Methyl formate as an adjuvant in phenolic foam formation
Assignee: Union Carbide Corp
•
Filing: 1975-09-26
•
Granted: 1977-07-05
•
Expires: 1995-09-26
Abstract
Abstract This invention relates to the use of methyl formate as an adjuvant in the formation of phenolic foam. The addition of methyl formate to phenol-aldehyde resoles causes a substantial reduction in resole viscosity and thus allows for the processing of resoles which are otherwise too viscous to be foamed. A further advantage of methyl formate as an adjuvant in the formation of phenolic foam is that it also functions as a blowing agent. In its use as a blowing agent, methyl formate is employed in combination with 1,1,2-trichloro-1,2,2-trifluoroethane. Depending upon the nature of the phenolic foaming resin, the use of methyl formate in combination with 1,1,2-trichloro-1,2,2-trifluoroethane as the source of blowing action further provides the advantageous result of allowing for the formation of phenolic foam of reduced friability.
Inventors
- 👤 Anthony Joseph Papa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:17
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08J9/149; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/101; C08J2361/00; C08J2361/04; C08J2361/06
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
91 words
A blend containing: (A) a phenolic resole, (B) methyl formate and (C) 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the total combined weight of (B) and (C) is from about 2 to about 40 parts by weight per 100 parts by weight of (A) and, of the total combined weight of (B) and (C) contained in the blend, from about 5 to about 80 weight percent is methyl formate, provided the blend contains at least 0.4 and no more than about 20 parts by weight of methyl formate per 100 parts by weight of component (A).
Claim 2
Dependent Claim
91 words
A blend containing: (A) a phenolic resole, (B) methyl formate and (C) 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the total combined weight of (B) and (C) is from about 2 to about 40 parts by weight per 100 parts by weight of (A) and, of the total combined weight of (B) and (C) contained in the blend, from about 5 to about 80 weight percent is methyl formate, provided the blend contains at least 0.4 and no more than about 20 parts by weight of methyl formate per 100 parts by weight of component (A).
Claim 3
Dependent Claim
15 words
A blend as defined in claim 1 in which the resole is a phenol-formaldehyde resole.
Claim 4
Dependent Claim
40 words
A blend as defined in claim 1 in which the resole is free of ionic species that respond to removal by the free acid form of a cation exchange resin and the free base form of an anion exchange resin.
Claim 5
Dependent Claim
34 words
A blend as defined in claim 1 in which the total combined weight of (B) and (C) is no more than about 20 parts by weight per 100 parts by weight of component (A).
Claim 6
Dependent Claim
28 words
A blend as defined in claim 4 which contains no more than about 10 parts by weight of methyl formate per 100 parts by weight of component (A).
Claim 7
Independent Claim
102 words
A method for producing phenolic foam which comprises polymerizing a phenolic resole in the presence of an acidic polymerization catalyst and, as a source of blowing action, methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane is from about 2 to about 40 parts by weight per 100 parts by weight of resole and, of this combined weight, from about 5 to about 80 weight percent is methyl formate, provided methyl formate is present in an amount of at least 0.4 and no more than about 20 parts by weight per 100 parts by weight of the resole.
Claim 8
Independent Claim
102 words
A method for producing phenolic foam which comprises polymerizing a phenolic resole in the presence of an acidic polymerization catalyst and, as a source of blowing action, methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane is from about 2 to about 40 parts by weight per 100 parts by weight of resole and, of this combined weight, from about 5 to about 80 weight percent is methyl formate, provided methyl formate is present in an amount of at least 0.4 and no more than about 20 parts by weight per 100 parts by weight of the resole.
Claim 9
Independent Claim
132 words
A method for producing phenolic foam which comprises polymerizing and foaming a reaction mixture containing a phenol-formaldehyde resole, an acidic polymerization catalyst and, as a source of blowing action, methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the resole has a water content of no more than about 10 parts by weight per 100 parts of resole, and the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane contained in the reaction mixture is from about 2 to about 40 parts by weight per 100 parts by weight of resole and, of this combined weight, from about 5 to about 80 weight percent is methyl formate, provided the reaction mixture contains methyl formate in an amount of at least about 0.5 and no more than about 20 parts by weight per 100 parts by weight of resole.
Claim 10
Independent Claim
132 words
A method for producing phenolic foam which comprises polymerizing and foaming a reaction mixture containing a phenol-formaldehyde resole, an acidic polymerization catalyst and, as a source of blowing action, methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the resole has a water content of no more than about 10 parts by weight per 100 parts of resole, and the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane contained in the reaction mixture is from about 2 to about 40 parts by weight per 100 parts by weight of resole and, of this combined weight, from about 5 to about 80 weight percent is methyl formate, provided the reaction mixture contains methyl formate in an amount of at least about 0.5 and no more than about 20 parts by weight per 100 parts by weight of resole.
Claim 11
Dependent Claim
62 words
A method as defined in claim 7 in which the reaction mixture contains, as an additional source of blowing action, trichloromonofluoromethane in an amount no more than about 5 parts by weight per 100 parts by weight of resole, provided no more than 30 weight percent of the combined weight of methyl formate, 1,2,2-trichloro-1,2,2-trifluoroethane and trichloromonofluoromethane is constituted of said latter component.
Claim 12
Dependent Claim
41 words
A method as defined in claim 7 in which the phenol-formaldehyde resole is free of ionic species that respond to removal by the free acid form of a cation exchange resin and the free base form of an anion exchange resin.
Claim 13
Dependent Claim
78 words
A method as defined in claim 7 in which the phenol-formaldehyde resole is the product of the method which comprises condensing phenol and formaldehyde in the presence of an alkaline metal catalyst, treating the alkaline condensate with the free acid form of a cationic exchange resin to a pH from 1.5 to about 4, and adding an alkaline compound to the cation exchanged liquid to raise the pH thereof to a value between about 5 and about 6.7.
Claim 14
Dependent Claim
68 words
A method as defined in claim 7 in which no more than about 50 weight percent of the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane is constituted of methyl formate and in which the resole is the product of the method which comprises condensing phenol and formaldehyde in the presence of an alkaline metal catalyst and neutralizing the alkaline condensate by the addition thereto of an acidic compound.
Claim 15
Independent Claim
165 words
A method for producing phenolic foam which comprises polymerizing and foaming a reaction mixture containing a phenol-formaldehyde resole, an acidic polymerization catalyst, and, as a source of blowing action, methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the resole has a water content of no more than about 10 parts by weight per 100 parts by weight of resole and is free of ionic species that respond to removal by the free acid form of a cation exchange resin and the free base form of an anion exchange resin, and wherein the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane contained in the reaction mixture is between about 2 and about 40 parts by weight per 100 parts by weight of resole and, of this combined weight, from about 5 to about 70 weight percent is methyl formate, provided the reaction mixture contains methyl formate in an amount of at least about 0.4 and no more than about 20 parts by weight per 100 parts by weight of resole.
Claim 16
Independent Claim
165 words
A method for producing phenolic foam which comprises polymerizing and foaming a reaction mixture containing a phenol-formaldehyde resole, an acidic polymerization catalyst, and, as a source of blowing action, methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane, wherein the resole has a water content of no more than about 10 parts by weight per 100 parts by weight of resole and is free of ionic species that respond to removal by the free acid form of a cation exchange resin and the free base form of an anion exchange resin, and wherein the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane contained in the reaction mixture is between about 2 and about 40 parts by weight per 100 parts by weight of resole and, of this combined weight, from about 5 to about 70 weight percent is methyl formate, provided the reaction mixture contains methyl formate in an amount of at least about 0.4 and no more than about 20 parts by weight per 100 parts by weight of resole.
Claim 17
Dependent Claim
38 words
A method as defined in claim 12 in which the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane contained in the reaction mixture is no more than about 20 parts by weight per 100 parts by weight of resole.
Claim 18
Dependent Claim
27 words
A method as defined in claim 12 in which at least about 20 weight percent of the combined weight of methyl formate and 1,1,2-trichloro-1,2,2-trifluoroethane is methyl formate.
References Cited (Backward Citations)
US2493075A
Cited
US2910446A
Cited
US2911381A
Cited
US2911382A
Cited
US3389094A
Cited
US3879315A
Cited
US3914191A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-04 | 1981-01-03 | 1981-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-04 | 1985-01-03 | 1985-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-04 | 1989-01-03 | 1989-07-05 | $7700.00 | Window Closed / Lapsed |