Glass cord adhesives comprising vinyl pyridine terpolymer/lignin sulfonate-resorcinol-formaldehyde reaction product; method of use and composite article
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1976-10-18
•
Granted: 1977-05-31
•
Expires: 1996-10-18
Abstract
Abstract Rubber compounds are readily bonded to reinforcing elements, particularly tire cords of glass fibers, using a one-step dip process in which the dip contains an alkaline aqueous dispersion of a mixture of a major amount by weight of a rubbery vinyl pyridine/styrene/butadiene terpolymer and a lignin sulfonate-resorcinol-formaldehyde reaction product. Good adhesion of the cords to a rubber compound are obtained with this process.
Inventors
- 👤 Otto C. Elmer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 00:16
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; C08J2321/00; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/249933; Y10T428/249937; Y10T428/249939; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
175 words
A method for adhering a reinforcing element to a vulcanized conjugated diene rubber compound which comprises treating said element with a composition comprising an aqueous alkaline dispersion of from about 10 to 30% by weight (as dry solids) of a mixture of 100 parts of a rubbery vinyl pyridine terpolymer containing about 50 to 95% of a conjugated diolefin, about 5 to 40% of vinyl pyridine and about 0 to 40% of a styrene; about 1.0 to 30 parts of a lignin sulfonate, resorcinol and formaldehyde reaction product; and heat treating said element to remove the water and to heat set the solids from said composition and to deposit on said element from said composition a total of from about 2 to 30% by weight (solids), said heat treatment being conducted at temperatures of from about 300° to 500° F. for from about 30 to 150 seconds, cooling said treated element, combining said cooled treated element with an unvulcanized vulcanizable rubber consisting essentially of conjugated diene as the major elastomer component, and vulcanizing the same.
Claim 2
Independent Claim
175 words
A method for adhering a reinforcing element to a vulcanized conjugated diene rubber compound which comprises treating said element with a composition comprising an aqueous alkaline dispersion of from about 10 to 30% by weight (as dry solids) of a mixture of 100 parts of a rubbery vinyl pyridine terpolymer containing about 50 to 95% of a conjugated diolefin, about 5 to 40% of vinyl pyridine and about 0 to 40% of a styrene; about 1.0 to 30 parts of a lignin sulfonate, resorcinol and formaldehyde reaction product; and heat treating said element to remove the water and to heat set the solids from said composition and to deposit on said element from said composition a total of from about 2 to 30% by weight (solids), said heat treatment being conducted at temperatures of from about 300° to 500° F. for from about 30 to 150 seconds, cooling said treated element, combining said cooled treated element with an unvulcanized vulcanizable rubber consisting essentially of conjugated diene as the major elastomer component, and vulcanizing the same.
Claim 3
Dependent Claim
21 words
A method according to claim 1 where said lignin sulfonate is present at a level of from 2 to 10 parts.
Claim 4
Dependent Claim
15 words
A method according to claim 1 where said reinforcing element is a cord of glass.
Claim 5
Dependent Claim
83 words
A bonded composite material comprising a reinforcing element embedded in a vulcanized rubber, said element containing a total of from about 2 to 30% by weight (dry) based on the weight of said uncoated element of an adhesive composition comprised of a deposit of a heat set mixture containing 100 parts of a rubbery vinyl pyridine terpolymer, 1 to 30 parts of a lignin sulfonate, and resorcinol and formaldehyde reaction product, said adhesive composition forming a bond between said element and said rubber.
Claim 6
Dependent Claim
83 words
A bonded composite material comprising a reinforcing element embedded in a vulcanized rubber, said element containing a total of from about 2 to 30% by weight (dry) based on the weight of said uncoated element of an adhesive composition comprised of a deposit of a heat set mixture containing 100 parts of a rubbery vinyl pyridine terpolymer, 1 to 30 parts of a lignin sulfonate, and resorcinol and formaldehyde reaction product, said adhesive composition forming a bond between said element and said rubber.
Claim 7
Dependent Claim
42 words
A bonded composite material according to claim 4 where said lignin sulfonate reaction product contains about 2 to 10 parts by weight of lignin sulfonate, 2 to 10 parts by weight of resorcinol and 2 to 10 parts by weight of formaldehyde.
Claim 8
Dependent Claim
69 words
A bonded composite material according to claim 4 where said rubbery vinyl pyridine terpolymer is a terpolymer containing from about 60 to 80% by weight of 1,3-butadiene, from 10 to 30% by weight of styrene, and from 5 to 30% by weight of 2-vinyl pyridine where the parts by weight ratio of said rubbery vinyl pyridine terpolymer to said lignin sulfonate reaction product is from about 100:5 to 100:30.
Claim 9
Dependent Claim
16 words
A bonded composite material according to claim 4 where said element is a cord of glass.
Claim 10
Dependent Claim
16 words
A bonded composite material according to claim 5 where said element is a cord of glass.
References Cited (Backward Citations)
US3227667A
Cited
US3167523A
Cited
US3300426A
Cited
GB1146304A
Cited
US3663491A
Cited
US3853605A
Cited
US3902950A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |