US4016244A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for production of cubic boron nitride
Assignee: Hitachi Ltd
•
Filing: 1975-01-23
•
Granted: 1977-04-05
•
Expires: 1995-01-23
Abstract
Abstract In synthesizing cubic boron nitride from hexagonal boron nitride under high temperature and high pressure conditions, if water is incorporated into the raw material in an amount of at least 3% by weight, cubic boron nitride of a higher purity in the form of smaller crystallites than in conventional products can be obtained under lower temperature and lower pressure conditions than in conventional methods. When graphitic hexagonal boron nitride is used as the raw material, the temperature and pressure necessary for synthesis can be reduced to about 600 DEG C. and 50 Kbar, respectively.
Inventors
- 👤 Kenzo Susa
- 👤 Toshio Kobayashi
- 👤 Satoshi Taniguchi
- 👤 Mitsuru Ishii
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 00:07
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/064; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/583; C04B35/5831; C01P; C01P2004/00; C01P2004/60; C01P2004/61
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
86 words
In the process for synthesizing cubic boron nitride by using graphitic hexagonal boron nitride as the raw material and applying to said raw material such high temperature and high pressure that cubic boron nitride is thermodynamically stable, and improvement wherein water is incorporated in the raw material in an amount of at least 3% by weight, the high pressure is applied for at least 2 minutes, the applied temperature is at least about 600° C. and the applied high pressure is at least about 50 Kbar.
Claim 2
Dependent Claim
86 words
In the process for synthesizing cubic boron nitride by using graphitic hexagonal boron nitride as the raw material and applying to said raw material such high temperature and high pressure that cubic boron nitride is thermodynamically stable, and improvement wherein water is incorporated in the raw material in an amount of at least 3% by weight, the high pressure is applied for at least 2 minutes, the applied temperature is at least about 600° C. and the applied high pressure is at least about 50 Kbar.
Claim 3
Dependent Claim
27 words
The process for the production of cubic boron nitride according to claim 1, wherein and the applied high temperature is about 600° C. to about 800° C.
Claim 4
Dependent Claim
33 words
The process for the production of cubic boron nitride according to claim 1, wherein an aqueous solution of NH 4 OH is used as the water source and incorporated into the raw material.
Claim 5
Dependent Claim
25 words
The process for the production of cubic boron nitride according to claim 3, wherein the applied high temperature is about 600° to about 800° C.
Claim 6
Dependent Claim
28 words
The process for the production of cubic boron nitride according to claim 1, wherein water is incorporated in an amount of at least about 10% 20% by weight.
Claim 7
Dependent Claim
28 words
The process for the production of cubic boron nitride according to claim 1, wherein the high temperature and high pressure are applied for at least about 2 minutes.
Claim 8
Dependent Claim
50 words
The process for the production of cubic boron nitride according to claim 1, wherein the high temperature and high pressure employed are within the thermodynamically stable region of cubic boron nitride, a part of which is shown in FIG. 1 to the left of curve 4 of the accompanying drawings.
Claim 9
Dependent Claim
27 words
The process for the production of cubic boron nitride according to claim 1, wherein the applied high temperature is between about 600° C to about 1900° C.
Claim 10
Dependent Claim
27 words
The process for the production of cubic boron nitride according to claim 8, wherein the applied high pressure is between about 50 Kbar to about 65 Kbar.
Claim 11
Dependent Claim
34 words
The process for the production of cubic boron nitride according to claim 1, wherein the amount of water incorporated in the raw material is between about 3% by weight to about 67% by weight.
Claim 12
Dependent Claim
33 words
The process for the production of cubic boron nitride according to claim 1, wherein the high temperature and high pressure are applied for a period between about 2 minutes and about 24 hours.
Claim 13
Dependent Claim
28 words
The process for the production of cubic boron nitride according to claim 11, wherein the high temperature and high pressure are applied for at least about 30 minutes.
Claim 14
Dependent Claim
28 words
The process for the production of cubic boron nitride according to claim 1, wherein the cubic boron nitride produced has a crystal size of not more than .01μ.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |