index of from about 3 to 3000, by initially contacting under polymerization conditions ethylene, in an amount sufficient to provide the desired weight fraction of said high molecular weight component, with a weight excess of a halogenated monomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, and mixtures thereof, and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, said vinyl monomers and mixtures thereof, conducting said polymerization to provide said high molecular weight component of said terpolymer in a reaction mixture, adding a chain transfer agent to said mixture after formation of said high molecular weight component and contacting said mixture, under polymerization conditions, with an additional amount of ethylene to provide said low molecular weight component, said high and low molecular weight components being chosen such that the following equations are satisfied: ##EQU14## wherein X i represents the weight fraction of each high molecular weight component i; Mw represents the weight-average molecular weight of the terpolymer, Mw i represents the weight-average molecular weight of each component i, ##EQU15## wherein X j represents the weight fraction of each low molecular weight component j; Mw j represents the weight-average molecular weight of each component j; and

Claim 22

A process of preparing stress-crack resistant terpolymers of from about 40 to about 60 mol percent ethylene, from about 60 to about 40 mol percent of a halogenated comonomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene and mixtures thereof, and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, a vinyl monomer selected from the group consisting of fluorinated alpha-monoolefins, and monomers of the formula R--CF=CF 2 ; ROCF=CF 2 ; CF 3 (CF 2 ) m CH 2 OCF=CF 2 ; CH 3 (CH 2 ) n OCF=CF 2 ; R'CH 2 (X)=CH 2 and R 2 OCH 2 C(X)=CH 2 , wherein R is an organic group containing 2 to 8 carbon atoms, R' is a perfluorinated or chlorofluoroalkyl group of 1 to 7 carbon atoms or a secondary or tertiary halo-alcohol group, R 2 is a perfluorinated or chlorofluoroalkyl of 1 to 7 carbon atoms, X is H or CH 3 , m is an integer of 0 to 6 and n is an integer of 1 to 7, and mixtures thereof, said process comprising forming a terpolymer containing a high molecular weight component present in a desired weight fraction and having a melt index in the range of about 0.0001 to 1.0 and a low molecular weight component having a melt index of from about 3 to 3000, by initially contacting under polymerization conditions ethylene, in an amount sufficient to provide the desired weight fraction of said high molecular weight component, with a weight excess of a halogenated monomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, and mixtures thereof, and about 0.1 to 10 mol percent of a termonomer selected from the group consisting of 3,3,3-trifluoro-2-trifluoromethyl propene, said vinyl monomers and mixtures thereof, conducting said polymerization to provide said high molecular weight component of said terpolymer in a reaction mixture, adding a chain transfer agent to said mixture after formation of said high molecular weight component and contacting said mixture, under polymerization conditions, with an additional amount of ethylene to provide said low molecular weight component, said high and low molecular weight components being chosen such that the following equations are satisfied: ##EQU14## wherein X i represents the weight fraction of each high molecular weight component i; Mw represents the weight-average molecular weight of the terpolymer, Mw i represents the weight-average molecular weight of each component i, ##EQU15## wherein X j represents the weight fraction of each low molecular weight component j; Mw j represents the weight-average molecular weight of each component j; and

Claim 23

1≦ f≦ 0.95 and therefore wherein said terpolymers contain from 0.2 to 57 weight percent of said high molecular weight component and from 99.8 to 43 weight percent of said low molecular weight component.

Claim 24

1≦ f≦ 0.95 and therefore wherein said terpolymers contain from 0.2 to 57 weight percent of said high molecular weight component and from 99.8 to 43 weight percent of said low molecular weight component.

Claim 25

The process of claim 17 wherein ethylene in the form of a gas is introduced into a pressure vessel containing said halogenated monomer in liquid form.

Claim 26

The process of claim 18 wherein said monomer is chlorotrifluoroethylene.

Claim 27

The process of claim 19 wherein said chain transfer agent is chloroform.

Claim 28

The process of claim 17 wherein a chain transfer agent is present during said initial contact and additional amounts of chain transfer agent are added during said contact between said mixture and said additional ethylene.

Claim 29

The process of claim 17 wherein said monomer is tetrafluoroethylene.

Claim 30

The process of claim 17 wherein said monomer is chlorotrifluoroethylene.