Abstract A process is disclosed for producing magnetite having an equiaxial morphology in the state of a hyperfine powder, starting from a solution of a bivalent iron solution, characterized in that: A. an aqueous suspension of Fe(OH) 2 is prepared by reacting an aqueous solution of a ferrous salt with alkali; B. said aqueous suspension of Fe(OH) 2 is fed into an autoclave into which is also introduced a quantity of air corresponding to 4-15 normal liters per 100 g of bivalent Fe; and C. the autoclave is then brought to a temperature between 150° and 200° C and maintained at this temperature until the inside pressure has stabilized itself at a constant level, thereby bringing about the formation of the desired magnetite which, once discharged from the autoclave, is washed and dried. The aqueous suspension of Fe(OH) 2 subjected to thermal decomposition in the autoclave may have present therein Cu + +ion , in a quantity between 0.3 and 1.4% by weight of the bivalent Fe. When Cu + + is present in the aqueous suspension of Fe(OH) 2 which is subjected to the thermal decomposition, it is also desirable to have dissolved therein Na 2 S in such a quantity as to provide from 20 to 60 mg of S per 100 g of bivalent Fe.
A process for producing magnetite having an equiaxial morphology in the state of a hyperfine powder, starting from an aqueous suspension of Fe(OH) 2 prepared by reacting an aqueous solution of a ferrous salt with alkali, characterized in that: (a) said aqueous suspension of Fe(OH) 2 is fed into an autoclave into which is also introduced a quantity of air corresponding to 4-15 normal liters per 100 g of bivalent Fe; and (b) the autoclave is then brought to a temperature between 150° and 200° C. and maintained at this temperature, in the presence of Cu + + ion in a quantity between 0.3 and 1.4% by weight of the bivalent Fe, until the inside pressure has stabilized itself at a constant level, thereby bringing about the formation of magnetite having a mean diameter of about 0.1μ which is removed from the autoclave, and then washed and dried.
Claim 2
Dependent Claim
148 words
A process for producing magnetite having an equiaxial morphology in the state of a hyperfine powder, starting from an aqueous suspension of Fe(OH) 2 prepared by reacting an aqueous solution of a ferrous salt with alkali, characterized in that: (a) said aqueous suspension of Fe(OH) 2 is fed into an autoclave into which is also introduced a quantity of air corresponding to 4-15 normal liters per 100 g of bivalent Fe; and (b) the autoclave is then brought to a temperature between 150° and 200° C. and maintained at this temperature, in the presence of Cu + + ion in a quantity between 0.3 and 1.4% by weight of the bivalent Fe, until the inside pressure has stabilized itself at a constant level, thereby bringing about the formation of magnetite having a mean diameter of about 0.1μ which is removed from the autoclave, and then washed and dried.
Claim 3
Dependent Claim
49 words
A process according to claim 1, wherein the aqueous suspension of Fe(OH) 2 is subjected in the autoclave to thermal decomposition in the presence of dissolved Na 2 S in such a quantity as to provide from 20 to 60 mg of S per 100 g of bivalent Fe.
Claim 4
Dependent Claim
21 words
A process according to claim 1, wherein air is introduced into the autoclave at a pressure between 4 and 10 atm.