Method of forming grooves in the [011] crystalline direction
Assignee: RCA Corp
•
Filing: 1976-03-29
•
Granted: 1977-06-14
•
Expires: 1996-03-29
Abstract
Abstract An A-B etchant is applied to a (100) surface of a body of semiconductor material, a portion of which along the (100) surface of the body is either gallium arsenide or gallium aluminum arsenide. The etchant is applied for at least 15 seconds at a temperature of approximately 80° C. The A-B etchant is a solution by weight percent of 47.5%, water, 0.2% silver nitrate, 23.8% chromium trioxide and 28.5% of a 48% aqueous solution of hydrofluoric acid. As a result of the application of the A-B etchant a pattern of elongated etch pits form having their longitudinal axes along the [011] crystalline direction. Grooves are formed in the body at a surface opposite the (100) surface on which was applied the etchant. The grooves are formed along the [011] crystalline direction by aligning the longitudinal axes of the grooves with the longitudinal axes of the etch pits.
Inventors
- 👤 Donald Paul Marinelli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:31
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/646; H10P50/648; Y; Y10; Y10S; Y10S438/00; Y10S438/928
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
38 words
A method of forming groove along the [011] crystalline direction of a body of semiconductor material a portion of which is gallium arsenide or gallium aluminum arsenide along a (100) surface of said body, comprising the steps of:
Claim 2
Independent Claim
38 words
A method of forming groove along the [011] crystalline direction of a body of semiconductor material a portion of which is gallium arsenide or gallium aluminum arsenide along a (100) surface of said body, comprising the steps of:
Claim 3
Dependent Claim
118 words
applying to the (100) surface an etchant for at least 15 seconds at a temperature on the order of 80° C., said etchant being a solution by weight percent of 47.5% water, H 2 O, 0.2% silver nitrate, AgNO 3 , 23.8% of chromium trioxide, CrO 3 , 28.5% of a 48% aqueous solution of hydrofluoric acid, HF, said etchant forming a pattern of elongated etch pits whose longitudinal axes are in the [011] crystalline direction; and forming grooves in said body at a surface opposite said surface on which said etchant is applied with said grooves being aligned with the longitudinal axes of said etch pits so that said grooves are formed along the [011] crystalline direction.
Claim 4
Dependent Claim
118 words
applying to the (100) surface an etchant for at least 15 seconds at a temperature on the order of 80° C., said etchant being a solution by weight percent of 47.5% water, H 2 O, 0.2% silver nitrate, AgNO 3 , 23.8% of chromium trioxide, CrO 3 , 28.5% of a 48% aqueous solution of hydrofluoric acid, HF, said etchant forming a pattern of elongated etch pits whose longitudinal axes are in the [011] crystalline direction; and forming grooves in said body at a surface opposite said surface on which said etchant is applied with said grooves being aligned with the longitudinal axes of said etch pits so that said grooves are formed along the [011] crystalline direction.
Claim 5
Dependent Claim
29 words
The method of forming grooves in accordance with claim 1 wherein said surface on which said etchant is applied is in a lapped condition when said etchant is applied.
Claim 6
Dependent Claim
23 words
The method of forming grooves in accordance with claim 2 wherein said etchant is applied to said [011] surface for approximately 30 seconds.
Claim 7
Dependent Claim
43 words
The method of forming grooves in accordance with claim 3 wherein a side surface of said body is cleaved parallel to said longitudinal axes of said etch pits thereby forming a reference surface for determining the [011] crystalline direction on said opposite surface.
Claim 8
Dependent Claim
16 words
The method of forming grooves in accordance with claim 4 wherein said body is gallium arsenide.
Claim 9
Dependent Claim
17 words
The method of forming grooves in accordance with claim 4 wherein said body is gallium aluminum arsenide.
Claim 10
Dependent Claim
40 words
The method of forming grooves in accordance with claim 4 wherein said body has a substrate of gallium arsenide along a (100) surface of said body with one or more layers of III-V semiconductor materials epitaxially and sequentially deposited thereon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-13 | 1980-12-13 | 1981-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-13 | 1984-12-13 | 1985-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-13 | 1988-12-13 | 1989-06-14 | $7700.00 | Window Closed / Lapsed |