US4009058A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of fabricating large area, high voltage PIN photodiode devices
Assignee: RCA Corp
•
Filing: 1976-01-26
•
Granted: 1977-02-22
•
Expires: 1996-01-26
Abstract
Abstract The body of a PIN photodiode is of a silicon semiconductor material. The PIN photodiode has a large area incident surface on which light impinges and is operated at high voltages. In the fabrication of a PIN photodiode, as described, a high concentration of N-type dopant is deposited on the body. It has been discovered that if a phosphorus silicate glass, as a source of N-type dopant, is in contact with a surface of the PIN photodiode body in a high temperature ambient and for an extended period of time, lattice damage on the surface of the silicon body results. These lattice defects are responsible for premature voltage breakdown in the device. In a first method of fabrication of PIN photodiode devices the phosphorus silicate glass is on the silicon surface for about 12 minutes after which it is removed and then any phosphorus atoms in the surface of the body are diffused into the body. In a second method of fabrication ion implantation is used to dope the body so that a surface of the body need not come in contact with phosphorus silicate glass.
Inventors
- 👤 Mark Philip Mills
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:49
CPC Classifications
H; H10; H10F; H10F30/00; H10F30/20; H10F30/21; H10F30/22; H10F30/223; H10P; H10P32/00; H10P32/10; H10P32/14; H10P32/1404; H10P32/1406; H10P32/17; H10P32/171; Y; Y10; Y10S; Y10S148/00; Y10S148/043; Y10S148/06; Y10S148/097; Y10S148/12; Y10S438/00; Y10S438/914; Y10S438/92
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
86 words
In a method of fabricating a PIN photodiode device having a body of intrinsic silicon semiconductor material with a resistivity in the range of 5,000 to 30,000 Ω-cm, a large incident surface area, and capable of operating in a reverse bias voltage in the range of 150 to 400 volts, the step of: doping said body with an N-type dopant source of a minimum dopant concentration of about 10 16 atoms per square centimeter without causing lattice damage to the surface of said PIN photodiode body.
Claim 2
Dependent Claim
86 words
In a method of fabricating a PIN photodiode device having a body of intrinsic silicon semiconductor material with a resistivity in the range of 5,000 to 30,000 Ω-cm, a large incident surface area, and capable of operating in a reverse bias voltage in the range of 150 to 400 volts, the step of: doping said body with an N-type dopant source of a minimum dopant concentration of about 10 16 atoms per square centimeter without causing lattice damage to the surface of said PIN photodiode body.
Claim 3
Dependent Claim
71 words
The method of fabricating a PIN photodiode device in accordance with claim 1, wherein said doping is performed by: growing a layer of phosphorus silicate glass on a surface of said body removing said layer of phosphorus silicate glass from said body; and diffusing into said body phosphorus which is in the surface of the body as a result of a chemical reaction of the phosphorus silicate glass with said body.
Claim 4
Dependent Claim
42 words
The method of fabricating a PIN photodiode device in accordance with claim 2 wherein the duration of time from when the layer of phosphorus silicate glass is first grown to the time it is removed is no more than about 12 minutes.
Claim 5
Dependent Claim
61 words
The method of fabricating a PIN photodiode device in accordance with claim 2 wherein the growing step is performed by bubbling oxygen gas, in the range of 60 to 90 cc/minute, through phosphorus oxychloride, said oxygen gas transporting the phosphorus oxychloride onto said body, which is in the range of 800° to 1000° C. for the growth of phosphorus silicate glass.
Claim 6
Dependent Claim
33 words
The method of fabricating a PIN photodiode device in accordance with claim 2 wherein the removing step is performed by placing said layer of phosphorus silicate glass in a buffered hydrofluoric acid solution.
Claim 7
Dependent Claim
41 words
The method of fabricating a PIN photodiode device in accordance with claim 2 wherein the diffusing step is performed by placing said body in a furnace for about 20 to 100 minutes in an oxygen ambient at 900° to 1050° C.
Claim 8
Dependent Claim
25 words
The method of fabricating a PIN photodiode device in accordance with claim 2, further comprising the step of: densifying said layer of phosphorus silicate glass.
Claim 9
Dependent Claim
35 words
The method of fabricating a PIN photodiode device in accordance with claim 7 wherein the densifying step is performed by passing a forming gas over said layer of phosphorus silicate glass for about 6 minutes.
Claim 10
Dependent Claim
35 words
The method of fabricating a PIN photodiode device in accordance with claim 7 wherein the densifying step is performed by passing an inert gas over said layer of phosphorus silicate glass for about 6 minutes.
Claim 11
Dependent Claim
28 words
The method of fabricating a PIN photodiode device in accordance with claim 1 wherein said doping is performed by: implanting N-type ions into a surface of said body.
Claim 12
Dependent Claim
38 words
The method of fabricating a PIN photodiode device in accordance with claim 10 wherein the implanting step is performed by impinging an ion beam in the range of 70 to 200 KeV onto a surface of said body.
Claim 13
Dependent Claim
19 words
The method of fabricating a PIN photodiode device in accordance with claim 11 wherein said N-type ions are arsenic.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-22 | 1980-08-23 | 1981-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-22 | 1984-08-23 | 1985-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-22 | 1988-08-23 | 1989-02-22 | $7700.00 | Window Closed / Lapsed |