Composition for making garnet films for improved magnetic bubble devices
Assignee: RCA Corp
•
Filing: 1975-03-13
•
Granted: 1977-04-19
•
Expires: 1995-03-13
Abstract
Abstract Garnet films suitable for bubble devices which are substituted with bismuth, aluminum or gallium and certain rare earth ions have improved magneto optic properties and can be formed at low temperatures on gadolinium gallium garnet substrates.
Inventors
- 👤 Aline Akselrad
- 👤 Richard Edwin Novak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:30
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/14; H01F41/24; H01F41/28; C; C30; C30B; C30B19/00; C30B19/02; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/28; G; G11; G11C; G11C19/00; G11C19/02; G11C19/08; G11C19/0808
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
94 words
A flux composition from which single crystal garnet films having growth induced uniaxial anisotropy can be epitaxially grown which comprises essentially of about 75 mol percent of lead oxide, about 15 mol percent of bismuth oxide, from about 8 - 8.5 mol percent of iron oxide, from about 0.5 - 1.0 mol percent of an oxide selected from one or more of the group consisting of yttrium oxide and trivalent rare earth oxides and from about 1 - 1.5 mol percent of gallium oxide, aluminum oxide or a mixture of gallium and aluminum oxides.
Claim 2
Dependent Claim
94 words
A flux composition from which single crystal garnet films having growth induced uniaxial anisotropy can be epitaxially grown which comprises essentially of about 75 mol percent of lead oxide, about 15 mol percent of bismuth oxide, from about 8 - 8.5 mol percent of iron oxide, from about 0.5 - 1.0 mol percent of an oxide selected from one or more of the group consisting of yttrium oxide and trivalent rare earth oxides and from about 1 - 1.5 mol percent of gallium oxide, aluminum oxide or a mixture of gallium and aluminum oxides.
Claim 3
Dependent Claim
32 words
A flux composition according to claim 1 wherein about 8.4 mol percent of iron oxide, about 0.5 mol percent of thulium oxide and about 1.1 mol percent of gallium oxide is present.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-18 | 1980-10-18 | 1981-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-18 | 1984-10-18 | 1985-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-18 | 1988-10-18 | 1989-04-19 | $7700.00 | Window Closed / Lapsed |