Methods of manufacturing embossed resinous products
Assignee: Congoleum Corp
•
Filing: 1975-12-24
•
Granted: 1977-05-10
•
Expires: 1995-12-24
Abstract
Abstract A method of manufacturing an embossed resinous product having a textured surface which comprises: forming a potentially foamable resinous composition containing a blowing agent therein; heating the potentially foamable resinous composition to an elevated temperature to activate the blowing agent to cause blowing of the potentially foamable resinous composition; and then, before the freshly blown resinous composition has cooled to ambient or room temperature and while it is still relatively soft, mechanically embossing the freshly blown resinous composition under pressure by applying to its surface a previously blown, chemically embossed resinous product having a suitably textured surface; and cooling the freshly blown and now embossed resinous composition to yield an embossed resinous product.
Inventors
- 👤 James R. Clark
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:36
CPC Classifications
B; B29; B29C; B29C59/00; B29C59/02; B29C59/04; B29C59/046; B29C37/00; B29C37/0067; B32; B32B; B32B5/00; B32B5/18; B32B5/20; B44; B44C; B44C1/00; B44C1/24; B44C3/00; B44C3/04; B44C3/044; D; D06; D06N; D06N7/00; D06N7/0005; D06N7/0007; D06N7/001; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/82; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1023; Y10T156/1039; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24496; Y10T428/24504; Y10T428/249921; Y10T428/249953; Y10T428/249981
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
127 words
A method of manufacturing an embossed resinous product having a textured surface which comprises: forming a potentially foamable resinous composition containing a blowing agent therein; heating said potentially foamable resinous composition for a sufficient period of time at an elevated temperature to activate said blowing agent to cause blowing of said potentially foamable resinous composition; and then, before the freshly blown resinous composition has cooled to ambient temperature and while it is still relatively soft, mechanically embossing said freshly blown resinous composition under sufficient pressure by applying to its surface a previously heated and blown, finished, hardened, chemically embossed resinous product having a suitably textured embossing surface; and cooling said freshly blown and now embossed resinous composition to yield and embossed resinous product having a textured surface.
Claim 2
Independent Claim
127 words
A method of manufacturing an embossed resinous product having a textured surface which comprises: forming a potentially foamable resinous composition containing a blowing agent therein; heating said potentially foamable resinous composition for a sufficient period of time at an elevated temperature to activate said blowing agent to cause blowing of said potentially foamable resinous composition; and then, before the freshly blown resinous composition has cooled to ambient temperature and while it is still relatively soft, mechanically embossing said freshly blown resinous composition under sufficient pressure by applying to its surface a previously heated and blown, finished, hardened, chemically embossed resinous product having a suitably textured embossing surface; and cooling said freshly blown and now embossed resinous composition to yield and embossed resinous product having a textured surface.
Claim 3
Dependent Claim
34 words
A method as defined in claim 1 wherein said potentially foamable resinous composition containing a blowing agent is applied to the surface of a backing sheet material, prior to the heating and blowing thereof.
Claim 4
Dependent Claim
35 words
A method as defined in claim 1 wherein the heating and blowing of said potentially foamable resinous composition containing a blowing agent creates a substantially uniform blowing or expanding of said potentially foamable resinous composition.
Claim 5
Dependent Claim
63 words
A method as defined in claim 1 wherein said potentially foamable resinous composition containing a blowing agent is printed in a design or pattern with a printing ink composition containing a blow modifier, prior to the heating and blowing thereof in order to modify the uniformity of the blowing of said potentially foamable resinous composition in accordance with the printed design or pattern.
Claim 6
Dependent Claim
39 words
A method as defined in claim 1 wherein a resinous wear layer is applied to the surface of said previously blown, chemically embossed resinous product prior to its pressure application against the surface of said freshly blown resinous composition.
Claim 7
Dependent Claim
39 words
A method as defined in claim 1 wherein a release coating composition is applied to the surface of said previously blown, chemically embossed resinous product prior to its pressure application against the surface of said freshly blown resinous composition.
Claim 8
Dependent Claim
128 words
Apparatus for manufacturing an embossed resinous product having a textured surface which comprises: means for forming a potentially foamable resinous composition containing a blowing agent therein; means for heating said potentially foamable resinous composition for a sufficient period of time at an elevated temperature to activate the blowing agent to cause blowing of said potentially foamable resinous composition; means for mechanically embossing the freshly blown resinous composition under sufficient pressure to create texture on its surface comprising a previously heated and blown, finished, hardened, chemically embossed resinous product having a suitably textured embossing surface which is pressed against the surface of said freshly blown resinous composition; and means to cool said freshly blown and now embossed resinous composition to yield an embossed resinous product having a textured surface.
Claim 9
Dependent Claim
128 words
Apparatus for manufacturing an embossed resinous product having a textured surface which comprises: means for forming a potentially foamable resinous composition containing a blowing agent therein; means for heating said potentially foamable resinous composition for a sufficient period of time at an elevated temperature to activate the blowing agent to cause blowing of said potentially foamable resinous composition; means for mechanically embossing the freshly blown resinous composition under sufficient pressure to create texture on its surface comprising a previously heated and blown, finished, hardened, chemically embossed resinous product having a suitably textured embossing surface which is pressed against the surface of said freshly blown resinous composition; and means to cool said freshly blown and now embossed resinous composition to yield an embossed resinous product having a textured surface.
Claim 10
Dependent Claim
25 words
Apparatus as defined in claim 7 wherein said printing ink composition contains a blow modifier to modify the blowing of said potentially foamable resinous composition.
Claim 11
Dependent Claim
36 words
A method as defined in claim 1, wherein said potentially foamable resinous composition containing a blowing agent is printed with a printing ink composition, prior to the heating and blowing of said potentially foamable resinous composition.
Claim 12
Dependent Claim
41 words
Apparatus as defined in claim 7, wherein means is provided for printing said potentially foamable resinous composition containing a blowing agent with a printing ink composition, prior to the application of heat to cause blowing of said potentially foamable resinous composition.
Claim 13
Dependent Claim
25 words
Apparatus as defined in claim 7, wherein said means for mechanically embossing said freshly blown resinous composition is in the form of an endless belt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |