Method of producing a monolithic semiconductor device
Assignee: Siemens AG
•
Filing: 1975-08-01
•
Granted: 1977-03-29
•
Expires: 1995-08-01
Abstract
Abstract A combination insulating means comprised of a pn-junction overlaid with a SiO 2 filling within a groove is provided between IC elements in a monolithic semiconductor device. Such combination insulating means electrically and mechanically isolate at least two areas of a n-conductive surface zone, each of which supports an IC element. The n-conductive surface zone is supported on a p-conductive silicon base and the free surface of the n-conductive surface zone is coated with a Si 3 N 4 layer, which during the various fabrication steps of the monolithic semiconductor device protects coated areas of the n-conductive surface zone from etchants, oxidation and from dopants.
Inventors
- 👤 Helmuth Murrmann
- 👤 Ulrich Schwabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:33
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0158; H10P; H10P14/00; H10P14/60; H10P14/61; H10P95/00; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0121; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S148/00; Y10S148/106; Y10S148/114; Y10S148/117; Y10S438/00; Y10S438/942; Y10S438/944
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
193 words
A method of fabricating a monolithic silicon semiconductor device having a surface zone exhibiting a first conductivity from a silicon crystal doped differently from said surface zone, the steps comprising: applying a silicon nitride layer consisting of at least two separate areas onto a free face of said surface zone for use as an etching mask; etching a groove-like cavity between said silicon nitride layer areas; guiding a dopant ion beam substantially perpendicularly to a centralized base area of said cavity while using said silicon nitride layer areas as an implantation mask so that only such cavity base area becomes doped; oxidizing the resultant doped cavity base area while using said silicon nitride layer areas as an oxidation mask so that a silicon dioxide layer forms only in said groove-like cavity and completely separates said surface zone into at least two separate sections; and treating said separate surface zone sections with a second dopant ion beam having sufficient energy to penetrate said silicon nitride layer areas and implant dopant within said separate surface zone sections so as to fabricate an element of a semiconductor device in each of said separate surface zone sections.
Claim 2
Independent Claim
193 words
A method of fabricating a monolithic silicon semiconductor device having a surface zone exhibiting a first conductivity from a silicon crystal doped differently from said surface zone, the steps comprising: applying a silicon nitride layer consisting of at least two separate areas onto a free face of said surface zone for use as an etching mask; etching a groove-like cavity between said silicon nitride layer areas; guiding a dopant ion beam substantially perpendicularly to a centralized base area of said cavity while using said silicon nitride layer areas as an implantation mask so that only such cavity base area becomes doped; oxidizing the resultant doped cavity base area while using said silicon nitride layer areas as an oxidation mask so that a silicon dioxide layer forms only in said groove-like cavity and completely separates said surface zone into at least two separate sections; and treating said separate surface zone sections with a second dopant ion beam having sufficient energy to penetrate said silicon nitride layer areas and implant dopant within said separate surface zone sections so as to fabricate an element of a semiconductor device in each of said separate surface zone sections.
Claim 3
Dependent Claim
146 words
A method as defined in claim 1 wherein said silicon crystal is of a given conductivity and said surface zone is comprised of at least two separate sections of a first conductivity opposite to the given conductivity, and including epitaxially applying a silicon layer onto said surface zone sections, said epitaxial silicon layer being of the same coductivity as said surface zone sections but having a lower dopant concentration therein relative to said surface zone sections; etching said groove-like cavity within said epitaxial silicon layer so that such cavity extends only between said separate surface zone sections; and selecting a dopant ion beam for use prior to the oxidation step as well as after such oxidation step so that the doped cavity base area and the doped surface zone sections below both sections of said epitaxial silicon layer exhibits the given conductivity of said silicon crystal.
Claim 4
Dependent Claim
35 words
A method as defined in claim 2 wherein said selected dopant ion beam imparts a lower conductivity to said cavity base area and said surface area sections relative to the conductivity of said silicon crystal.
Claim 5
Dependent Claim
60 words
A method as defined in claim 3 wherein said silicon crystal is of the p-type conductivity, said cavity base area is of the p +-type conductivity, said surface zone sections are of the p-type conductivity, said epitaxial layer areas above said surface zone sections are of the n-type conductivity and said surface zone sections are of the n +-type conductivity.
Claim 6
Dependent Claim
42 words
A method as defined in claim 1 wherein said oxidizing step for forming a silicon dioxide layer in the groove-like cavity is conducted until the thickness of such dioxide layer substantially exceeds the thickness of the two separate silicon nitride layer areas.
Claim 7
Dependent Claim
53 words
A method as defined in claim 1 wherein the formation of said groove-like cavity between said silicon nitride layer areas involves forming such cavity so that the edges of such silicon nitride layer areas adjacent said cavity protrude over the transverse axial boundary of said cavity a distance of at least about 0.2μm.
Claim 8
Dependent Claim
26 words
A method as defined in claim 1 wherein said oxidation step is conducted at a temperature below 1100° C. and in the presence of water vapor.
Claim 9
Dependent Claim
21 words
A method as defined in claim 1 wherein said oxidation step is conducted at room temperature via an anodic oxidation process.
Claim 10
Dependent Claim
71 words
A method as defined in claim 1 wherein the silicon nitride layer areas only over said separate surface zone areas are removed after treatment of said zone areas by a dopant ion beam and after the oxidation step while the remaining silicon nitride layer areas are used as a diffusion mask while fabricating additional doped areas within the so-uncovered surface area zones so as to complete the semiconductor device being fabricated.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-28 | 1980-09-27 | 1981-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-28 | 1984-09-27 | 1985-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-28 | 1988-09-27 | 1989-03-29 | $7700.00 | Window Closed / Lapsed |