Foamed polyester resin
Assignee: Vast Products Inc
•
Filing: 1976-10-05
•
Granted: 1977-06-07
•
Expires: 1996-10-05
Abstract
Abstract A method of preparing lightweight molded objects having high structural strength and uniform closed cell structure comprises forming a uniform mixture of a liquid general purpose polyester resin, an inorganic filler or a mixture thereof, bicarbonate of soda, sodium acetate, aluminum ammonium sulfate, ferrous ammonium sulfate and tannic acid and a catalyst mixture containing a peroxide catalyst for the polyester resin, an acidic substance to release the carbon dioxide gas from the bicarbonate of soda and water. The resin mixture and the catalyst mixture are uniformly blended and applied to the mold or cavity and the foamed polyester allowed to form.
Inventors
- 👤 William F. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:43
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0095; C08J9/0066; C08K; C08K3/00; C08K3/18; C08K3/24; C08K5/00; C08K5/04; C08K5/09; C08K7/00; C08K7/22; C08K7/24; C08J2367/00; C08J2367/06
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
117 words
The method of preparing objects of a foamed-filled polyester resin material which comprises (a) preparing a liquid resin blend comprised of a liquid polyester resin, an inorganic filler, bicarbonate of soda, and an effective amount of a cell stabilizing mixture containing sodium acetate, aluminum ammonium sulfate, ferrous ammonium sulfate and tannic acid; (b) preparing a catalyst blend comprised of an effective amount of an organic peroxide catalyst for the polyester resin, an acidic substance effective to release carbon dioxide from the bicarbonate of soda, and water; (c) combining the resin blend and the catalyst blend to form a uniform liquid mixture; and (d) applying that mixture to a mold or surface and allowing the mixture to foam.
Claim 2
Independent Claim
117 words
The method of preparing objects of a foamed-filled polyester resin material which comprises (a) preparing a liquid resin blend comprised of a liquid polyester resin, an inorganic filler, bicarbonate of soda, and an effective amount of a cell stabilizing mixture containing sodium acetate, aluminum ammonium sulfate, ferrous ammonium sulfate and tannic acid; (b) preparing a catalyst blend comprised of an effective amount of an organic peroxide catalyst for the polyester resin, an acidic substance effective to release carbon dioxide from the bicarbonate of soda, and water; (c) combining the resin blend and the catalyst blend to form a uniform liquid mixture; and (d) applying that mixture to a mold or surface and allowing the mixture to foam.
Claim 3
Dependent Claim
19 words
The method of claim 1 in which the inorganic filler is a mixture of wollastonite nepheline syenite and mica.
Claim 4
Dependent Claim
23 words
The method of claim 1 in which the sodium bicarbonate is present in an amount equal to 1-3% of the peroxide catalyst weight.
Claim 5
Dependent Claim
32 words
The method of claim 3 in which the acidic substance is glacial acetic acid which is present in an amount sufficient to effect the release of carbon dioxide from the sodium bicarbonate.
Claim 6
Dependent Claim
39 words
The method of claim 4 in which the organic peroxide catalyst is a mixture of benzoyl peroxide and methyl ethyl ketone peroxide in which each is present in an amount equivalent to 0.5-3.5% by weight of the polyester resin.
Claim 7
Dependent Claim
26 words
The method of claim 1 in which each of the ingredients is present in an amount equivalent to about 1/2% of the benzoyl peroxide by weight.
Claim 8
Dependent Claim
32 words
The method of claim 6 in which the amount of water present in the catalyst mixture is about 1-4% of the weight of the organic peroxide catalyst and the glacial acetic acid.
Claim 9
Dependent Claim
27 words
The method of claim 7 in which the inorganic filler is present in an amount of up to about 80% by weight of the combined resin-filler mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-06 | 1980-12-06 | 1981-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-06 | 1984-12-06 | 1985-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-06 | 1988-12-06 | 1989-06-07 | $7700.00 | Window Closed / Lapsed |