Method of preparing vinyl chloride resins
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1972-12-05
•
Granted: 1977-06-14
•
Expires: 1992-12-05
Abstract
Abstract Vinyl chloride monomer is polymerized in aqueous medium under the influence of oil soluble polymerization initiators in the presence of alkali metal salts of higher fatty acid, higher alcohols and/or higher fatty acids, and hydroxides of alkali metals in certain amounts respectively, to produce vinyl chloride resin, stable for making resin/plasticizer pastes, mostly composed of particles having diameters lying between 0.1 and 2 microns. The resins are suitable for making resin/plasticizer pastes that have a low initial viscosity, little change in viscosities during storage, good thermal stability and excellent degassing property. Reduced deposition of polymer scales on the walls of the polymerization vessels was successful.
Inventors
- 👤 Shigenobu Tajima
- 👤 Kazuhiko Kurimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:14
CPC Classifications
C; C08; C08F; C08F14/00; C08F14/02; C08F14/04; C08F14/06; Y; Y10; Y10S; Y10S526/00; Y10S526/911
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
153 words
A method comprising polymerizing in aqueous medium, under the influence of at least one oil soluble polymerization initiator, vinyl chloride or a mixture thereof with at least one copolymerizable monomer, containing at least 50% by weight of the vinyl chloride in the presence of (a) from 0.5 to 4% by weight, based on the weight of the monomer mixture, of at least one alkali metal salt of higher fatty acid, having from 8 to 18 carbon atoms in the molecule, (b) from 0.05 to 3% by weight, based on the weight of the monomer mixture and equivalent to from 4 to 75% by weight of said alkali metal salt, of at least one higher alcohol or higher fatty acid, having 8 to 18 carbon atoms, alone or in combination, and (c) from 0.001 to 0.1% by weight, based on the weight of the monomer mixture, of at least one hydroxide of alkali metal.
Claim 2
Independent Claim
153 words
A method comprising polymerizing in aqueous medium, under the influence of at least one oil soluble polymerization initiator, vinyl chloride or a mixture thereof with at least one copolymerizable monomer, containing at least 50% by weight of the vinyl chloride in the presence of (a) from 0.5 to 4% by weight, based on the weight of the monomer mixture, of at least one alkali metal salt of higher fatty acid, having from 8 to 18 carbon atoms in the molecule, (b) from 0.05 to 3% by weight, based on the weight of the monomer mixture and equivalent to from 4 to 75% by weight of said alkali metal salt, of at least one higher alcohol or higher fatty acid, having 8 to 18 carbon atoms, alone or in combination, and (c) from 0.001 to 0.1% by weight, based on the weight of the monomer mixture, of at least one hydroxide of alkali metal.
Claim 3
Dependent Claim
40 words
The method as claimed in claim 1 wherein said alkali metal salt of higher fatty acid is selected from the gourp consisting of sodium laurate, potassium laurate, sodium myristate, potassium myristate, sodium palmitate, potassium palmitate, sodium stearate and potassium stearate.
Claim 4
Independent Claim
46 words
The method as claimed in calim 1 wherein said higher alcohol is selected from the group consisting of lauryl alcohols, cetyl alcohols and stearyl alcohols, and said higher fatty acid is selected from the group consisting of lauric acids, myristic acids, palmitic acids and stearic acids.
Claim 5
Dependent Claim
29 words
The method as claimed in claim 1 wherein said hydroxide of alkali metal is selected from the group consisting of sodium hydroxides, potassium hydroxides, lithium hydroxides and sodium oxides.
Claim 6
Dependent Claim
32 words
The method as claimed in claim 1 wherein said copolymerizable monomer is selected from the group consisting of vinyl acetate, vinylidene chloride, acrylonitrile, acrylic acid esters, methacrylic acid esters and maleic acids.
Claim 7
Dependent Claim
35 words
The method as claimed in claim 1 wherein said oil soluble polymerization initiator is selected from the group consisting of azobisisobutylonitrile, azobisdimethylvaleronitrile, lauroyl peroxides, benzoyl peroxides, isopropyl peroxydicarbonate, acetyl cyclohexyl sulfonyl peroxides and tertiarybutyl peroxypivalate.
Claim 8
Independent Claim
138 words
A method comprising polymerizing vinyl chloride under the influence of at least one oil soluble polymerization initiator in aqueous medium in the presence of (a) from 0.5 to 4% by weight, based on the weight of the monomer, of at least one alkali metal salt of saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule. (b) from 0.05 to 3% by weight, based on the weight of the monomer and equivalent to from 4 to 75% by weight of said alkali metal salt, of at least one saturated higher fatty alcohol or saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule, alone or in combination, and (c) from 0.001 to 0.1% by weight, based on the weight of the monomer, of at least one hydroxide of alkali metal.
Claim 9
Independent Claim
138 words
A method comprising polymerizing vinyl chloride under the influence of at least one oil soluble polymerization initiator in aqueous medium in the presence of (a) from 0.5 to 4% by weight, based on the weight of the monomer, of at least one alkali metal salt of saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule. (b) from 0.05 to 3% by weight, based on the weight of the monomer and equivalent to from 4 to 75% by weight of said alkali metal salt, of at least one saturated higher fatty alcohol or saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule, alone or in combination, and (c) from 0.001 to 0.1% by weight, based on the weight of the monomer, of at least one hydroxide of alkali metal.
Claim 10
Dependent Claim
25 words
The method as claimed in claim 7 wherein said oil soluble polymerization initiator is an azo compound or an organic peroxide, alone or in combination.
Claim 11
Dependent Claim
35 words
The method as claimed in claim 7 wherein said oil soluble polymerization initiator is selected from the group consisting of azobisisobutylonitrile, azobisdimethylvaleronitrile, lauroyl peroxides benzoyl peroxides, isopropyl peroxydicarbonate, acetyl cyclohexyl sulfonyl peroxides and tertiarybutyl peroxypivalate.
Claim 12
Independent Claim
159 words
A method comprising polymerizing in aqueous medium under the influence of at least one oil soluble polymerization initiator a mixture containing at least 80% by weight of vinyl chloride and at most 20% by weight of vinyl acetate in the presence of (a) from 0.5 to 4% by weight, based on the weight of the monomer mixture, of at least one alkali metal salt of saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule, (b) from 0.05 to 3% by weight, based on the weight of the monomer mixture and equivalent to from 4 to 75% by weight of said alkali metal salt, of at least one saturated higher fatty alcohol or saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule, alone or in combination, and (c) from 0.001 to 0.1% by weight, based on the weight of the monomer mixture, of at least one hydroxide of alkali metal.
Claim 13
Independent Claim
159 words
A method comprising polymerizing in aqueous medium under the influence of at least one oil soluble polymerization initiator a mixture containing at least 80% by weight of vinyl chloride and at most 20% by weight of vinyl acetate in the presence of (a) from 0.5 to 4% by weight, based on the weight of the monomer mixture, of at least one alkali metal salt of saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule, (b) from 0.05 to 3% by weight, based on the weight of the monomer mixture and equivalent to from 4 to 75% by weight of said alkali metal salt, of at least one saturated higher fatty alcohol or saturated higher fatty acid, having from 12 to 18 carbon atoms in the molecule, alone or in combination, and (c) from 0.001 to 0.1% by weight, based on the weight of the monomer mixture, of at least one hydroxide of alkali metal.
Claim 14
Dependent Claim
25 words
The method as claimed in claim 10 wherein said oil soluble polymerization initiator is an azo compound or an organic peroxide, alone or in combination.
Claim 15
Dependent Claim
35 words
The method as claimed in claim 10 wherein said oil soluble polymerization initiator is selected from the group consisting of azobisisobutylonitrile, azobisdimethylvaleronitrile, lauroyl peroxides, benzoyl peroxides, isopropyl peroxydicarbonate, acetyl cyclohexyl sulfonyl peroxides and tertiarybutyl peroxypivalate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-13 | 1980-12-13 | 1981-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-13 | 1984-12-13 | 1985-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-13 | 1988-12-13 | 1989-06-14 | $7700.00 | Window Closed / Lapsed |