Thermosetting polyester composition containing normally solid carboxy-containing diene polymer
Assignee: Phillips Petroleum Co
•
Filing: 1976-04-22
•
Granted: 1977-04-26
•
Expires: 1996-04-22
Abstract
Abstract A thermosettable composition suitable for preparing reinforced plastic articles is prepared by combining an unsaturated polyester, a normally solid carboxy-containing polymer of a conjugated diene, a vinyl monomer, a catalyst and a reinforcing agent or filler. Preferably the composition is prepared utilizing a mixer giving moderate shear such as a twin-rotor mixer. The resulting composition when cured exhibits high impact strength and good surface finish.
Inventors
- 👤 Aubrey South, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:07
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/24; C08K3/26; C08K5/00; C08K5/04; C08K5/09; C08K7/00; C08K7/02; C08K7/04; C08K7/14; C08L; C08L13/00; C08L67/00; C08L67/06; Y; Y10; Y10S; Y10S525/00; Y10S525/901
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
59 words
A composition comprising: a. an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; b. a normally solid carboxy-containing polymer of a conjugated diene having a weight average molecular weight within the range of 30,000 to 400,000; c. a vinyl monomer; d. a catalyst; and e. at least one of a reinforcing agent or a filler.
Claim 2
Dependent Claim
59 words
A composition comprising: a. an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; b. a normally solid carboxy-containing polymer of a conjugated diene having a weight average molecular weight within the range of 30,000 to 400,000; c. a vinyl monomer; d. a catalyst; and e. at least one of a reinforcing agent or a filler.
Claim 3
Dependent Claim
37 words
A composition according to claim 1 wherein said polymer of a conjugated diene has a weight average molecular weight within the range of 50,000 to 250,000 and an inherent viscosity within the range of 0.6 to 2.
Claim 4
Dependent Claim
20 words
A composition according to claim 1 wherein said polymer of a conjugated diene is a copolymer of butadiene and styrene.
Claim 5
Dependent Claim
18 words
A composition according to claim 1 wherein said polyester is prepared by reacting fumaric acid and propylene glycol.
Claim 6
Dependent Claim
12 words
A composition according to claim 1 wherein said vinyl monomer is styrene.
Claim 7
Dependent Claim
50 words
A composition according to claim 1 wherein a ratio of (a) to (b) is within the range of 5:1 to 1:1 and wherein said vinyl monomer is present in an amount within the range of 30 to 200 parts by weight per 100 parts by weight of (a) plus (b).
Claim 8
Dependent Claim
12 words
A composition according to claim 1 wherein said catalyst is a peroxide.
Claim 9
Dependent Claim
12 words
A composition according to claim 1 containing glass fibers and calcium carbonate.
Claim 10
Dependent Claim
218 words
A composition according to claim 1 wherein said unsaturated polyester is produced by reacting fumaric acid and propylene glycol, said normally solid carboxy-containing polymer is a copolymer of butadiene and styrene characterized by a vinyl addition of 5 to 76 percent and having 0.01 to 5 weight percent carboxyl content, said vinyl monomer is styrene, a ratio of (a) to (b) being within the range of 5:1 to 1:1, said vinyl monomer is present in an amount within the range of 30 to 200 parts by weight per 100 parts by weight of (a) plus (b), said catalyst is tertiary butyl perbenzoate present in an amount within the range of 1-5 parts by weight per 100 parts by weight of (a) plus (b) and wherein said composition contains calcium carbonate filler in an amount within the range of 200 to 800 parts by weight of filler per 100 parts per weight of (a) plus (b), glass fiber reinforcing agent in an amount within the range of 40 to 200 parts by weight per 100 parts by weight of (a) plus (b), 1 to 15 parts by weight of zinc stearate per 100 parts by weight of (a) plus (b) and 1 to 10 parts by weight of magnesium hydroxide per 100 parts by weight of (a) plus (b).
Claim 11
Dependent Claim
13 words
A cured article produced by subjecting the composition of claim 9 to heat.
Claim 12
Dependent Claim
13 words
A cured article produced by subjecting the composition of claim 1 to heat.
Claim 13
Independent Claim
76 words
A method of forming thermosetting compositions suitable for preparing reinforced plastic articles comprising milling together under conditions of moderate shear: a. an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; b. a normally solid carboxy-containing polymer of a conjugated diene having a weight average molecular weight within the range of 30,000 to 400,000; c. a vinyl monomer; d. a catalyst; and e. at least one of a reinforcing agent or a filler.
Claim 14
Independent Claim
76 words
A method of forming thermosetting compositions suitable for preparing reinforced plastic articles comprising milling together under conditions of moderate shear: a. an unsaturated polyester prepared by reacting an unsaturated dicarboxylic acid and a polyol; b. a normally solid carboxy-containing polymer of a conjugated diene having a weight average molecular weight within the range of 30,000 to 400,000; c. a vinyl monomer; d. a catalyst; and e. at least one of a reinforcing agent or a filler.
Claim 15
Dependent Claim
18 words
A method according to claim 12 wherein said milling is done with a twin-rotor mixer using sigma blades.
Claim 16
Dependent Claim
190 words
A method according to claim 13 wherein said unsaturated polyester is produced by reacting fumaric acid and propylene glycol, said normally solid carboxy-containing polymer is a copolymer of butadiene and styrene characterized by a vinyl unsaturation of 5 to 76 percent and having 0.01 to 5 weight percent carboxyl content, said vinyl monomer is styrene, a ratio of (a) to (b) is within the range of 5:1 to 1:1, said vinyl monomer is present in an amount within the range of 30 to 200 parts by weight per 110 parts by weight of (a) plus (b), said catalyst is tertiary butyl perbenzoate and wherein said composition contains calcium carbonate filler in an amount within the range of 200 to 800 parts by weight of filler per 100 parts per weight of (a) plus (b), glass fiber reinforcing agent in an amount within the range of 40 to 200 parts by weight of (a) plus (b), 1 to 15 parts by weight of a lubricant per 100 parts by weight of (a) plus (b) and 1 to 10 parts by weight of an oxide or hydroxide of a group II metal.
Claim 17
Dependent Claim
18 words
A method according to claim 13 wherein said shear produces a temperature rise of 2° to 30° C.
Claim 18
Dependent Claim
31 words
A method according to claim 12 wherein the resulting composition is subjected to curing conditions of 100° to 200° C for a time within the range of 1 to 15 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |