Process for manufacturing rapid hardening portland cement clinker
Assignee: Taiheiyo Cement Corp
•
Filing: 1974-01-07
•
Granted: 1977-06-07
•
Expires: 1994-01-07
Abstract
Abstract A process for manufacturing a rapid hardening portland cement clinker containing a calcium halo-aluminate having the formula; 11CaO.7Al 2 O 3 .CaX 2 , in which X is a halogen, characterized by adding at least one sulfur compound selected from calcium sulfate, calcium sulfite and calcium sulfide to the mixed raw materials comprising mainly an aluminous material, a calcareous material, a silicious material, an iron source and a halogen source, and burning the obtained mixture in an oxidizing temperature.
Inventors
- 👤 Shigejiro Mori
- 👤 Hiroshi Uchikawa
- 👤 Shunichiro Uchida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:42
CPC Classifications
C; C04; C04B; C04B7/00; C04B7/32; C04B7/326; C04B7/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
164 words
A process for manufacturing rapid hardening portland cement which comprises adding calcium sulfate hemihydrate and anhydrite to a clinker containing 10 - 70% by weight of 11CaO.7Al 2 O 3 .CaX 2 , wherein X is a halogen, 15 - 60% by weight of 3CaO.SiO 2 and less than 1% by weight of free CaO which clinker is prepared by adding 0.5 - 4.5% by weight based on SO 3 of at least one sulfur compound selected from the group consisting of calcium sulfate, calcium sulfite and calcium sulfide to mixed raw materials which comprise an aluminous material, a calcareous material, a siliceous material, an iron source and a halogen source; and burning the obtained mixture at the temperature of 1265° - 1400° C in an oxidizing atmosphere, wherein said calcium sulfate hemihydrate and anhydrite are added in an amount such that the weight ratio of Al 2 O 3 /SO 3 in the cement is present in a range of 0.7 - 1.8.
Claim 2
Dependent Claim
164 words
A process for manufacturing rapid hardening portland cement which comprises adding calcium sulfate hemihydrate and anhydrite to a clinker containing 10 - 70% by weight of 11CaO.7Al 2 O 3 .CaX 2 , wherein X is a halogen, 15 - 60% by weight of 3CaO.SiO 2 and less than 1% by weight of free CaO which clinker is prepared by adding 0.5 - 4.5% by weight based on SO 3 of at least one sulfur compound selected from the group consisting of calcium sulfate, calcium sulfite and calcium sulfide to mixed raw materials which comprise an aluminous material, a calcareous material, a siliceous material, an iron source and a halogen source; and burning the obtained mixture at the temperature of 1265° - 1400° C in an oxidizing atmosphere, wherein said calcium sulfate hemihydrate and anhydrite are added in an amount such that the weight ratio of Al 2 O 3 /SO 3 in the cement is present in a range of 0.7 - 1.8.
Claim 3
Dependent Claim
15 words
A process claimed in claim 1, in which said halogen source is a fluorine source.
Claim 4
Dependent Claim
12 words
A process of claim 2, wherein the fluorine source is calcium fluoride.
Claim 5
Dependent Claim
15 words
A process claimed in claim 1, in which said halogen source is a chlorine source.
Claim 6
Dependent Claim
27 words
A process claimed in claim 1, in which the calcareous material is at least one member selected from the group consisting of quick lime and slaked lime.
Claim 7
Dependent Claim
31 words
A process claimed in claim 1, in which the calcareous mixture is a mixture of more than 60% by weight of quick lime and less than 40% by weight of limestone.
Claim 8
Dependent Claim
14 words
A process claimed in claim 1, in which the aluminous material burned is bauxite.
Claim 9
Dependent Claim
47 words
A process claimed in claim 1, in which the calcareous material is at least one member selected from the group consisting of quick lime and slaked lime and the aluminous material is at least one member selected from the group consisting of crude bauxite and burned bauxite.
Claim 10
Dependent Claim
22 words
A process of claim 1, in which the mixed raw materials are shaped under a pressure greater than 50 Kg/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-06-06 | 1980-12-06 | 1981-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-06-06 | 1984-12-06 | 1985-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-06-06 | 1988-12-06 | 1989-06-07 | $7700.00 | Window Closed / Lapsed |