Addition of diethylene glycol in continuous production of polyester yarn
Assignee: EIDP Inc
•
Filing: 1975-08-13
•
Granted: 1977-05-24
•
Expires: 1995-08-13
Abstract
Abstract Polyester texturing feed yarns are produced by preparing an ethylene terephthalate polymer from ethylene glycol plus a small amount of diethylene glycol, and dimethyl terephthalate or terephthalic acid, and melt-spinning the polymer into filaments. The filaments may be partially oriented by spinning at high speed without cold drawing, or may be fully drawn after conventional spinning. The diethylene glycol is added in controlled amounts to provide uniform dyeability in fabrics prepared from the yarn after texturing.
Inventors
- 👤 David E. Bosley
- 👤 Patrick J. Duncan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:21
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/58; D01F6/62; C; C08; C08G; C08G63/00; C08G63/66; C08G63/668; C08G63/672
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
86 words
An improvement in a continuous process for producing polyester texturing feed yarn from ethylene glycol and dimethyl terephthalate or terephthalic acid in which a polymer of less than 3 mole percent ether content is prepared and melt-spun to form partially oriented yarn or fully drawn yarn, wherein the improvement comprises adding diethylene glycol to increase the ether content of the polymer by an amount within the range of 0.1 to 2 mole percent to correct for non-uniformity in dyeability of products prepared from the feed yarn.
Claim 2
Dependent Claim
86 words
An improvement in a continuous process for producing polyester texturing feed yarn from ethylene glycol and dimethyl terephthalate or terephthalic acid in which a polymer of less than 3 mole percent ether content is prepared and melt-spun to form partially oriented yarn or fully drawn yarn, wherein the improvement comprises adding diethylene glycol to increase the ether content of the polymer by an amount within the range of 0.1 to 2 mole percent to correct for non-uniformity in dyeability of products prepared from the feed yarn.
Claim 3
Dependent Claim
34 words
A process as defined in claim 1 wherein dyeability of products prepared from the feed yarn is determined periodically and the amount of diethylene glycol added is adjusted to maintain a substantially uniform dyeability.
Claim 4
Dependent Claim
42 words
A process as defined in claim 1 wherein diethylene glycol is added to increase the ether content of the polymer by 1 to 2 mole percent and the total ether content of the polymer is maintained between 2 and 4 mole percent.
Claim 5
Dependent Claim
21 words
A process as defined in claim 1 wherein the total ether content of the polymer is maintained below 3 mole percent.
References Cited (Backward Citations)
US2534028A
Cited
US3051212A
Cited
US3423370A
Cited
US3496146A
Cited
US3554976A
Cited
US3829543A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |