Product reinforcing fabric and two-component weft yarn useful therein
Assignee: EIDP Inc
•
Filing: 1976-03-24
•
Granted: 1977-05-24
•
Expires: 1996-03-24
Abstract
Abstract A reinforcing fabric comprising a web of tire cords maintained in spaced relationship with sheath-core weft yarns having a cotton sheath about a core of spin-oriented polyester filaments. The weft yarns have a high initial modulus and a high break elongation which is substantially retained after heat aging the yarn at 450° or 475° F. The fabric is particularly useful as reinforcement in radial tire constructions.
Inventors
- 👤 Eugene R. Barron
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:48
CPC Classifications
D; D02; D02G; D02G3/00; D02G3/44; D02G3/48; B; B60; B60C; B60C9/00; B60C9/0042; D02G3/22; D02G3/36; D03; D03D; D03D15/00; D03D15/20; D03D15/208; D03D15/217; D03D15/283; D03D15/40; D03D15/41; D03D15/47; D03D15/50; D03D15/573; D10; D10B; D10B2201/00; D10B2201/01; D10B2201/02; D10B2331/00; D10B2331/04; D10B2505/00; D10B2505/02; D10B2505/022; Y; Y10; Y10S; Y10S57/00; Y10S57/902
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
92 words
In a reinforcing fabric having a web of tire cords maintained in spaced relationship by weft yarns, an improved weft yarn comprising a cotton sheath twisted about a core of spin-oriented polyester filaments, which yarn has an initial modulus of at least 15 grams per denier and a break elongation of 100 to 150 percent when tested before heating, and which has an initial modulus of at least 15 grams per denier and a break elongation of at least 75 percent when tested after heat aging at 450° F. for 2 minutes.
Claim 2
Dependent Claim
92 words
In a reinforcing fabric having a web of tire cords maintained in spaced relationship by weft yarns, an improved weft yarn comprising a cotton sheath twisted about a core of spin-oriented polyester filaments, which yarn has an initial modulus of at least 15 grams per denier and a break elongation of 100 to 150 percent when tested before heating, and which has an initial modulus of at least 15 grams per denier and a break elongation of at least 75 percent when tested after heat aging at 450° F. for 2 minutes.
Claim 3
Dependent Claim
25 words
A fabric as defined in claim 1 wherein the polyester core is from 35 to 65 percent of the total weight of the weft yarn.
Claim 4
Dependent Claim
17 words
A fabric as defined in claim 2 wherein the polyester core is from 80 to 240 denier.
Claim 5
Dependent Claim
24 words
A fabric as defined in claim 3 wherein the polyester core has a break elongation of 120 to 180 percent when tested before heating.
Claim 6
Dependent Claim
73 words
A yarn comprising a cotton sheath twisted about a core of spin-oriented polyester filaments, which yarn has an initial modulus of at least 15 grams per denier and a break elongation of 100 to 150 percent when tested before heating, and which has an initial modulus of at least 15 grams per denier and a break elongation of at least 75 percent when tested after heat aging at 450° F. for 2 minutes.
Claim 7
Dependent Claim
73 words
A yarn comprising a cotton sheath twisted about a core of spin-oriented polyester filaments, which yarn has an initial modulus of at least 15 grams per denier and a break elongation of 100 to 150 percent when tested before heating, and which has an initial modulus of at least 15 grams per denier and a break elongation of at least 75 percent when tested after heat aging at 450° F. for 2 minutes.
Claim 8
Dependent Claim
24 words
A yarn as defined in claim 5 wherein the polyester core is from 35 to 65 percent of the total weight of the yarn.
Claim 9
Dependent Claim
17 words
A yarn as defined in claim 6 wherein the polyester core is from 80 to 240 denier.
Claim 10
Dependent Claim
24 words
A yarn as defined in claim 7 wherein the polyester core has a break elongation of 120 to 180 percent when tested before heating.
References Cited (Backward Citations)
US2745240A
Cited
US2755214A
Cited
US2890567A
Cited
US3395744A
Cited
US3429354A
Cited
US3455100A
Cited
US3486546A
Cited
US3677318A
Cited
US3534782A
Cited
US3863683A
Cited
US3772872A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |