Environmentally durable metal honeycomb structure
Assignee: Boeing Co
•
Filing: 1975-03-24
•
Granted: 1977-05-24
•
Expires: 1995-03-24
Abstract
Abstract An environmentally durable, aluminum honeycomb structure is obtained by surface treatment and application of a polymeric film forming substance to the aluminum foil used in manufacture of honeycomb core prior to application of the adhesive and expanding the stacked and bonded core whereby the cells of the honeycomb core structure are formed. By application of a polymeric film forming substance before bonding, all surfaces of the honeycomb core are protected from corrosion and other environmental degradations. The presence of a polymeric film forming substance on honeycomb core surfaces aids in the formation of strong core-to-face sheet bonds by improving the fillet configuration and thereby the strength obtained in face sheet-to-core bonding.
Inventors
- 👤 Dennis J. Donnelly
- 👤 Joseph Arthur Marceau
- 👤 Joseph Corey McMillan
- 👤 Yukimori Moji
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:41
CPC Classifications
B; B32; B32B; B32B3/00; B32B3/10; B32B3/12; B05; B05D; B05D7/00; B05D7/14; B29; B29D; B29D24/00; B29D24/002; B29D24/005; B29D99/00; B29D99/0089; B32B37/00; B32B37/14; B32B37/146; B32B7/00; B32B7/04; B32B7/12; C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/06; C25D11/08; F; F16; F16B; F16B11/00; F16B11/006; B05D2202/00; B05D2202/20; B05D2202/25; B05D2252/00; B05D2252/10; B05D2350/00; B05D2350/10; B32B38/00; B32B2038/0052; B32B2038/0076; B32B2038/0088; B32B2255/00; B32B2255/06; B32B2255/26; B32B2305/00; B32B2305/02; B32B2305/024; B32B2307/00; B32B2307/70; B32B2307/714; B32B2311/00; B32B2311/24; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1003; Y10T428/00; Y10T428/24; Y10T428/24149
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
229 words
A method of forming an environmentally durable, corrosion resistant honeycomb core structure from aluminum metal comprising the steps of: preparing a polymer receptive oxide coating on both surfaces of an aluminum foil by anodization of said aluminum foil in phosphoric acid said anodization taking place at a temperature in the range of about 75° F. to 160° F. for 0.1 to 30 minutes at a potential of from 5 to 50 volts with phosphoric acid concentration of 5% to 50%; applying a thin coating of an organic resin primer to said surfaces; curing said primer to a coherent film to form a primed aluminum foil; emplacing an adhesive on said primed aluminum foil, said adhesive being placed in locations chosen to form node bonds in a honeycomb structure; stacking said foil; curing said adhesive to form bonds between adjacent layers of primed aluminum foil to form a bonded stack of aluminum foil layers; expanding said stack to form honeycomb cells therein forming a honeycomb core; and bonding a face sheet to opposed end edge surfaces of said core with an adhesive which wets the surfaces of said primed aluminum foil to form fillets extending into said honeycomb cells; whereby a honeycomb core panel assembly is formed having all metal surfaces of said core coated with corrosion resistant, organic coating to render said core environmentally stable and resistant to corrosion.
Claim 2
Independent Claim
229 words
A method of forming an environmentally durable, corrosion resistant honeycomb core structure from aluminum metal comprising the steps of: preparing a polymer receptive oxide coating on both surfaces of an aluminum foil by anodization of said aluminum foil in phosphoric acid said anodization taking place at a temperature in the range of about 75° F. to 160° F. for 0.1 to 30 minutes at a potential of from 5 to 50 volts with phosphoric acid concentration of 5% to 50%; applying a thin coating of an organic resin primer to said surfaces; curing said primer to a coherent film to form a primed aluminum foil; emplacing an adhesive on said primed aluminum foil, said adhesive being placed in locations chosen to form node bonds in a honeycomb structure; stacking said foil; curing said adhesive to form bonds between adjacent layers of primed aluminum foil to form a bonded stack of aluminum foil layers; expanding said stack to form honeycomb cells therein forming a honeycomb core; and bonding a face sheet to opposed end edge surfaces of said core with an adhesive which wets the surfaces of said primed aluminum foil to form fillets extending into said honeycomb cells; whereby a honeycomb core panel assembly is formed having all metal surfaces of said core coated with corrosion resistant, organic coating to render said core environmentally stable and resistant to corrosion.
Claim 3
Dependent Claim
21 words
The process of claim 1 wherein said facesheets are primed on at least a core engaging surface thereof prior to assembly.
Claim 4
Dependent Claim
59 words
The process of claim 1 wherein said polymer receptive coating is formed by anodization in phosphoric acid at the following conditions: Temperature -- 130 ± 5° F. Potential (Volts) -- 5 to 10 Time -- 0.2 to 2 minutes H 3 po 4 concentration -- 30 ± 2% by weight Current Density (amp/ft 2 ) -- 15 to 22.
Claim 5
Dependent Claim
47 words
The process of claim 1 wherein said adhesive bonding said face sheet to said core comprises an adhesive which wets the surface of said primer and extends in a fillet into said honeycomb core forming a strong bond between said face sheet and said primed aluminum foil.
Claim 6
Dependent Claim
119 words
An aluminum honeycomb core structure comprising a honeycomb core formed of aluminum foil, said aluminum foil having a polymer receptive surface thereon and being primed over its entire surface prior to emplacement of node bond adhesive and stacking and bonding; and at least one facesheet means adhered to one end edge surface of said core; wherein said polymer receptive surface is an oxide coating formed by anodization of said foil in phosphoric acid, said anodization taking place under the following conditions: Temperature -- 75° to 160° F. Potential (volts) -- 1 to 50 Time -- 0.1 to 30 minutes H 3 po 4 concentration -- 5 to 50% by weight Current Density (amp/ft 2 ) -- 1 to 200.
Claim 7
Dependent Claim
119 words
An aluminum honeycomb core structure comprising a honeycomb core formed of aluminum foil, said aluminum foil having a polymer receptive surface thereon and being primed over its entire surface prior to emplacement of node bond adhesive and stacking and bonding; and at least one facesheet means adhered to one end edge surface of said core; wherein said polymer receptive surface is an oxide coating formed by anodization of said foil in phosphoric acid, said anodization taking place under the following conditions: Temperature -- 75° to 160° F. Potential (volts) -- 1 to 50 Time -- 0.1 to 30 minutes H 3 po 4 concentration -- 5 to 50% by weight Current Density (amp/ft 2 ) -- 1 to 200.
Claim 8
Dependent Claim
9 words
The product produced by the process of claim 3.
Claim 9
Dependent Claim
9 words
The product produced by the process of claim 1.
References Cited (Backward Citations)
US2674295A
Cited
US3458385A
Cited
US3414489A
Cited
US3853681A
Cited
US3734784A
Cited
US3672972A
Cited
US3714001A
Cited
US3799848A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |