Silica hydrosol bound cracking catalysts

Claim 2

A process for preparing a hydrocarbon cracking catalyst which comprises: a. preparing a silica hydrosol by decreasing the pH of a sodium silicate solution to about 2.0 to 3.2, b. adding from about 0.1 to 10 percent based on the hydrosol silica content of a precursor of an oxide of titanium, zirconium, iron, boron or quadrivalent cerium and mixtures thereof thereto, c. adding clay before, during, or after hydrosol formation, d. preparing a water slurry of crystalline zeolitic aluminosilicate and adjusting the pH to about 3 to 4.5, e. mixing said zeolite slurry with the modified silica hydrosol clay slurry prepared in step (b) to prepare a spray drier feed slurry having a pH of 2.8 to 3.5, f. spray drying, before gellation occurs, g. washing, drying and recovering the product.

Claim 3

The process according to claim 1 wherein the oxide precursors are added as solutions of soluble salts.

Claim 4

The process according to claim 1 wherein the clay is added in an amount equal to about 10-65 percent of the finished catalyst.

Claim 5

The process according to claim 1 wherein the zeolitic aluminosilicate is added in an amount equal to about 4-60 percent of final catalyst.

Claim 6

The process according to claim 1 wherein the zeolitic aluminosilicate has a silica to alumina ratio of about 3.5 to 10.

Claim 7

The process according to claim 5 wherein the zeolite is faujasite having a silica to alumina ratio of 3.5 to 6.0.

Claim 8

The process according to claim 1 wherein the oxide is titanium dioxide.

Claim 9

The process according to claim 1 wherein the oxide is zirconium dioxide or a mixture of titanium and zirconium dioxides.

Claim 10

The process according to claim 1 wherein the oxide is iron oxide or a mixture of titanium and iron oxides.

Claim 11

The process according to claim 1 wherein the oxide is cerium dioxide or a mixture of titanium dioxide and cerium dioxide.

Claim 12

A process for preparing a petroleum cracking catalyst which comprises: a. preparing a silica hydrosol by rapidly adjusting the pH of a sodium silicate solution to a pH of 2.0 to 3.0 with a 20-65 percent solution of sulfuric acid, b. adding from about 0.1 to 10 percent, based on the hydrosol silica content of a precursor of an oxide of titanium, zirconium, iron, boron or quadrivalent cerium and mixtures thereof, thereto, c. adding clay before, during and after hydrosol formation, d. preparing an aqueous slurry of faujasite having a silica to alumina ratio of about 3.5 to 6.0 and adjusting the pH of said slurry to about 3.0 to 4.5 with dilute mineral acid, e. adding said slurry to the silica hydrosol-oxide-clay-slurry prepared in step (c) in an amount sufficient to provide about 15 to 25% faujasite in the final catalyst, f. spray drying the resulting slurry before gellation occurs and washing with water to decrease the sulfate content to less than 1%, g. exchanging the spray drier product with an ammonium or rare earth salt solution, h. washing, drying and recovering the product.

Claim 13

A process for preparing a petroleum cracking catalyst which comprises: a. preparing a silica hydrosol by rapidly adjusting the pH of a sodium silicate solution to a pH of 2.0 to 3.0 with a 20-65 percent solution of sulfuric acid, b. adding from about 0.1 to 10 percent, based on the hydrosol silica content of a precursor of an oxide of titanium, zirconium, iron, boron or quadrivalent cerium and mixtures thereof, thereto, c. adding clay before, during and after hydrosol formation, d. preparing an aqueous slurry of faujasite having a silica to alumina ratio of about 3.5 to 6.0 and adjusting the pH of said slurry to about 3.0 to 4.5 with dilute mineral acid, e. adding said slurry to the silica hydrosol-oxide-clay-slurry prepared in step (c) in an amount sufficient to provide about 15 to 25% faujasite in the final catalyst, f. spray drying the resulting slurry before gellation occurs and washing with water to decrease the sulfate content to less than 1%, g. exchanging the spray drier product with an ammonium or rare earth salt solution, h. washing, drying and recovering the product.

Claim 14

The process according to claim 11 wherein the spray drier product is exchanged with a rare earth solution to provide a rare earth content of about 2.5 to 5.0 weight percent in the final product.