US4014831A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Novel ionic polymer compositions
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1975-05-21
•
Granted: 1977-03-29
•
Expires: 1995-05-21
Abstract
Abstract The instant invention relates to a method for making processable ionic polymer compositions which are characterized as being processable at high temperatures, for example, 200 DEG C, while retaining adequate physical properties at both room temperatures and elevated temperatures which are below the processing temperature, for example, up to 100 DEG C and more. In this method, an ionic polymer comprising an elastomeric or plastic backbone and pendant acid groups is combined with a first neutralizing agent having two components. One component of said neutralizing agent is a metal or ammonium type moiety which combines with the pendant acid groups as a metal or ammonium salt thereof; the other component of neutralizing agent takes up the hydrogen ion present in the pendant acid groups and is converted into a preferential plasticizer for said ionomer. The preferential plasticizer acts to disrupt the ionic association of the metal or ammonium salt groups, thus allowing the ionic polymer to act as a noncrosslinked material. When the composition is in this state, it can be compounded with oils, fillers, etc. An ionic composition in this state is also characterized as having poor physical properties, for example, tensile strength, and excellent processing characteristics, e.g., low viscosity at elevated temperatures. This neutralized composition is then contacted with a second neutralizing agent which acts to substantially convert said preferential plasticizer to a higher melting species, for example, a salt. The composition, after the second neutralizing step, is then characterized as having the desired properties, for example, excellent physical properties at room temperature and up to 100 DEG C and more than adequate processability at temperatures of from 200 DEG C and above. Preferably, the ionic polymer is an ionic elastomer having from 0.2 to 25 mole % pendant acid groups, for example, carboxylic, phosphonic and sulfonic acid groups. Preferably, the pendant acid groups are sulfonic acid groups.
Inventors
- 👤 Jan Bock
- 👤 Neville G. Thame
- 👤 Lowell Westerman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:54
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/44
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
201 words
An improved process for forming a neutralized sulfonated polymer having a hydrocarbon backbone from an acid form of the sulfonated polymer having about 0.2 to about 25 mole percent SO 3 H groups, wherein the improvement comprises the following steps: a. adding a first neutralizing agent to said acid form of said sulfonated polymer to neutralize at least about 50% of said SO 3 H groups, said first neutralizing agent being selected from the group consisting essentially of Groups I-A, II-A, II-B, III-A, IV-A or ammonium derivatives of fatty acids, to form a mixture of a partially neutralized sulfonated polymer and said fatty acid formed from said derivative of said fatty acid; and b. adding a second neutralizing agent to form a metallic salt of said fatty acid, said metallic salt of said fatty acid having a higher melting point than said fatty acid and further neutralizing said SO 3 H groups of said partially neutralized sulfonated polymer to at least about 95%, said second neutralizing agent being selected from about consisting essentially of hydroxides, lower alkoxides, and lower alkonoates of Group I-A, II-A and II-B metals, at least 25% of the fatty acid being converted into the higher melting salt.
Claim 2
Dependent Claim
201 words
An improved process for forming a neutralized sulfonated polymer having a hydrocarbon backbone from an acid form of the sulfonated polymer having about 0.2 to about 25 mole percent SO 3 H groups, wherein the improvement comprises the following steps: a. adding a first neutralizing agent to said acid form of said sulfonated polymer to neutralize at least about 50% of said SO 3 H groups, said first neutralizing agent being selected from the group consisting essentially of Groups I-A, II-A, II-B, III-A, IV-A or ammonium derivatives of fatty acids, to form a mixture of a partially neutralized sulfonated polymer and said fatty acid formed from said derivative of said fatty acid; and b. adding a second neutralizing agent to form a metallic salt of said fatty acid, said metallic salt of said fatty acid having a higher melting point than said fatty acid and further neutralizing said SO 3 H groups of said partially neutralized sulfonated polymer to at least about 95%, said second neutralizing agent being selected from about consisting essentially of hydroxides, lower alkoxides, and lower alkonoates of Group I-A, II-A and II-B metals, at least 25% of the fatty acid being converted into the higher melting salt.
Claim 3
Dependent Claim
27 words
An improved process according to claim 1 wherein said hydrocarbon backbone is elastomeric being selected from the group consisting of butyl rubber, polybutadiene, or ethylene propylene terpolymers.
Claim 4
Dependent Claim
21 words
An improved process according to claim 1 wherein said neutralized sulfonated polymer contains a minor amount of carboxylic acid unsaturated monomers.
Claim 5
Dependent Claim
15 words
An improved process according to claim 1 wherein said hydrocarbon polymer comprises a plastic backbone.
Claim 6
Dependent Claim
23 words
An improved process according to claim 4 wherein said plastic backbone is selected from the group consisting essentially of polystyrene, polyethylene, or polypropylene.
Claim 7
Dependent Claim
18 words
An improved process according to claim 1 wherein said fatty acid has from 10 to 30 carbon atoms.
Claim 8
Dependent Claim
15 words
An improved process according to claim 1 wherein said second neutralizing agent is a hydroxide.
Claim 9
Dependent Claim
13 words
An improved process according to claim 7 wherein said hydroxide is magnesium hydroxide.
Claim 10
Dependent Claim
32 words
An improved process according to claim 1 wherein the first neutralizing agent is combined with said sulfonated polymer at a level of from 0.5 to 5 equivalents per equivalent of acid groups.
Claim 11
Dependent Claim
29 words
An improved process according to claim 9 wherein the second neutralizating agent is combined with said sulfonated polymer at from 0.25 to 3 equivalent per equivalent of acid groups.
Claim 12
Dependent Claim
15 words
An improved process according to claim 1 wherein said sulfonated polymer is a sulfonated polystyrene.
Claim 13
Dependent Claim
15 words
An improved process according to claim 1 wherein said sulfonated polymer is sulfonated ethylenepropylene terpolymer.
Claim 14
Dependent Claim
249 words
An improved process for forming a neutralized sulfonated polymer having a hydrocarbon backbone from an acid form of the sulfonated polymer having about 0.2 to about 25 mole percent SO 3 H groups, wherein the improvement comprises the following steps: a. adding a first neutralizing agent to said acid form of said sulfonated polymer to neutralize at least about 50% of said SO 3 H groups, said first neutralizing agent being selected from the group consisting essentially of Groups I-A, II-A, II-B, III-A, IV-A or ammonium derivatives of carboxylic acid having about 1 to about 3 carbon atoms, a metallic hydroxide of Group I-A, II-A and II-B metals, a lower alkanoate of Group I-A, II-A and II-B metals, to form a mixture of said partially neutralized sulfonated polymer and a chemical species being selected from the group consisting essentially of water, lower alcohols, carboxylic acids, or lower esters; b. adding a preferential plasticizer to said partially neutralized sulfonated polymer, said preferential plasticizer being a fatty acid; and c. adding a second neutralizing agent to form a metallic salt of said fatty acid, said metallic salt having a higher melting point than said fatty acid and further neutralizing said SO 3 H groups of said polymer to about at least 95%, said second neutralizing agent being selected from the group consisting essentially of hydroxides, lower alkoxides, and lower alkanoates of Group I-A, and II-A and II-B metals at least 25% of the fattyacid being converted into the higher melting salt.
Claim 15
Dependent Claim
249 words
An improved process for forming a neutralized sulfonated polymer having a hydrocarbon backbone from an acid form of the sulfonated polymer having about 0.2 to about 25 mole percent SO 3 H groups, wherein the improvement comprises the following steps: a. adding a first neutralizing agent to said acid form of said sulfonated polymer to neutralize at least about 50% of said SO 3 H groups, said first neutralizing agent being selected from the group consisting essentially of Groups I-A, II-A, II-B, III-A, IV-A or ammonium derivatives of carboxylic acid having about 1 to about 3 carbon atoms, a metallic hydroxide of Group I-A, II-A and II-B metals, a lower alkanoate of Group I-A, II-A and II-B metals, to form a mixture of said partially neutralized sulfonated polymer and a chemical species being selected from the group consisting essentially of water, lower alcohols, carboxylic acids, or lower esters; b. adding a preferential plasticizer to said partially neutralized sulfonated polymer, said preferential plasticizer being a fatty acid; and c. adding a second neutralizing agent to form a metallic salt of said fatty acid, said metallic salt having a higher melting point than said fatty acid and further neutralizing said SO 3 H groups of said polymer to about at least 95%, said second neutralizing agent being selected from the group consisting essentially of hydroxides, lower alkoxides, and lower alkanoates of Group I-A, and II-A and II-B metals at least 25% of the fattyacid being converted into the higher melting salt.
Claim 16
Dependent Claim
26 words
An improved process according to claim 13 wherein said hydrocarbon backbone is elastomeric being selected from the group consisting of butyl rubber, polybutadiene and ethylene-propylene terpolymers.
Claim 17
Dependent Claim
15 words
An improved process according to claim 13 wherein said hydrocarbon backbone comprises a plastic backbone.
Claim 18
Dependent Claim
21 words
An improved process according to claim 13 wherein said neutralized sulfonated polymer contains a minor amount of carboxylic acid unsaturated monomer.
Claim 19
Dependent Claim
22 words
An improved process according to claim 16 wherein said plastic backbone is selected from the group consisting of polystyrene, polyethylene and polypropylene.
Claim 20
Dependent Claim
18 words
An improved process according to claim 13 wherein said fatty acid has from 10 to 30 carbon atoms.
Claim 21
Dependent Claim
15 words
An improved process according to claim 13 wherein said second neutralization agent is a hydroxide.
Claim 22
Dependent Claim
15 words
An improved process according to claim 19 wherein said second neutralization agent is magnesium hydroxide.
Claim 23
Dependent Claim
32 words
An improved process according to claim 13 wherein the first neutralizing agent is combined with said sulfonated polymer at a level of from 0.5 to 5 equivalents per equivalent of acid groups.
Claim 24
Dependent Claim
29 words
An improved process according to claim 21 wherein said second neutralizing agent is combined with said sulfonated polymer at from 0.25 to 3 equivalent per equivalent of acid groups.
Claim 25
Dependent Claim
15 words
An improved process according to claim 13 wherein said sulfonated polymer is a sulfonated polystryene.
Claim 26
Dependent Claim
15 words
An improved process according to claim 13 wherein said sulfonated polymer is sulfonated ethylenepropylene terpolymer.
Claim 27
Dependent Claim
21 words
An improved process according to claim 13 wherein the anion of the second neutralization agent is volatilized off from said mixture.
References Cited (Backward Citations)
US3642728A
Cited
US3903039A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-28 | 1980-09-27 | 1981-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-28 | 1984-09-27 | 1985-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-28 | 1988-09-27 | 1989-03-29 | $7700.00 | Window Closed / Lapsed |