Flame spray powder for wear resistant alloy coating containing tungsten carbide
Assignee: Eutectic Corp
•
Filing: 1975-07-11
•
Granted: 1977-03-22
•
Expires: 1995-07-11
Abstract
Abstract A method and coating material are provided for improving the wear and abrasion resistance of a composite nickel-base hard facing alloy applied to metal substrates comprising the system Ni-Cr-Si-B having dispersed therein particles comprising tungsten carbide, the improvement residing in controlling the average particle size of tungsten carbide to below 10 microns, e.g. 0.1 to 10 microns, preferably an average size ranging from about 2 to 8 microns (such as 2 to 6 microns), at an average interparticle spacing of less than 15 microns, and preferably less than 10 microns, e.g. up to 5 microns, the hard facing coating produced being further characterized in that the coating exhibits metallographically a substantially uniform structure at the surface thereof with respect to said tungsten carbide particles.
Inventors
- 👤 Mahesh S. Patel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:08
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/32; B23K35/327; C; C23; C23C; C23C4/00; C23C4/04; C23C4/06; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
149 words
A composition of matter in the form of a powder mixture for use in the hard facing of metal substrates comprising a nickel-base alloy powder having substantially uniformly blended therewith a powder comprising agglomerates of nickel powder intimately combined with tungsten carbide powder, the amount of tungsten carbide in said agglomerates ranging from about 70% to 90% by weight, with the nickel powder in said agglomerates ranging from about 30% to 10% by weight, the ratio of said agglomerates to said nickel-base alloy powder in the powder mixture being such that the total mixture has an average tungsten carbide content ranging from about 10% to 30% by weight of said mixture, the composition of said nickel-base alloy powder in said mixture comprising by weight about 2.5% to 20% Cr, about 0.5% to 6% Si, about 0.5% to 5% B, up to about 10% Fe and the balance essentially nickel.
Claim 2
Dependent Claim
149 words
A composition of matter in the form of a powder mixture for use in the hard facing of metal substrates comprising a nickel-base alloy powder having substantially uniformly blended therewith a powder comprising agglomerates of nickel powder intimately combined with tungsten carbide powder, the amount of tungsten carbide in said agglomerates ranging from about 70% to 90% by weight, with the nickel powder in said agglomerates ranging from about 30% to 10% by weight, the ratio of said agglomerates to said nickel-base alloy powder in the powder mixture being such that the total mixture has an average tungsten carbide content ranging from about 10% to 30% by weight of said mixture, the composition of said nickel-base alloy powder in said mixture comprising by weight about 2.5% to 20% Cr, about 0.5% to 6% Si, about 0.5% to 5% B, up to about 10% Fe and the balance essentially nickel.
Claim 3
Dependent Claim
25 words
The composition of matter of claim 1, wherein the total powder mixture has an average tungsten carbide content of about 12% to 24% by weight.
Claim 4
Dependent Claim
42 words
The composition of matter of claim 1, wherein said nickel-base alloy powder in said mixture contains by weight about 10% to 20% Cr, about 2% to 6% Si, about 1.5% to 5% B, up to 10% Fe and the balance essentially nickel.
Claim 5
Dependent Claim
25 words
The composition of matter of claim 1, wherein the ratio of the agglomerate powder to said nickel-base alloy powder ranges from about 0.15 to 0.5.
Claim 6
Dependent Claim
171 words
A composition of matter in the form of a powder mixture for use in the hard facing of metal substrates comprising an atomized nickel-base alloy powder having substantially uniformly blended therewith a powder comprising agglomerates of nickel powder intimately combined with tungsten carbide powder, said agglomerates having a particle size less than about 150 mesh and having a tungsten carbide content of from about 70% to 90% by weight, with the nickel powder in said agglomerates ranging from about 30% to 10% by weight, said atomized nickel-base alloy powder having a particle size less than 100 mesh, the ratio of said agglomerates to said nickel-base alloy powder in said powder mixture being such that the total mixture has an average tungsten carbide content ranging from about 10% to 30% weight of said mixture, the composition of said nickel-base alloy powder in said mixture comprising by weight about 2.5% to 20% Cr, about 0.5% to 6% Si, about 0.5% to 5% B, up to about 10% Fe and the balance essentially nickel.
Claim 7
Dependent Claim
171 words
A composition of matter in the form of a powder mixture for use in the hard facing of metal substrates comprising an atomized nickel-base alloy powder having substantially uniformly blended therewith a powder comprising agglomerates of nickel powder intimately combined with tungsten carbide powder, said agglomerates having a particle size less than about 150 mesh and having a tungsten carbide content of from about 70% to 90% by weight, with the nickel powder in said agglomerates ranging from about 30% to 10% by weight, said atomized nickel-base alloy powder having a particle size less than 100 mesh, the ratio of said agglomerates to said nickel-base alloy powder in said powder mixture being such that the total mixture has an average tungsten carbide content ranging from about 10% to 30% weight of said mixture, the composition of said nickel-base alloy powder in said mixture comprising by weight about 2.5% to 20% Cr, about 0.5% to 6% Si, about 0.5% to 5% B, up to about 10% Fe and the balance essentially nickel.
Claim 8
Dependent Claim
41 words
The composition of matter of claim 5, wherein the nickel powder in said agglomerates has an average particle size ranging from about 0.1 to 10 microns and said tungsten carbide powder in said agglomerates ranges from about 0.1 to 10 microns.
Claim 9
Dependent Claim
31 words
The composition of matter of claim 6, wherein the average particle size of each of the nickel and the tungsten carbide in said agglomerates ranges from about 2 to 8 microns.
Claim 10
Dependent Claim
28 words
The composition of matter of claim 6, wherein the total powder mixture has an average tungsten carbide content of about 12% to 24% by weight of said mixture.
Claim 11
Dependent Claim
44 words
The composition of matter of claim 6, wherein said atomized nickel-base alloy powder in said mixture contains by weight about 10% to 20% Cr, about 2% to 6% Si, about 1.5% to 5% B, up to about 10% Fe and the balance essentially nickel.
Claim 12
Dependent Claim
24 words
The composition of matter of claim 6, wherein the ratio of the agglomerate powder to said nickel-base alloy ranges from about 0.15 to 0.5.
Claim 13
Dependent Claim
19 words
The composition of matter of claim 6, wherein the agglomerate powder has a size of less than 270 mesh.
Claim 14
Dependent Claim
19 words
The composition of matter of claim 5, wherein at least 30% of the atomized powder passes through 325 mesh.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-21 | 1980-09-20 | 1981-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-21 | 1984-09-20 | 1985-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-21 | 1988-09-20 | 1989-03-22 | $7700.00 | Window Closed / Lapsed |