Method of manufacturing an endless printing belt for a belt type printing apparatus
Assignee: Kyuroku KK
•
Filing: 1976-06-11
•
Granted: 1977-05-10
•
Expires: 1996-06-11
Abstract
Abstract A thin heat-treated steel sheet material having marginal zones formed along four edges thereof is photo-etched to produce printing types and the like which are integral with the sheet material. The reverse side thereof is also slightly photo-etched for removing and equalizing the strains on both side surfaces of the sheet. The transverse marginal zones are utilized for successive welding and trimming operations. The welding of the longitudinal edges of the sheet material for making the material into an endless form and its temper is made by subjecting said edges to primary and secondary electron beams.
Inventors
- 👤 Soroku Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:35
CPC Classifications
B; B41; B41J; B41J1/00; B41J1/20; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49826; Y10T29/49861
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
181 words
A method of manufacturing an endless printing belt for belt type printing apparatus, which comprises the steps of forming on one side of a thin heat-treated steel sheet material, with marginal zones formed along the four sides thereof, printing types, timing marks, sprockets and non-etched zones by a photo-etching process, said non-etched zones being located in the transverse marginal zones, subjecting the reverse side surface of the sheet material to a slight degree of photoetching, heating the sheet material, perforating the non-etched zones with reference openings to be used for welding and trimming operations, removing the longitudinal end portions of the sheet, grinding the end edges of the sheet, securing the end edges together with the type surfaces facing outwardly, welding the secured edges of the sheet material, by using an electron beam focused into a circular spot, applying to the welded zone an additional electron beam of lower energy density after completion of the welding with decreased filament current and diverged spot of the beam, removing the transverse edge portions of the sheet by grinding, and finishing the type faces.
Claim 2
Independent Claim
181 words
A method of manufacturing an endless printing belt for belt type printing apparatus, which comprises the steps of forming on one side of a thin heat-treated steel sheet material, with marginal zones formed along the four sides thereof, printing types, timing marks, sprockets and non-etched zones by a photo-etching process, said non-etched zones being located in the transverse marginal zones, subjecting the reverse side surface of the sheet material to a slight degree of photoetching, heating the sheet material, perforating the non-etched zones with reference openings to be used for welding and trimming operations, removing the longitudinal end portions of the sheet, grinding the end edges of the sheet, securing the end edges together with the type surfaces facing outwardly, welding the secured edges of the sheet material, by using an electron beam focused into a circular spot, applying to the welded zone an additional electron beam of lower energy density after completion of the welding with decreased filament current and diverged spot of the beam, removing the transverse edge portions of the sheet by grinding, and finishing the type faces.
Claim 3
Dependent Claim
19 words
A method as claimed in claim 1, in which the steel sheet material is a heat-treated martensite stainless steel.
Claim 4
Dependent Claim
30 words
A method as claimed in claim 2, in which the heating of the sheet material after photo-etching is conducted at a temperature of about 200° C for about 2 hours.
Claim 5
Independent Claim
150 words
A method of manufacturing an endless printing belt for belt type printing apparatus, which comprises the steps of forming on one side of a thin heat-treated steel sheet material, with marginal zones formed along the four sides thereof, printing types, timing marks, sprockets and non-etched zones by a photo-etching process, said non-etched zones being located in the transverse marginal zones, subjecting the reverse side surface of the sheet material to a slight degree of photoetching, heating the sheet material, perforating the non-etched zones with reference openings to be used for welding and trimming operations, removing the longitudinal end portions of the sheet, grinding the end edges of the sheet, securing the end edges together with the type surfaces facing outwardly, welding the secured edges of the sheet material, annealing the welded zone after completion of the welding, removing the transverse edge portions of the sheet, and finishing the type faces.
Claim 6
Independent Claim
150 words
A method of manufacturing an endless printing belt for belt type printing apparatus, which comprises the steps of forming on one side of a thin heat-treated steel sheet material, with marginal zones formed along the four sides thereof, printing types, timing marks, sprockets and non-etched zones by a photo-etching process, said non-etched zones being located in the transverse marginal zones, subjecting the reverse side surface of the sheet material to a slight degree of photoetching, heating the sheet material, perforating the non-etched zones with reference openings to be used for welding and trimming operations, removing the longitudinal end portions of the sheet, grinding the end edges of the sheet, securing the end edges together with the type surfaces facing outwardly, welding the secured edges of the sheet material, annealing the welded zone after completion of the welding, removing the transverse edge portions of the sheet, and finishing the type faces.
References Cited (Backward Citations)
US1094299A
Cited
US1565583A
Cited
US1852115A
Cited
US2754606A
Cited
US2762297A
Cited
US2896312A
Cited
US3279050A
Cited
US3436515A
Cited
US3431627A
Cited
US3763544A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |