Steel plate for preparing cans by ironing
Assignee: Nippon Steel Corp
•
Filing: 1975-03-05
•
Granted: 1977-05-31
•
Expires: 1995-03-05
Abstract
Abstract A steel plate for preparing cans by ironing having on its surface a composite oil coating which comprises a base oil and one or more, each amounting to 3 to 50 parts, selective from the group comprising of polybutene, polypropylene, polyethylene and ethyl or methyl polymethacrylate, the average molecular weight for each being in the range 500 to 30,000.
Inventors
- 👤 Hidejiro Asano
- 👤 Shigeyoshi Maeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:18
CPC Classifications
C; C10; C10M; C10M111/00; C10M111/04; B; B21; B21D; B21D22/00; B21D22/20; B21D22/201; C10M2205/00; C10M2205/02; C10M2205/024; C10M2205/026; C10M2207/00; C10M2207/10; C10M2207/12; C10M2207/125; C10M2207/129; C10M2207/18; C10M2207/28; C10M2207/287; C10M2207/40; C10M2207/404; C10M2209/00; C10M2209/02; C10M2209/08; C10M2209/084; C10M2209/10; C10M2209/103; C10M2209/104; C10N; C10N2040/00; C10N2040/20; C10N2040/24; C10N2040/241; C10N2040/242; C10N2040/243; C10N2040/244; C10N2040/245; C10N2040/246; C10N2040/247; Y; Y10; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31699; Y10T428/31714; Y10T428/31844
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
90 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of polyethylene having an average molecular weight from 500 to 30,000 and wherein the steel plate has on its surface under said composite oil layer, a layer of 0.2 to 10 mg/dm .spsb.2 thickness of a substance selected from a group consisting of zinc phosphate, manganese phosphate, and iron phosphate.
Claim 2
Dependent Claim
90 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of polyethylene having an average molecular weight from 500 to 30,000 and wherein the steel plate has on its surface under said composite oil layer, a layer of 0.2 to 10 mg/dm .spsb.2 thickness of a substance selected from a group consisting of zinc phosphate, manganese phosphate, and iron phosphate.
Claim 3
Dependent Claim
54 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of ethyl or methyl polymethacrylate having an average molecular weight from 500 to 30,000.
Claim 4
Dependent Claim
54 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of ethyl or methyl polymethacrylate having an average molecular weight from 500 to 30,000.
Claim 5
Dependent Claim
93 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of ethyl or methyl polymethacrylate having an average molecular weight from 500 to 30,000, and wherein the steel plate has on its surface under said composite oil layer, a layer of 0.2 to 10 mg/dm .spsb.2 thickness of a substance selected from a group consisting of zinc phosphate, manganese phosphate, and iron phosphate.
Claim 6
Dependent Claim
93 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of ethyl or methyl polymethacrylate having an average molecular weight from 500 to 30,000, and wherein the steel plate has on its surface under said composite oil layer, a layer of 0.2 to 10 mg/dm .spsb.2 thickness of a substance selected from a group consisting of zinc phosphate, manganese phosphate, and iron phosphate.
Claim 7
Dependent Claim
79 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of ethyl or methyl polymethacrylate having an average molecular weight from 500 to 30,000, and wherein the composite oil coating further comprises 2 to 20% of a branched chain monocarboxylic acid having 10 to 18 carbon atoms per molecule.
Claim 8
Dependent Claim
79 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of ethyl or methyl polymethacrylate having an average molecular weight from 500 to 30,000, and wherein the composite oil coating further comprises 2 to 20% of a branched chain monocarboxylic acid having 10 to 18 carbon atoms per molecule.
Claim 9
Dependent Claim
76 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of polyethylene having an average molecular weight from 500 to 30,000, and wherein the composite oil coating further comprises 2 to 20% of a branched chain monocarboxylic acid having 10 to 18 carbon atoms per molecule.
Claim 10
Dependent Claim
76 words
A steel plate for preparing cans by ironing having on its surface a composite oil coating in an amount effective to avoid scratching or gashing of said steel plate surface consisting essentially of mineral oil and 3 to 50 parts of polyethylene having an average molecular weight from 500 to 30,000, and wherein the composite oil coating further comprises 2 to 20% of a branched chain monocarboxylic acid having 10 to 18 carbon atoms per molecule.
References Cited (Backward Citations)
US1273358A
Cited
US2281676A
Cited
US2274673A
Cited
US2389227A
Cited
US2486493A
Cited
US2516914A
Cited
GB710109A
Cited
GB767002A
Cited
US2767111A
Cited
US2880188A
Cited
US3340194A
Cited
US3298954A
Cited
US3454495A
Cited
US3838049A
Cited
US3480485A
Cited
US3941910A
Cited
US3884820A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |