Opal glasses prepared through clay vitrification
Assignee: Corning Glass Works
•
Filing: 1976-08-09
•
Granted: 1977-04-12
•
Expires: 1996-08-09
Abstract
Abstract The instant invention is directed to the production of opal glasses through the solid state vitrification of certain bentonite-type clays. The process involves five general steps: (1) the clay is ion exchanged at low temperatures in aqueous solutions; (2) the ion exchanged clay is thoroughly washed with water; (3) the ion exchanged clay is preferably heated at moderate temperatures to expedite removal of the water; (4) the dehydrated clay is shaped into a body of a desired configuration; and (5) the shaped body is fired to vitrification utilizing a defined sintering schedule. The resulting body is a white or off-white opal glass containing minor amounts of crystal phases. Uniformly colored glasses can be prepared employing such conventional glass coloring agents as chromium, cobalt, copper, nickel, vanadium, etc. The process possesses the practical advantages of inexpensive batch materials, the elimination of the need for glass melting facilities, and low energy consumption in forming glass articles.
Inventors
- 👤 Syed N. Hoda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:16
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/005; C03C1/00; C03C1/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
204 words
A method for making an opal glass comprising the steps of: A. a bentonite clay exhibiting a DTA curve free from a sharp rise in slope at about 900° C., having a cation exchange capacity of about 100-200 milliequivalents/100 grams, and consisting essentially, in weight percent on the oxide basis, of about 57-78.5% SiO 2 , 13.8-23% A1 2 O 3 , 0-4% MgO, 0-5% Fe 2 O 3 , 0-2.5% CaO, 0-5.4% Na 2 O, and 0-0.5% K 2 O, is treated with an aqueous solution of a sodium and/or potassium salt to exchange sodium and/or potassium ions with other cations present in said clay to obtain a mono-cationic derivative having a composition within the Na 2 O/K 2 O-A1 2 O 3 -SiO 2 system; B. the ion exchanged clay is washed with water; C. the washed clay is dried; D. the dried clay is shaped into a desired form; and E. the clay shape is fired to vitrification in accordance with the schedule: a. the clay shape is dried; b. the clay shape is dehydroxylized and carbonaceous material is burned out by heating to about 700°-900° C.; and then c. the clay shape is vitrified by heating to about 950°-1200° C.
Claim 2
Independent Claim
204 words
A method for making an opal glass comprising the steps of: A. a bentonite clay exhibiting a DTA curve free from a sharp rise in slope at about 900° C., having a cation exchange capacity of about 100-200 milliequivalents/100 grams, and consisting essentially, in weight percent on the oxide basis, of about 57-78.5% SiO 2 , 13.8-23% A1 2 O 3 , 0-4% MgO, 0-5% Fe 2 O 3 , 0-2.5% CaO, 0-5.4% Na 2 O, and 0-0.5% K 2 O, is treated with an aqueous solution of a sodium and/or potassium salt to exchange sodium and/or potassium ions with other cations present in said clay to obtain a mono-cationic derivative having a composition within the Na 2 O/K 2 O-A1 2 O 3 -SiO 2 system; B. the ion exchanged clay is washed with water; C. the washed clay is dried; D. the dried clay is shaped into a desired form; and E. the clay shape is fired to vitrification in accordance with the schedule: a. the clay shape is dried; b. the clay shape is dehydroxylized and carbonaceous material is burned out by heating to about 700°-900° C.; and then c. the clay shape is vitrified by heating to about 950°-1200° C.
Claim 3
Dependent Claim
21 words
A method according to claim 1 wherein said ion exchange is conducted in 0.1N-10N aqueous solutions of sodium and/or potassium salts.
Claim 4
Dependent Claim
16 words
A method according to claim 2 wherein said sodium and/or potassium salts are NaCl and/or KC1.
Claim 5
Dependent Claim
25 words
A method according to claim 1 wherein said ion exchange is conducted at temperatures between the freezing point and boiling point of the aqueous solution.
Claim 6
Dependent Claim
15 words
A method according to claim 4 wherein said ion exchange is conducted at room temperature.
Claim 7
Dependent Claim
37 words
A method according to claim 1 wherein said clay contains carbonate impurities such that it is treated in a dilute acid solution, washed with water, and, optionally, dried prior to being subjected to the ion exchange reaction.
Claim 8
Dependent Claim
19 words
A method according to claim 1 wherein said washed clay is dried at a temperature between about 100°-200° C.
Claim 9
Dependent Claim
21 words
A method according to claim 1 wherein said clay shape is dried by heating at a temperature between about 100°-200° C.
Claim 10
Dependent Claim
24 words
A method according to claim 1 wherein said clay shape is dehydroxylized and carbonaceous material is burned out by heating for about 2-8 hours.
References Cited (Backward Citations)
US2000338A
Cited
US2266646A
Cited
US2880099A
Cited
US2973278A
Cited
US3012050A
Cited
US3764283A
Cited
US3553063A
Cited
US3674521A
Cited
US3753743A
Cited
US3779982A
Cited
US3850602A
Cited
US3834981A
Cited
US3963506A
Cited
US3844812A
Cited
US3967943A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-11 | 1980-10-11 | 1981-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-11 | 1984-10-11 | 1985-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-11 | 1988-10-11 | 1989-04-12 | $7700.00 | Window Closed / Lapsed |