Thin layer leaching method
Assignee: Bechtel Civil and Minerals Inc
•
Filing: 1975-03-28
•
Granted: 1977-04-12
•
Expires: 1995-03-28
Abstract
Abstract A technique is provided for leaching particulate ores for recovering metal values. Ore is crushed to less than about one inch with at least 25% being greater than 4 mesh. The crushed ore is mixed with a small amount of acid and the moistened mixture is kept in a curling pile for about two days for dehydration and induration of the ore. The induration is sufficient that the ore can sustain the weight of a thin layer of about one-half to one meter thick without appreciable compacting. The indurated ore is spread on a permeable substrate in a thin layer about one-half to one meter thick. A leaching solution is then percolated through this thin layer to remove the metal values. The initial effluent leach liquor has high metal values and low acid content and is passed to a solvent extraction system where the metal values are recovered. The solvent extraction raffinate, which is high in acid, is recirculated as a leach liquid. Leaching of the thin layer is essentially countercurrent since progressively leaner leach liquids are used. Leaching of extremely fine ore is provided by mixing with at least 50% particles larger than about 4 mesh.
Inventors
- 👤 Paul H. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:29
CPC Classifications
C; C22; C22B; C22B3/00; C22B3/04; C22B3/06; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 75
Claim 1
Independent Claim
53 words
A method for leaching material values from particles comprising the steps of: forming a thin layer of particles having more than about 25% by weight particles larger than about 4 mesh, the thickness of the layer being less than about one and 1/2 meters; and percolating a leach liquid downwardly through the layer.
Claim 2
Independent Claim
53 words
A method for leaching material values from particles comprising the steps of: forming a thin layer of particles having more than about 25% by weight particles larger than about 4 mesh, the thickness of the layer being less than about one and 1/2 meters; and percolating a leach liquid downwardly through the layer.
Claim 3
Dependent Claim
16 words
A method as defined in claim 1 wherein the layer is formed on a permeable substrate.
Claim 4
Dependent Claim
24 words
A method as defined in claim 1 wherein the forming step comprises forming a thin layer having a thickness greater than about one-half meter.
Claim 5
Dependent Claim
33 words
A method as defined in claim 3 wherein the step of forming a layer comprises spreading the particles on a substrate having a slope of approximately the angle of repose of the particles.
Claim 6
Dependent Claim
38 words
A method as claimed in claim 4 further comprising the steps of: forming a second layer of ore particles over the first formed layer after the percolating step; and percolating a leach liquid downwardly through the second layer.
Claim 7
Dependent Claim
76 words
A method as defined in claim 4 wherein the step of forming comprises increasing the permeability of a thin layer on the face of a pile resting at the angle of repose and further comprising: removing the first thin layer after the percolating step; increasing the permeability of a second thin layer at the angle of repose beneath the position of the first thin layer; and percolating a leach liquid downwardly through the second thin layer.
Claim 8
Dependent Claim
29 words
A method as defined in claim 3 further comprising the step of contacting the particles with a strong leach solution and curing the so-contacted particles before the percolating step.
Claim 9
Dependent Claim
17 words
A method as defined in claim 7 wherein the curing step is performed before the forming step.
Claim 10
Dependent Claim
42 words
A method as defined in claim 7 wherein the curing step is conducted for a sufficient time to indurate the particles sufficiently to withstand spreading in a layer in the range of from about one-half to one meter thick without substantial compaction.
Claim 11
Dependent Claim
51 words
A method as defined in claim 3 further comprising, before the forming step, the step of forming a mixture of particles by mixing relatively fine particles with a sufficient quantity of coarse particles so that the resulting mixture has more than about 25% by weight particles larger than about 4 mesh.
Claim 12
Dependent Claim
32 words
A method as defined in claim 10 wherein the relatively fine particles are a metal bearing ore to be leached and the relatively coarse particles are essentially inert to the leach liquid.
Claim 13
Dependent Claim
38 words
A method as defined in claim 1 wherein the percolating step comprises percolating a weight of leach liquid at a rate in the range of from about 0.5 to 3.5 times the weight of the particles per day.
Claim 14
Dependent Claim
29 words
A method as defined in claim 1 wherein the percolating step comprises recirculating at least a portion of the effluent leach liquid and repercolating it through the thin layer.
Claim 15
Independent Claim
100 words
A method for reacting a reagent in solution with particles of solids comprising the steps of: forming a layer of particles subject to compaction under their own weight having a thickness in the range of from about one-half to one and 1/2 meters, the layer having a sufficiently small thickness that the permeability of the bottom of the layer is not appreciably less than the permeability of the top of the layer; applying a solution containing reagent to the top of the layer; percolating the solution downwardly through the layer; and withdrawing the solution from the bottom of the layer.
Claim 16
Independent Claim
100 words
A method for reacting a reagent in solution with particles of solids comprising the steps of: forming a layer of particles subject to compaction under their own weight having a thickness in the range of from about one-half to one and 1/2 meters, the layer having a sufficiently small thickness that the permeability of the bottom of the layer is not appreciably less than the permeability of the top of the layer; applying a solution containing reagent to the top of the layer; percolating the solution downwardly through the layer; and withdrawing the solution from the bottom of the layer.
Claim 17
Dependent Claim
31 words
A method as defined in claim 14 wherein the forming step comprises forming a thin layer of particles having more than about 25% by weight particles larger than about 4 mesh.
Claim 18
Dependent Claim
33 words
A method as defined in claim 14 wherein the step of forming a layer comprises spreading the particles on a substrate having a slope of approximately the angle of repose of the particles.
Claim 19
Dependent Claim
68 words
A method as defined in claim 14 wherein the forming step comprises ripping a thin layer of particles on a pre-existing bed of particles for enhancing the permeability of the thin layer and further comprising: removing the thin layer after the percolating step; ripping a second layer beneath the position of the first layer for enhancing its permeability; and percolating a solution containing reagent through the second layer.
Claim 20
Dependent Claim
24 words
A method as defined in claim 17 wherein the layers are formed on the face of a pile at approximately the angle of repose.
Claim 21
Dependent Claim
23 words
A method as defined in claim 17 wherein the layer is formed on an approximately horizontal top of a pre-existing bed of particles.
Claim 22
Dependent Claim
60 words
A method as defined in claim 14 further comprising the step of contacting the particles with a strong leach solution and curing the so-contacted particles before the forming step for a sufficient time to indurate the particles sufficiently to withstand spreading in a layer in the range of from about one-half to one and 1/2 meters thick without substantial compaction.
Claim 23
Dependent Claim
30 words
A method as defined in claim 14 wherein the particles comprise an ore containing metal values and the solution contains a reagent for leaching the metal values from the ore.
Claim 24
Independent Claim
125 words
A method for reacting a reagent in solution with particles of solids comprising the steps of: mixing relatively fine particles of metal bearing ore to be leached with relatively coarse particles essentially inert to the reagent in sufficient quantities that the resulting mixture has more than about 25% by weight particles larger than about 4 mesh; forming a layer of particles subject to compaction under their own weight, the layer having a sufficiently small thickness that the permeability of the bottom of the layer is not appreciably less than the permeability of the top of the layer; applying a solution containing reagent to the top of the layer; percolating the solution downwardly through the layer; and withdrawing the solution from the bottom of the layer.
Claim 25
Independent Claim
125 words
A method for reacting a reagent in solution with particles of solids comprising the steps of: mixing relatively fine particles of metal bearing ore to be leached with relatively coarse particles essentially inert to the reagent in sufficient quantities that the resulting mixture has more than about 25% by weight particles larger than about 4 mesh; forming a layer of particles subject to compaction under their own weight, the layer having a sufficiently small thickness that the permeability of the bottom of the layer is not appreciably less than the permeability of the top of the layer; applying a solution containing reagent to the top of the layer; percolating the solution downwardly through the layer; and withdrawing the solution from the bottom of the layer.
Claim 26
Dependent Claim
22 words
A method as defined in claim 22 wherein the thin layer has a thickness in order of about 1/2 to one meter.
Claim 27
Independent Claim
102 words
A method for neutralizing an acidic solution with particles of solids comprising the steps of: forming a layer of particles subject to compaction under their own weight, the layer having a sufficiently small thickness that the permeability of the bottom of the layer is not appreciably less than the permeability of the top of the layer, the particles being selected from the group consisting of limestone, dolomite, calcareous rock and rock containing iron oxide; applying the acidic solution to the top of the layer; percolating the solution downwardly through the layer; and withdrawing the neutralized solution from the bottom of the layer.
Claim 28
Independent Claim
102 words
A method for neutralizing an acidic solution with particles of solids comprising the steps of: forming a layer of particles subject to compaction under their own weight, the layer having a sufficiently small thickness that the permeability of the bottom of the layer is not appreciably less than the permeability of the top of the layer, the particles being selected from the group consisting of limestone, dolomite, calcareous rock and rock containing iron oxide; applying the acidic solution to the top of the layer; percolating the solution downwardly through the layer; and withdrawing the neutralized solution from the bottom of the layer.
Claim 29
Dependent Claim
165 words
A process for operating a leaching plant having first and second curing stations and first and second leach pads comprising the steps of: leaching a first batch of ore in a thin layer on the first leach pad for first and second days; curing a second batch of ore in the first curing station for the first and second days; leaching a third batch of ore in a thin layer on the second leach pad for the second day and a third day; curing a fourth batch of ore in the second curing station for the second and third days; leaching the second batch of ore in a thin layer on the first leach pad for the third day and a fourth day; curing a fifth batch of ore in the first leaching station for the third and fourth days; and continuing the leaching and curing steps in the first and second sets of curing station and leach pad, respectively, on alternating pairs of days.
Claim 30
Dependent Claim
165 words
A process for operating a leaching plant having first and second curing stations and first and second leach pads comprising the steps of: leaching a first batch of ore in a thin layer on the first leach pad for first and second days; curing a second batch of ore in the first curing station for the first and second days; leaching a third batch of ore in a thin layer on the second leach pad for the second day and a third day; curing a fourth batch of ore in the second curing station for the second and third days; leaching the second batch of ore in a thin layer on the first leach pad for the third day and a fourth day; curing a fifth batch of ore in the first leaching station for the third and fourth days; and continuing the leaching and curing steps in the first and second sets of curing station and leach pad, respectively, on alternating pairs of days.
Claim 31
Dependent Claim
45 words
A process as defined in claim 25 further comprising the steps of: cycling at least a portion of effluent from the second day of each leaching step as leach solution input on the first day of a concurrent leaching step on the other leach pad.
Claim 32
Dependent Claim
37 words
A process as defined in claim 25 further comprising the step of: leaching each batch of ore in a thin layer on the face of a tailings pile after its respective leaching step on the leach pad.
Claim 33
Independent Claim
253 words
A method of leaching metal values from ore comprising the steps of: mixing a first batch of ore with a strong leaching solution; curing the first batch of ore in a first curing station for about two days; mixing a second batch of ore with a strong leaching solution about a day after the first mixing step; curing the second batch of ore in a second curing station for about two days; spreading the first batch of ore in a thin layer in a first leach pad about a day after the second mixing step; mixing a third batch of ore with a strong leaching solution about one day after the second mixing step; curing the third batch of ore in the first curing station for about two days; leaching the first batch of ore for about two days concurrent with the third curing step by percolating leach solution therethrough; spreading the second batch of ore in a thin layer on a second leach pad about a day after the third mixing step; mixing a fourth batch of ore with a strong leaching solution about one day after the third mixing step; curing the fourth batch of ore in the second curing station for about two days; leaching the second batch of ore for about two days concurrent with the fourth curing step by percolating leach solution therethrough; and repeating the steps on alternate days for the first curing station and leach pad and for the second curing station and leach pad, respectively.
Claim 34
Independent Claim
253 words
A method of leaching metal values from ore comprising the steps of: mixing a first batch of ore with a strong leaching solution; curing the first batch of ore in a first curing station for about two days; mixing a second batch of ore with a strong leaching solution about a day after the first mixing step; curing the second batch of ore in a second curing station for about two days; spreading the first batch of ore in a thin layer in a first leach pad about a day after the second mixing step; mixing a third batch of ore with a strong leaching solution about one day after the second mixing step; curing the third batch of ore in the first curing station for about two days; leaching the first batch of ore for about two days concurrent with the third curing step by percolating leach solution therethrough; spreading the second batch of ore in a thin layer on a second leach pad about a day after the third mixing step; mixing a fourth batch of ore with a strong leaching solution about one day after the third mixing step; curing the fourth batch of ore in the second curing station for about two days; leaching the second batch of ore for about two days concurrent with the fourth curing step by percolating leach solution therethrough; and repeating the steps on alternate days for the first curing station and leach pad and for the second curing station and leach pad, respectively.
Claim 35
Dependent Claim
73 words
A process as defined in claim 28 further comprising the steps of: removing the first batch of ore from the first leach pad at the end of the first mentioned leaching step; spreading the first batch of ore in a thin layer on the face of a tailings pile; leaching the first batch of ore on the face of the trailings pile for at least about a day by percolating leach solution therethrough.
Claim 36
Dependent Claim
53 words
A process as defined in claim 28 further comprising the step of: cycling at least a portion of the second day's effluent from the first mentioned leaching step on the first batch of ore as leach solution on the first day of the second mentioned leaching step on the second batch of ore.
Claim 37
Independent Claim
114 words
A method for leaching metal values from particles comprising the steps of: forming a thin layer of particles subject to compaction under their own weight; introducing a leach liquid to the top surface of the layer; percolating the leach liquid downwardly through the layer for leaching metal values therefrom; and withdrawing the leach liquid from the bottom surface of the layer; and wherein the layer has a thickness greater than about one-half meter and a sufficiently small thickness that the yield of metal values from a portion of the layer adjacent the bottom surface is not appreciably less than the yield of metal values from a portion of the layer adjacent the top surface.
Claim 38
Independent Claim
114 words
A method for leaching metal values from particles comprising the steps of: forming a thin layer of particles subject to compaction under their own weight; introducing a leach liquid to the top surface of the layer; percolating the leach liquid downwardly through the layer for leaching metal values therefrom; and withdrawing the leach liquid from the bottom surface of the layer; and wherein the layer has a thickness greater than about one-half meter and a sufficiently small thickness that the yield of metal values from a portion of the layer adjacent the bottom surface is not appreciably less than the yield of metal values from a portion of the layer adjacent the top surface.
Claim 39
Dependent Claim
31 words
A method as defined in claim 31 wherein the forming step comprises forming a thin layer of particles having more than about 25% by weight particles larger than about 4 mesh.
Claim 40
Dependent Claim
26 words
A method as defined in claim 31 wherein the thin layer has a thickness in the range of from about 1/2 to one and 1/2 meters.
Claim 41
Dependent Claim
33 words
A method as defined in claim 31 wherein the step of forming a layer comprises spreading the particles on a substrate having a slope of approximately the angle of repose of the particles.
Claim 42
Dependent Claim
60 words
A method as defined in claim 31 further comprising the step of contacting the particles with a strong leach solution and curing the so-contacted particles before the percolating step for a sufficient time to indurate the particles sufficiently to withstand spreading in a layer in the range of from about one-half to one and one-half meters thick without substantial compaction.
Claim 43
Dependent Claim
54 words
A method as defined in claim 31 further comprising, before the forming step, mixing relatively fine particles of metal bearing ore to be leached with relatively coarse particles essentially inert to the leaching liquid in sufficient quantities that the resulting mixture has more than about 25% by weight particles larger than about 4 mesh.
Claim 44
Dependent Claim
38 words
A method as defined in claim 31 wherein the percolating step comprises percolating a weight of leach liquid at a rate in the range of from about 0.5 to 3.5 times the weight of the particles per day.
Claim 45
Dependent Claim
29 words
A method as defined in claim 31 wherein the percolating step comprises recirculating at least a portion of the effluent leach liquid and repercolating it through the thin layer.
Claim 46
Independent Claim
65 words
A method for leaching a solid comprising the steps of: forming a thin layer of particles of the solid on a slope approximately at the angle of repose of the particles, the thin layer being less than about one meter thick; spraying a leach liquid on the sloping face of the thin layer of particles; and recovering leach liquid at the toe of the slope.
Claim 47
Independent Claim
65 words
A method for leaching a solid comprising the steps of: forming a thin layer of particles of the solid on a slope approximately at the angle of repose of the particles, the thin layer being less than about one meter thick; spraying a leach liquid on the sloping face of the thin layer of particles; and recovering leach liquid at the toe of the slope.
Claim 48
Dependent Claim
40 words
A method as defined in claim 39 further comprising the steps of: intermittently adding thin layers of particles of the solid over the first formed thin layer; and spraying a leach liquid on the face of each subsequent thin layer.
Claim 49
Dependent Claim
19 words
A method as defined in claim 39 wherein the slope is the face of a pile of similar particles.
Claim 50
Dependent Claim
43 words
A method as defined in claim 39 further comprising the steps of: removing the thin layer of particles from the slope after the recovering step; and repeating the forming, spraying and removing steps with an additional layer of thin particles on the slope.
Claim 51
Dependent Claim
19 words
A method as defined in claim 39 wherein the thin layer has a thickness greater than about 1/2 meter.
Claim 52
Dependent Claim
25 words
A method as defined in claim 43 wherein at least about 25% by weight of the particles have a size larger than about 4 mesh.
Claim 53
Dependent Claim
33 words
In a process for leaching metal values from an ore the improvement comprising: mixing relatively coarse inert particles with relatively fine ore; and percolating leach liquid through the mixed ore and inert particles.
Claim 54
Dependent Claim
33 words
In a process for leaching metal values from an ore the improvement comprising: mixing relatively coarse inert particles with relatively fine ore; and percolating leach liquid through the mixed ore and inert particles.
Claim 55
Dependent Claim
23 words
A method as defined in claim 45 further comprising the step of removing coarse inert particles from the mixture after the percolating step.
Claim 56
Dependent Claim
30 words
In a process as defined in claim 45 the further improvement wherein about 2/3 by weight of the mixture comprises coarse inert particles and about 1/3 comprises relatively fine ore.
Claim 57
Dependent Claim
34 words
In a process as defined in claim 45 the further improvement comprising mixing at least 25% by weight of the final mixture of inert particles having a particle size greater than about 4 mesh.
Claim 58
Dependent Claim
42 words
In a process as defined in claim 48 the further improvement wherein the percolating step comprises percolating leach liquid through the mixed ore and inert particles in a layer having a thickness in the range of from about one-half to one meter.
Claim 59
Dependent Claim
45 words
In a process as defined in claim 45 the further improvement wherein the percolating step comprises percolating leach liquid through the mixed ore and inert particles in a layer having a thickness in the range of from about one-half to one and one-half meters thick.
Claim 60
Dependent Claim
78 words
In a process as defined in claim 45 the further improvement comprising, between the mixing and percolating steps, the steps of: contacting the mixed inert particles and fine ore with a strong leaching solution; and curing the mixture of coarse inert particles, fine ore and strong leach liquid for a sufficient time to indurate the ore sufficiently to withstand the weight of a layer in the range of from about 1/2 to one meter thick without substantial compacting.
Claim 61
Dependent Claim
53 words
In a process as defined in claim 51 the further improvement wherein the contacting step comprises contacting the mixed coarse inert particles and fine ore with a sufficient quantity of strong leach solution that the total liquid content of the mixture is in the range of from about 8 to 18% by weight.
Claim 62
Independent Claim
98 words
A method for leaching metal values from ore particles comprising the steps of: contacting the ore particles with a strong leaching solution for a sufficient time to indurate the ore sufficiently to sustain the weight of a layer of ore in the range of from about 1/2 to one and one-half meter thick without appreciable compacting; placing the indurated ore particles on a permeable substrate in a layer in the range of from about one-half of one and one-half meter thick; and percolating liquid down through the layer for leaching metal values from the layer of ore particles.
Claim 63
Independent Claim
98 words
A method for leaching metal values from ore particles comprising the steps of: contacting the ore particles with a strong leaching solution for a sufficient time to indurate the ore sufficiently to sustain the weight of a layer of ore in the range of from about 1/2 to one and one-half meter thick without appreciable compacting; placing the indurated ore particles on a permeable substrate in a layer in the range of from about one-half of one and one-half meter thick; and percolating liquid down through the layer for leaching metal values from the layer of ore particles.
Claim 64
Dependent Claim
41 words
A method as defined in claim 53 wherein the quantity of strong leaching solution is sufficient that the resultant mixture has a total weight of liquid relative to the weight of ore in the range of from about 8 to 18%.
Claim 65
Dependent Claim
34 words
A method as defined in claim 53 further comprising the step, preceding the contacting step, of sizing the ore to have more than about 25% by weight particles in excess of about 4 mesh.
Claim 66
Dependent Claim
43 words
A method as defined in claim 55 wherein the sizing step comprises mixing relatively fine ore with relatively coarse inert particles in a sufficient quantity that the resultant mixture has more than about 25% by weight of particles greater than about 4 mesh.
Claim 67
Dependent Claim
31 words
A method as defined in claim 53 wherein the placing step comprises placing the ore particles on a substrate having a slope approximately the angle of repose of the ore particles.
Claim 68
Independent Claim
97 words
A method for leaching metal values from particles of ore comprising the steps of: forming a first thin layer of particles of ore; percolating a first leach solution through the first thin layer and recovering a first effluent; thereafter percolating a second leach solution through the first thin layer and recovering a second effluent; forming a second thin layer of particles of ore; percolating at least a portion of the second effluent through the second thin layer and recovering a third effluent; and recovering metal values from at least a portion of the first and third effluents.
Claim 69
Independent Claim
97 words
A method for leaching metal values from particles of ore comprising the steps of: forming a first thin layer of particles of ore; percolating a first leach solution through the first thin layer and recovering a first effluent; thereafter percolating a second leach solution through the first thin layer and recovering a second effluent; forming a second thin layer of particles of ore; percolating at least a portion of the second effluent through the second thin layer and recovering a third effluent; and recovering metal values from at least a portion of the first and third effluents.
Claim 70
Dependent Claim
30 words
A method as defined in claim 58 further comprising recirculating at least a portion of the second effluent through the first thin layer for enhancing its content of metal values.
Claim 71
Dependent Claim
30 words
A method as defined in claim 58 further comprising recirculating at least a portion of the third effluent through the second thin layer for enhancing its content of metal values.
Claim 72
Dependent Claim
55 words
A method as defined in claim 58 further comprising: contacting the particles of ore with a strong leaching solution before the first percolating step; curing the so-contacted ore before the first percolating step; and cycling the very first effluent from the first percolating step to the contacting step for a subsequent batch of ore particles.
Claim 73
Dependent Claim
30 words
A method as defined in claim 58 wherein the metal values are recovered by solvent extraction to form a raffinate and wherein the second leach solution comprises solvent extraction raffinate.
Claim 74
Dependent Claim
102 words
A method as recited in claim 14 wherein during a first period of time the solution applied to the top of the layer comprises a second stage effluent, and the solution withdrawn from the bottom of the layer comprises a first stage effluent; and during a second period of time the solution applied to the top of the layer comprises a solvent extraction raffinate and the solution withdrawn from the bottom of the layer comprises a second stage effluent; and further comprising the step of extracting metal values from the first stage effluent by solvent extraction and producing a solvent extraction raffinate.
Claim 75
Dependent Claim
96 words
A method as recited in claim 1 wherein during a first period of time the leach liquid percolated through the layer comprises a second stage effluent and liquid withdrawn from the bottom of the layer comprises a first stage effluent; and during a second period of time the leach liquid percolated through the layer comprises a solvent extraction raffinate and liquid withdrawn from the bottom of the layer comprises a second stage effluent; and further comprising the stop of extracting metal values from the first stage effluent by solvent extraction and producing a solvent extraction raffinate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-11 | 1980-10-11 | 1981-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-11 | 1984-10-11 | 1985-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-11 | 1988-10-11 | 1989-04-12 | $7700.00 | Window Closed / Lapsed |