Claim 1

Independent Claim 283 words

A process to decrease the cold flow of a conjugated diene polymer wherein said conjugated diene polymer is a homopolymer or copolymer of a conjugated diene or of a conjugated diene with a monomer containing a vinylidene group, which process comprises contacting said conjugated diene polymer with a homogeneous olefin disproportionation catalyst, wherein said catalyst is an admixture of (a) an NO-containing transition metal complex represented by the formula [L a (NO) b M c Z d ] x and (b) an aluminum-containing component, wherein in said (a) L is a ligand; M is a transition metal selected from Group VIB, VIIB, and the iron and cobalt subgroups of Group VIII; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6; b is 1 or 2; c is 1 to 4; and x is a number indicative of the polymeric state of the complex; and wherein said (b) aluminum-containing component is (1) represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical, including radicals substituted with halo groups or alkoxy groups, and having up to about 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1 and the sum of n and m is 3; or (3) a compound represented by the formula R n AlX m wherein R, X, n and m are as defined herein, and wherein the ratio of (b):(a) and the conditions of said contacting including temperature, pressure, and time, are effective to decrease said cold flow of said conjugated diene polymer.

Claim 2

Dependent Claim 283 words

A process to decrease the cold flow of a conjugated diene polymer wherein said conjugated diene polymer is a homopolymer or copolymer of a conjugated diene or of a conjugated diene with a monomer containing a vinylidene group, which process comprises contacting said conjugated diene polymer with a homogeneous olefin disproportionation catalyst, wherein said catalyst is an admixture of (a) an NO-containing transition metal complex represented by the formula [L a (NO) b M c Z d ] x and (b) an aluminum-containing component, wherein in said (a) L is a ligand; M is a transition metal selected from Group VIB, VIIB, and the iron and cobalt subgroups of Group VIII; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6; b is 1 or 2; c is 1 to 4; and x is a number indicative of the polymeric state of the complex; and wherein said (b) aluminum-containing component is (1) represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical, including radicals substituted with halo groups or alkoxy groups, and having up to about 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1 and the sum of n and m is 3; or (3) a compound represented by the formula R n AlX m wherein R, X, n and m are as defined herein, and wherein the ratio of (b):(a) and the conditions of said contacting including temperature, pressure, and time, are effective to decrease said cold flow of said conjugated diene polymer.

Claim 3

Dependent Claim 224 words

The process of treating a conjugated diene polymer to decrease the cold flow thereof which process comprises contacting said polymer with a homogeneous olefin disproportionation catalyst under treating conditions wherein said homogeneous olefin disproportionation catalyst is (a) an NO-containing-transition metal complex and (b) an aluminum-containing component, wherein said (a) is represented by [L a (NO) b M c Z d ] wherein L is a ligand; M is a transition metal of Group IB, IIIB, IVB, VB, VIB, VIIB, or the iron-cobalt subgroups of Group VIII; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6 inclusive; b is 1 or 2; c is a number 1 to 4 inclusive; said (b) is (1) represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical having up to 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1, such that the sum of n + m is 3; or (3) a compound represented by the formula R n AlX m ; and wherein the ratio of said (b)-(a) and said treating conditions including time and temperature are effective to decrease the cold flow of said conjugated diene polymer.

Claim 4

Dependent Claim 224 words

The process of treating a conjugated diene polymer to decrease the cold flow thereof which process comprises contacting said polymer with a homogeneous olefin disproportionation catalyst under treating conditions wherein said homogeneous olefin disproportionation catalyst is (a) an NO-containing-transition metal complex and (b) an aluminum-containing component, wherein said (a) is represented by [L a (NO) b M c Z d ] wherein L is a ligand; M is a transition metal of Group IB, IIIB, IVB, VB, VIB, VIIB, or the iron-cobalt subgroups of Group VIII; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6 inclusive; b is 1 or 2; c is a number 1 to 4 inclusive; said (b) is (1) represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical having up to 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1, such that the sum of n + m is 3; or (3) a compound represented by the formula R n AlX m ; and wherein the ratio of said (b)-(a) and said treating conditions including time and temperature are effective to decrease the cold flow of said conjugated diene polymer.

Claim 5

Dependent Claim 237 words

A process for preparing a conjugated diene polymer which is a polymer of a conjugated diene or conjugated diene with a vinylidene group containing monomer, wherein the improvement comprises contacting a preformed conjugated diene polymer with a homogeneous olefin disproportionation catalyst, wherein said homogeneous olefin disproportionation catalyst is (a) an NO-containing-transition metal complex, and (b) an aluminum-containing component in a ratio of (b):(a) and under treating conditions in the substantial absence of monomer effective to decrease the cold flow of said preformed conjugated diene polymer, wherein said (a) is represented by [L a (NO) b M c Z d ] wherein L is a ligand; M is a transition metal of Group IB, IIIB, IVB, VB, VIB, VIIB, or the iron-cobalt subgroups of Group VIII; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6 inclusive; b is 1 or 2; and c is a number 1 to 4 inclusive; and said (b) is (1)represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical having up to 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1, such that the sum of n + n is 3; or (3) a compound represented by the formula R n AlX m .

Claim 6

Dependent Claim 237 words

A process for preparing a conjugated diene polymer which is a polymer of a conjugated diene or conjugated diene with a vinylidene group containing monomer, wherein the improvement comprises contacting a preformed conjugated diene polymer with a homogeneous olefin disproportionation catalyst, wherein said homogeneous olefin disproportionation catalyst is (a) an NO-containing-transition metal complex, and (b) an aluminum-containing component in a ratio of (b):(a) and under treating conditions in the substantial absence of monomer effective to decrease the cold flow of said preformed conjugated diene polymer, wherein said (a) is represented by [L a (NO) b M c Z d ] wherein L is a ligand; M is a transition metal of Group IB, IIIB, IVB, VB, VIB, VIIB, or the iron-cobalt subgroups of Group VIII; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6 inclusive; b is 1 or 2; and c is a number 1 to 4 inclusive; and said (b) is (1)represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical having up to 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1, such that the sum of n + n is 3; or (3) a compound represented by the formula R n AlX m .

Claim 7

Dependent Claim 222 words

A process for preparing a conjugated diene polymer which is a polymer of a conjugated diene or conjugated diene with a vinylidene group-containing monomer, wherein the improvement comprises contacting a preformed conjugated diene polymer with a homogeneous olefin disproportionation catalyst, wherein said homogeneous olefin disproportionation catalyst is (a) an NO-containing-transition metal complex and (b) an aluminum-containing component in a ratio of (b):(a) and under treating conditions in the substantial absence of monomer effective to decrease the cold flow of said preformed polymer, wherein said (a) is represented by [L a (NO) b M c Z d ] wherein L is a ligand; M is molybdenum, tungsten, rhenium, ruthenium or rhodium; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6 inclusive; b is 1 or 2; c is a number 1 to 4 inclusive; and said (b) is (1) represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical having up to 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1, such that the sum of n + m is 3; or (3) a compound represented by the formula R n AlX m .

Claim 8

Dependent Claim 222 words

A process for preparing a conjugated diene polymer which is a polymer of a conjugated diene or conjugated diene with a vinylidene group-containing monomer, wherein the improvement comprises contacting a preformed conjugated diene polymer with a homogeneous olefin disproportionation catalyst, wherein said homogeneous olefin disproportionation catalyst is (a) an NO-containing-transition metal complex and (b) an aluminum-containing component in a ratio of (b):(a) and under treating conditions in the substantial absence of monomer effective to decrease the cold flow of said preformed polymer, wherein said (a) is represented by [L a (NO) b M c Z d ] wherein L is a ligand; M is molybdenum, tungsten, rhenium, ruthenium or rhodium; Z is a halide, CN, SCN, OCN, or SnCl 3 ; a and d are numbers 0 to 6 inclusive; b is 1 or 2; c is a number 1 to 4 inclusive; and said (b) is (1) represented by the formula RAlX 2 ; (2) a mixture of (1) and a compound represented by the formula R n AlX m wherein R is an aromatic or saturated aliphatic radical having up to 20 carbon atoms, X is halogen, n is 2 or 3, m is 0 or 1, such that the sum of n + m is 3; or (3) a compound represented by the formula R n AlX m .

Claim 9

Dependent Claim 46 words

The process of claim 1 wherein said L ligand is represented by the formula R 5 (COO) k wherein R 5 is a saturated aliphatic or ethylenically unsaturated aliphatic radical having up to 30 carbon atoms, and wherein the (b) component of the catalyst is (2).

Claim 10

Dependent Claim 15 words

The process of claim 5 wherein said M is molybdenum, tungsten, rhenium, ruthenium, or rhodium.

Claim 11

Dependent Claim 45 words

The process of claim 5 wherein said conjugated diene polymer is a polymer of butadiene, isoprene, or a copolymer of butadiene and styrene, and wherein the ratio of said (b) complex to said (a) component is in the range of about 0.1:1 to about 20:1.

Claim 12

Dependent Claim 174 words

The process according to claim 2 wherein said L is R 3 Q, R 3 QO, R 2 Q--QR 2 ,R 2 NR', O, CO, R 2 N--R 2 --NR 2 , R--S--R, R 3 S, [π-(CHR 4 --CR 4 --CH 2 )], R 5 (CN) k , R 5 (COO) k , RCOR 6 (COO) k , [(RCO) 2 CH], (R 2 NCSS) unsubstituted and R 5 group-substituted pyridine, unsubstituted and R 5 group-substituted bipyridine, or unsubstituted and R group-substituted cyclopentadienyl radicals, wherein R is an aromatic saturated aliphatic radical, R' is hydrogen or an R radical, R 2 is a divalent R radical, R 3 is a divalent saturated aliphatic or ethylenically unsaturated aliphatic radical having 4 to 10 carbon atoms, R 4 is hydrogen or methyl radical, R 5 is an aromatic, saturated aliphatic, or ethylenically unsaturated aliphatic radical having up to 30 carbon atoms, R 6 is a divalent saturated aliphatic radical having 1 to 10 carbon atoms, Q is phosphorus, arsenic, or antimony, and k is 1 or 2.

Claim 13

Dependent Claim 16 words

The process according to claim 8 wherein said M is molybdenum tungsten, rhenium, ruthenium, or rhodium.

Claim 14

Dependent Claim 162 words

The process according to claim 8 wherein said (a) is (triphenylphosphine) 2 (NO) 2 MoCl 2 , (NO) 2 MoCl 2 , (pyridine) 2 (NO) 2 MoCl 2 , NO-treated (triphenylphosphine) 2 MoCl 4 , NO-treated (pyridine) 2 MoCl 4 , NO-treated (butyronitrile) 2 MoCl 4 , NO-treated (stearate) 2 MoCl 3 , NO-treated pyridine-treated MoCl 5 , NO-treated (benzoate) 2 MoCl 3 , NO-treated (acetylacetonate) 2 MoO 2 , NO-treated MoOCl 3 , NO-treated tetrallyltin-treated MoCl 5 , NO-treated MoCl 5 , NOCl-treated pyridine-treated MoO 2 , NO-treated tributylphosphine-treated MoCl 5 , NO-treated thiophene-treated MoCl 5 , NO-treated pyridine-treated WCl 6 , NO-treated benzoic acid-treated WCl 6 , (triphenylphosphine) 2 (NO) 2 WCl 2 , NO-treated RuCl 3 , NO-treated triphenylphosphine-treated RuCl 3 , NOCl-treated (triphenylphosphine) 3 RhCl, NO-treated (triphenylphosphine) 3 RhCl, NO-treated triphenylphosphine-treated RhCl 3 , NO-treated benzoic acid-treated NbCl 5 , NO-treated (triphenylphosphine) 2 CoCl 2 , NO-treated triphenylphosphine-treated IrCl 3 , or NO-treated CO-treated triphenylphosphine-treated IrCl 3 .

Claim 15

Dependent Claim 34 words

The process according to claim 8 wherein said (b) is methylaluminum dichloride, ethylaluminum dichloride, n-butylaluminum dichloride, n-heptylaluminum dibromide, cyclohexylaluminum dibromide, 4-methylcyclohexylaluminum difluoride, n-eicosylaluminum difluoride, isopropylaluminum diiodide, benzylaluminum dichloride, 2,4,6-trimethylphenylaluminum dichloride, n-decylaluminum dichloride, or 2-naphthylaluminum.

Claim 16

Dependent Claim 44 words

The process according to claim 8 wherein said (b) is trimethylaluminum, triethylaluminum, tri-n-propylaluminum, triisobutylaluminum, tri-n-hexylaluminum, tri-n-octylaluminum, tricyclohexylaluminum, triphenylaluminum, tri-n-decylaluminum, tri-n-eicosylaluminum, methyldiphenylaluminum, tribenzylaluminum, tri-l-naphtylaluminum, di-n-octylphenylaluminum, tri-4-tolylaluminum, dimethylaluminum chloride, di-n-propylaluminum bromide, diethylaluminum chloride, diisobutylaluminum chloride, methylisobutylaluminum chloride, di-n-heptylaluminum fluoride, dipheylaluminum bromide, dibenzylaluminum chloride, or di-n-octylaluminum iodide.

Claim 17

Dependent Claim 27 words

The process according to claim 8 wherein said homogeneous disproportionation catalyst employs a molar ratio of said (b):(a) is in the range of about 0.1:1 to 20:1.

Claim 18

Dependent Claim 22 words

The process according to claim 9 wherein said molar ratio of said (b):(a) is in the range of about 1:1 to 10:1.

Claim 19

Dependent Claim 83 words

The process according to claim 8 wherein said (a) [L a (NO) b M c Z d ] represents a product obtained by combining at least one salt of a transition metal with at least one ligand-forming material under conditions of time and temperature which permit the complex represented by [L a (NO) b M c Z d ] to form, employing a molar proportion of said transition metal salt to said ligand forming material in the range of about 0.1:1 to 10:1.

Claim 20

Dependent Claim 43 words

The process according to claim 15 wherein said molar proportion of said transition metal salt to said ligand forming material is in the range of about 0.2:1 to 2:1, and said combining temperature is in the range of about 0° to 130° C.

Claim 21

Dependent Claim 37 words

The process according to claim 13 wherein said polymer is a polybutadiene, said (a) is molybdenum trichloride di-octanoate treated with nitric oxide, said (b) is ethylaluminum sesquichloride, and said ratio of (b):(a) is about 1:2 to 20:1.

Claim 22

Dependent Claim 48 words

The process according to claim 13 wherein said contacting is conducted at a temperature in the range of about 50° to 250° F., for a time in the range of about 1 minute to 100 hours, employing treating conditions wherein said polymer is dissolved in a hydrocarbon diluent.

Claim 23

Dependent Claim 27 words

The process according to claim 13 wherein said conjugated diene polymer is a conjugated diene homopolymer, or copolymer of a conjugated diene with a vinylidine group-containing monomer.

Claim 24

Dependent Claim 28 words

The process according to calim 13 wherein said polymer is said copolymer wherein said vinylidine group-containing comonomer is styrene, vinyl-naphthalene, vinylpyridine, acrylonitrile, methacrylonitrile, methyl acrylate, or methyl methacrylate.

Claim 25

Dependent Claim 28 words

The process according to calim 13 wherein said polymer is said copolymer wherein said vinylidine group-containing comonomer is styrene, vinyl-naphthalene, vinylpyridine, acrylonitrile, methacrylonitrile, methyl acrylate, or methyl methacrylate.

Claim 26

Dependent Claim 44 words

The process according to claim 3 wherein said polymer is an unquenched polymer obtained by the polymerization of said conjugated diene or of said conjugated diene with said vinylidine group-containing monomer with a lithium based catalyst under solution polymerization conditions in a hydrocarbon diluent.

Claim 27

Dependent Claim 35 words

The process according to claim 13 wherein said polymer is an unquenched polymer obtained by the polymerization of a conjugated diene with a catalyst system comprising iodine, triisobutylaluminum, and titanium tetrachloride under solution polymerization conditions.

Claim 28

Dependent Claim 23 words

The process of claim 22 wherein said polymer is polybutadiene; said (a) is NO-treated molybdenum trichloride dioctanoate, and said (b) is ethylaluminum sesquichloride.

Claim 29

Dependent Claim 22 words

The process of claim 22 wherein said polymer is polybutadiene, said (a) is NO-treated molybdenum trichloride dioctanoate, and said (b) is triisobutylaluminum.

Claim 30

Dependent Claim 59 words

The process of treating a polybutadiene, which process comprises contacting said polybutadiene with a homogeneous olefin disproportionation catalyst under treating conditions, wherein said homogeneous olefin disproportionation catalyst is (a) nitric oxide-treated molybdenum trichloride distearate and (b) ethylaluminum sesquichloride wherein the ratio of gram atoms of Al:Mo is about 5:1 such that the inherent viscosity of said polybutadiene is increased.

Claim 31

Dependent Claim 59 words

The process of treating a polybutadiene, which process comprises contacting said polybutadiene with a homogeneous olefin disproportionation catalyst under treating conditions, wherein said homogeneous olefin disproportionation catalyst is (a) nitric oxide-treated molybdenum trichloride distearate and (b) ethylaluminum sesquichloride wherein the ratio of gram atoms of Al:Mo is about 5:1 such that the inherent viscosity of said polybutadiene is increased.

Claim 32

Dependent Claim 59 words

The process of treating a polyisoprene, which process comprises contacting said polyisoprene with a homogeneous olefin disproportionation catalyst under treating conditions, wherein said homogeneous olefin disproportionation catalyst is (a) NO-treated molybdenum dioctanoate trichloride and (b) is ethylaluminum sesquichloride wherein the ratio of gram atoms of Al:Mo is about 5:1 such that the inherent viscosity of said polyisoprene is increased.

Claim 33

Dependent Claim 59 words

The process of treating a polyisoprene, which process comprises contacting said polyisoprene with a homogeneous olefin disproportionation catalyst under treating conditions, wherein said homogeneous olefin disproportionation catalyst is (a) NO-treated molybdenum dioctanoate trichloride and (b) is ethylaluminum sesquichloride wherein the ratio of gram atoms of Al:Mo is about 5:1 such that the inherent viscosity of said polyisoprene is increased.

Claim 34

Dependent Claim 67 words

The process of treating a butadiene/styrene copolymer, which process comprises contacting said butadiene/styrene copolymer with a homogeneous olefin disproportionation catalyst under treating conditions, wherein said homogeneous olefin disproportionation catalyst is (a) molybdenum trichloride dioctanoate treated with nitric oxide and (b) ethylaluminum sesquichloride wherein the treating conditions include a ratio of gram atoms Al:Mo of about 5:1 such that the inherent viscosity of said butadiene/styrene copolymer is increased.

Claim 35

Dependent Claim 67 words

The process of treating a butadiene/styrene copolymer, which process comprises contacting said butadiene/styrene copolymer with a homogeneous olefin disproportionation catalyst under treating conditions, wherein said homogeneous olefin disproportionation catalyst is (a) molybdenum trichloride dioctanoate treated with nitric oxide and (b) ethylaluminum sesquichloride wherein the treating conditions include a ratio of gram atoms Al:Mo of about 5:1 such that the inherent viscosity of said butadiene/styrene copolymer is increased.

Claim 36

Dependent Claim 118 words

A polymerization process which comprises: polymerizing butadiene, isoprene, or a mixture of butadiene and styrene, in the presence of a hydrocarbon lithium catalyst under polymerization conditions thereby producing a conjugated diene polymer; contacting the unquenched reaction mixture of the polymerization including the resulting conjugated diene polymer with an olefin disproportionation catalyst represented by (a) NO-treated [R(VOO)] 2 MoCl 3 wherein R is an aliphatic radical with up to 30 carbon atoms; and (b) R'AlX 2 , or a mixture of at least 50 mol percent R'AlX 2 and R' 2 AlX, wherein R' is aryl or alkyl, X is halogen; wherein the ratio of component (b) to component (a) is in the range of about 0.1:1 to 20:1.

Claim 37

Dependent Claim 118 words

A polymerization process which comprises: polymerizing butadiene, isoprene, or a mixture of butadiene and styrene, in the presence of a hydrocarbon lithium catalyst under polymerization conditions thereby producing a conjugated diene polymer; contacting the unquenched reaction mixture of the polymerization including the resulting conjugated diene polymer with an olefin disproportionation catalyst represented by (a) NO-treated [R(VOO)] 2 MoCl 3 wherein R is an aliphatic radical with up to 30 carbon atoms; and (b) R'AlX 2 , or a mixture of at least 50 mol percent R'AlX 2 and R' 2 AlX, wherein R' is aryl or alkyl, X is halogen; wherein the ratio of component (b) to component (a) is in the range of about 0.1:1 to 20:1.

Claim 38

Dependent Claim 27 words

The process of claim 28 wherein the olefin disproportionation catalyst is a mixture of ethylaluminum sesquichloride and the reaction product of nitric oxide and molybdenum trichloride dioctanoate.

Claim 39

Dependent Claim 25 words

The process of claim 28 wherein the contact with the olefin disproportionation catalyst is at a temperature in the range of 50° to 250° F.

Claim 40

Dependent Claim 12 words

The process of claim 28 wherein the conjugated diene polymer is polybutadiene.

Claim 41

Dependent Claim 17 words

The process of claim 28 wherein said conjugated diene polymer is a copolymer of butadiene and styrene.

Claim 42

Dependent Claim 27 words

The process of claim 28 wherein said olefin disproportionation catalyst is a mixture of ethylaluminum sesquichloride and the reaction product of nitric acid and molybdenum trichloride distearate.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1980-03-14	1980-09-13	1981-03-15	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1984-03-14	1984-09-13	1985-03-15	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1988-03-14	1988-09-13	1989-03-15	$7700.00	Window Closed / Lapsed

Method for modifying the properties of rubbery polymers of conjugated dienes

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag