Chemical strengthening of glass

Claim 2

In a method for strengthening an alkali metal silicate glass article in which sodium ions in the surface of the glass article are replaced by larger monovalent alkali metal ions by bringing the surface of the glass article into contact with the source of said larger monovalent alkali metal ions so as to place a compression layer in the surface of the glass article, the improvement which comprises forming the article to be strengthened from an alkali metal oxide-zirconia-aluminosilicate glass consisting essentially by weight on the oxide basis of about: ______________________________________ Component Percent by Weight ______________________________________ SiO.sub.2 [50-58] 52-57 Na.sub.2 O [8-23] 10-19 K.sub.2 O [0-15] 0-10 Na.sub.2 O + K.sub.2 O [13-25] 17-23 Al.sub.2 O.sub.3 [7-17] 9-13 ZrO.sub.2 [1-4.5] 2-4.5 Al.sub.2 O.sub.3 + ZrO.sub.2 [10-21] 12-17 [CaO] [0-10] MgO [0-6.5] 4-6 [CaO + MgO] [2.5-10] TiO.sub.2 [0-7] 1-6 [TiO.sub.2 + (MgO + CaO)] [4-14] ______________________________________ wherein the glass includes less than 0.1 percent by weight Li 2 O and the above components constitute at least 95 percent by weight of the glass composition and are proportioned relative to one another so as to provide glass having a viscosity of 100 poises at a temperature less than 2800° F. and a viscosity of 10,000 poises at a temperature less than 2050° F. and having a working range of at least 125° F.

Claim 3

A chemically strengthened glass article exhibiting a surface compressive stress after being subjected to surface abrasion composed of an interior portion which is in tension and a surface compressive layer, said interior portion comprising a base glass consisting essentially by weight on the oxide basis of about: ______________________________________ Component Percent by Weight ______________________________________ SiO.sub.2 [50-58] 52-57 Na.sub.2 O [8-23] 10-19 K.sub.2 O [0-15] 0-10 Na.sub.2 O + K.sub.2 O [13-25] 17-23 Al.sub.2 O.sub.3 [7-17] 9-13 ZrO.sub.2 [1-4.5] 2-4.5 Al.sub.2 O.sub.3 + ZrO.sub.2 [10-21] 12-17 [CaO] [0-10] MgO [0-6.5] 4-6 [CaO + MgO] [2.5-10] TiO.sub.2 [0-7] 1-6 [TiO.sub.2 + (MgO + CaO)] [4-14] ______________________________________ wherein the glass includes less than 0.1 percent by weight Li 2 O and the above components constitute at least 95 percent by weight of the base glass composition and are proportioned relative to one another so as to provide a base glass having a viscosity of 100 poises at a temperature less than 2800° F. and a viscosity of 10,000 poises at a temperature less than 2050° F., and having a working range of at least 125° F.; said surface layer having a composition chemically altered from that of the base glass to the extent that the surface layer has a lesser content of sodium with a correspondingly greater content on an ionic basis of a monovalent alkali metal ion having a larger ionic diameter than sodium.

Claim 4

A chemically strengthened glass article exhibiting a surface compressive stress after being subjected to surface abrasion composed of an interior portion which is in tension and a surface compressive layer, said interior portion comprising a base glass consisting essentially by weight on the oxide basis of about: ______________________________________ Component Percent by Weight ______________________________________ SiO.sub.2 [50-58] 52-57 Na.sub.2 O [8-23] 10-19 K.sub.2 O [0-15] 0-10 Na.sub.2 O + K.sub.2 O [13-25] 17-23 Al.sub.2 O.sub.3 [7-17] 9-13 ZrO.sub.2 [1-4.5] 2-4.5 Al.sub.2 O.sub.3 + ZrO.sub.2 [10-21] 12-17 [CaO] [0-10] MgO [0-6.5] 4-6 [CaO + MgO] [2.5-10] TiO.sub.2 [0-7] 1-6 [TiO.sub.2 + (MgO + CaO)] [4-14] ______________________________________ wherein the glass includes less than 0.1 percent by weight Li 2 O and the above components constitute at least 95 percent by weight of the base glass composition and are proportioned relative to one another so as to provide a base glass having a viscosity of 100 poises at a temperature less than 2800° F. and a viscosity of 10,000 poises at a temperature less than 2050° F., and having a working range of at least 125° F.; said surface layer having a composition chemically altered from that of the base glass to the extent that the surface layer has a lesser content of sodium with a correspondingly greater content on an ionic basis of a monovalent alkali metal ion having a larger ionic diameter than sodium.