Porous carbonaceous electrode structure and method for secondary electrochemical cell
Assignee: Energy Research and Development Administration ERDA
•
Filing: 1975-12-02
•
Granted: 1977-03-08
•
Expires: 1995-12-02
Abstract
Abstract Positive and negative electrodes are provided as rigid, porous carbonaceous matrices with particulate active material fixedly embedded. Active material such as metal chalcogenides, solid alloys of alkali metal or alkaline earth metals along with other metals and their oxides in particulate form are blended with a thermosetting resin and a solid volatile to form a paste mixture. Various electrically conductive powders or current collector structures can be blended or embedded into the paste mixture which can be molded to the desired electrode shape. The molded paste is heated to a temperature at which the volatile transforms into vapor to impart porosity as the resin begins to cure into a rigid solid structure.
Inventors
- 👤 Thomas D. Kaun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:00
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/399; H01M4/00; H01M4/02; H01M4/62; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
67 words
An improved electrode for use in a high-temperature, secondary electrochemical cell including a molten salt electrolyte, said electrode comprises a solid, porous matrix of thermosetting, carbonaceous material of about 50-65% porosity having solid particles of metal sulfide selected from the group consisting of sulfides of iron, cobalt, nickel and copper, fixedly embedded therein in a generally uniform distribution and exposed to interstitial volume within said porous matrix.
Claim 2
Dependent Claim
67 words
An improved electrode for use in a high-temperature, secondary electrochemical cell including a molten salt electrolyte, said electrode comprises a solid, porous matrix of thermosetting, carbonaceous material of about 50-65% porosity having solid particles of metal sulfide selected from the group consisting of sulfides of iron, cobalt, nickel and copper, fixedly embedded therein in a generally uniform distribution and exposed to interstitial volume within said porous matrix.
Claim 3
Dependent Claim
18 words
The electrode of claim 1 wherein said matrix includes a continuous, electrically conductive lattice comprising a metal carbide.
Claim 4
Dependent Claim
28 words
The electrode of claim 2 wherein said metal carbide is selected from the group consisting of Mn 5 C 2 , NbC and Cr 3 C 2 .
Claim 5
Dependent Claim
68 words
A paste composition for forming an electrode for use in a high-temperature, secondary electrochemical cell, said paste composition comprising a thermosetting material in liquid form, particulate active material and solid volatile in a generally uniform mixture, said particulate active material being selected from the group consisting of sulfides of iron, cobalt, nickel and copper and said solid volatile being about 50-65% of the total volume of paste constituents.
Claim 6
Dependent Claim
68 words
A paste composition for forming an electrode for use in a high-temperature, secondary electrochemical cell, said paste composition comprising a thermosetting material in liquid form, particulate active material and solid volatile in a generally uniform mixture, said particulate active material being selected from the group consisting of sulfides of iron, cobalt, nickel and copper and said solid volatile being about 50-65% of the total volume of paste constituents.
Claim 7
Dependent Claim
26 words
The paste composition of claim 4 wherein said thermosetting material is a resin selected from the group consisting of phenol formaldehyde, phenol benzaldehyde and furfuryl alcohol.
Claim 8
Dependent Claim
28 words
The paste composition of claim 4 wherein said solid volatile transforms to vapor at a temperature below that at which said thermosetting material cures to a rigid solid.
Claim 9
Dependent Claim
27 words
The paste composition of claim 4 wherein said paste includes particles of an electrically conductive filler selected from the group consisting of metal powders and carbon powder.
Claim 10
Dependent Claim
27 words
The paste composition of claim 4 wherein said volatile is a solid particulate material that is capable of transforming directly from solid to vapor at atmospheric pressure.
Claim 11
Dependent Claim
28 words
The paste composition of claim 4 wherein said volatile is selected from the group consisting of ammonium carbonate, ammonium bicarbonate, copper acetylacetone, hexachloroethane, potassium amide and ferrous chloride.
Claim 12
Dependent Claim
15 words
The paste composition of claim 4 wherein said volatile is ammonium carbonate or ammonium bicarbonate.
Claim 13
Independent Claim
101 words
A method of preparing an electrode including a particulate active material selected from the group consisting of sulfides of iron, cobalt, nickel and copper for use in a high-temperature, secondary electrochemical cell, said method comprising blending thermosetting carbonaceous material in liquid form with the particulate active material and solid volatile to form a generally uniform paste, said solid volatile being provided in sufficient amount to be about 50-65% of the total volume of paste constituents; and heating said paste to transform said volatile to vapor and to cure said thermosetting, carbonaceous material into a rigid, porous matrix containing said active material.
Claim 14
Independent Claim
101 words
A method of preparing an electrode including a particulate active material selected from the group consisting of sulfides of iron, cobalt, nickel and copper for use in a high-temperature, secondary electrochemical cell, said method comprising blending thermosetting carbonaceous material in liquid form with the particulate active material and solid volatile to form a generally uniform paste, said solid volatile being provided in sufficient amount to be about 50-65% of the total volume of paste constituents; and heating said paste to transform said volatile to vapor and to cure said thermosetting, carbonaceous material into a rigid, porous matrix containing said active material.
Claim 15
Dependent Claim
21 words
The method of claim 11 wherein said paste is molded into the shape of said electrode prior to said heating step.
Claim 16
Dependent Claim
43 words
The method of claim 11 wherein said paste is heated to a temperature of about 40° C. to 200° C. to cure said thermosetting material and transform said volatile whereby emission of vapors just before and during thermosetting produces porosity in said matrix.
Claim 17
Dependent Claim
35 words
The method of claim 11 wherein said porous matrix is heated to a temperature in excess of 900° C. to carburize and then to a temperature in excess of 2800° C. to graphitize said matrix.
Claim 18
Dependent Claim
45 words
The method of claim 11 wherein a particulate metal carbide and carbon are blended into said uniform paste and said matrix is heated to 400°-550° C. to react said metal carbide and carbon to form a continuous electrically conductive lattice within said rigid, porous matrix.
Claim 19
Dependent Claim
42 words
The method of claim 15 wherein said metal carbide is Nb 2 C, Mn 3 C or Cr 23 C 6 and reacts with carbon to form a continuous lattice of NbC, Mn 5 C 2 or Cr 3 C 2 respectively.
References Cited (Backward Citations)
US3219731A
Cited
US3395049A
Cited
US3380856A
Cited
US3442715A
Cited
US3410731A
Cited
US3573122A
Cited
US3634569A
Cited
US3629007A
Cited
US3753782A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-07 | 1980-09-06 | 1981-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-07 | 1984-09-06 | 1985-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-07 | 1988-09-06 | 1989-03-08 | $7700.00 | Window Closed / Lapsed |