Primary alkaline cell having a stable divalent silver oxide depolarizer mix
Assignee: Spectrum Brands Inc
•
Filing: 1976-03-15
•
Granted: 1977-02-22
•
Expires: 1996-03-15
Abstract
Abstract A primary alkaline cell having a stable divalent silver oxide depolarizer mix comprising a negative electrode (anode), a divalent silver oxide (AgO) depolarizer mix, a separator between said negative electrode and depolarizer mix, and an alkaline electrolyte. The surface of the depolarizer mix is treated with a mild reducing solution to form a reduced layer surrounding the mix, and the surface of the reduced layer adjacent to the separator is coated with a layer of silver. The reduced layer surrounding the depolarizer mix in combination with the layer of silver provides improved stability of the depolarizer mix in the alkaline electrolyte and a single voltage plateau during discharge of the cell. The primary alkaline cell is characterized by a maximum open circuit voltage of about 1.75 volts.
Inventors
- 👤 El Sayed Megahed
- 👤 Carol Ruth Buelow
- 👤 Patrick Joseph Spellman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:46
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/54; H01M4/06; H01M6/00; H01M6/04; H01M6/06; H01M6/12; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
107 words
A primary alkaline cell comprising a negative electrode, a divalent silver oxide depolarizer mix containing divalent silver oxide, a separator between said negative electrode and said divalent silver oxide depolarizer mix, and an aqueous alkaline electrolyte, said divalent silver oxide depolarizer mix being surrounded by a reduced layer formed by treating said depolarizer mix with a mild reducing solution, and a layer of silver on the surface of the reduced layer adjacent to the separator, whereby the cell is characterized by the stability of the depolarizer mix in the alkaline electrolyte, a maximum open circuit voltage of about 1.75 volts and a single voltage plateau during discharge.
Claim 2
Dependent Claim
107 words
A primary alkaline cell comprising a negative electrode, a divalent silver oxide depolarizer mix containing divalent silver oxide, a separator between said negative electrode and said divalent silver oxide depolarizer mix, and an aqueous alkaline electrolyte, said divalent silver oxide depolarizer mix being surrounded by a reduced layer formed by treating said depolarizer mix with a mild reducing solution, and a layer of silver on the surface of the reduced layer adjacent to the separator, whereby the cell is characterized by the stability of the depolarizer mix in the alkaline electrolyte, a maximum open circuit voltage of about 1.75 volts and a single voltage plateau during discharge.
Claim 3
Dependent Claim
46 words
A primary alkaline cell in accordance with claim 1 in which the silver layer is substantially continuous and electrolyte permeable having been formed by treating the depolarizer mix with the reduced layer with a strong reducing agent capable of reducing the reduced layer to metallic silver.
Claim 4
Dependent Claim
25 words
A primary alkaline cell in accordance with claim 1 in which the depolarizer mix contains at least about 50% by weight of divalent silver oxide.
Claim 5
Dependent Claim
47 words
A primary alkaline cell in accordance with claim 2 in which the silver layer is only on the surface of the reduced layer adjacent to the separator having been formed by treating the depolarizer mix with the reduced layer after it is placed in a cathode container.
Claim 6
Dependent Claim
25 words
A primary alkaline cell in accordance with claim 2 in which the depolarizer mix contains at least about 50% by weight of divalent silver oxide.
Claim 7
Dependent Claim
41 words
A primary alkaline cell in accordance with claim 4 in which the alkaline electrolyte is an aqueous solution of potassium hydroxide having a concentration ranging from at least about 3% by weight up to about 50% by weight of potassium hydroxide.
Claim 8
Dependent Claim
41 words
A primary alkaline cell in accordance with claim 5 in which the alkaline electrolyte is an aqueous solution of potassium hydroxide having a concentration ranging from at least about 3% by weight up to about 50% by weight of potassium hydroxide.
Claim 9
Dependent Claim
120 words
A primary alkaline cell comprising a negative electrode, a divalent silver oxide depolarizer mix containing divalent silver oxide, a separator between said negative electrode and said divalent silver oxide depolarizer mix, and an aqueous alkaline electrolyte, said divalent silver oxide depolarizer mix having a reduced layer on its top surface near the separator formed by treating the depolarizer mix with a mild reducing solution after it is placed in a cathode container, and a layer of silver on the surface of the reduced layer adjacent to the separator, whereby the cell is characterized by the stability of the depolarizer mix in the alkaline electrolyte, a maximum open circuit voltage of about 1.75 volts and a single voltage plateau during discharge.
Claim 10
Dependent Claim
120 words
A primary alkaline cell comprising a negative electrode, a divalent silver oxide depolarizer mix containing divalent silver oxide, a separator between said negative electrode and said divalent silver oxide depolarizer mix, and an aqueous alkaline electrolyte, said divalent silver oxide depolarizer mix having a reduced layer on its top surface near the separator formed by treating the depolarizer mix with a mild reducing solution after it is placed in a cathode container, and a layer of silver on the surface of the reduced layer adjacent to the separator, whereby the cell is characterized by the stability of the depolarizer mix in the alkaline electrolyte, a maximum open circuit voltage of about 1.75 volts and a single voltage plateau during discharge.
Claim 11
Dependent Claim
46 words
A primary alkaline cell in accordance with claim 8 in which the silver layer is substantially continuous and electrolyte permeable having been formed by treating the depolarizer mix with the reduced layer with a strong reducing agent capable of reducing the reduced layer to metallic silver.
Claim 12
Dependent Claim
25 words
A primary alkaline cell in accordance with claim 9 in which the depolarizer mix contains up to about 70% by weight of divalent silver oxide.
Claim 13
Dependent Claim
112 words
A primary alkaline cell comprising a zinc negative electrode, a divalent silver oxide depolarizer mix containing divalent silver oxide and a polymeric binder, a separator between said zinc electrode and said divalent silver oxide depolarizer mix, and an aqueous alkaline electrolyte, said divalent silver oxide depolarizer mix being surrounded by a reduced layer formed by treating said depolarizer mix with a mild reducing solution, and a layer of silver on the surface of the reduced layer adjacent to the separator, whereby the cell is characterized by the stability of the depolarizer mix in the alkaline electrolyte, a maximum open circuit voltage of about 1.75 volts and a single voltage plateau during discharge.
Claim 14
Dependent Claim
112 words
A primary alkaline cell comprising a zinc negative electrode, a divalent silver oxide depolarizer mix containing divalent silver oxide and a polymeric binder, a separator between said zinc electrode and said divalent silver oxide depolarizer mix, and an aqueous alkaline electrolyte, said divalent silver oxide depolarizer mix being surrounded by a reduced layer formed by treating said depolarizer mix with a mild reducing solution, and a layer of silver on the surface of the reduced layer adjacent to the separator, whereby the cell is characterized by the stability of the depolarizer mix in the alkaline electrolyte, a maximum open circuit voltage of about 1.75 volts and a single voltage plateau during discharge.
Claim 15
Dependent Claim
46 words
A primary alkaline cell in accordance with claim 11 in which the silver layer is substantially continuous and electrolyte permeable having been formed by treating the depolarizer mix with the reduced layer with a strong reducing agent capable of reducing the reduced layer to metallic silver.
Claim 16
Dependent Claim
27 words
A primary alkaline cell in accordance with claim 12 in which the silver layer is only on the surface of the reduced layer adjacent to the separator.
Claim 17
Dependent Claim
25 words
A primary alkaline cell in accordance with claim 13 in which the depolarizer mix contains at least about 50% by weight of divalent silver oxide.
Claim 18
Dependent Claim
29 words
A primary alkaline cell in accordance with claim 14 in which the alkaline electrolyte has a concentration ranging from about 3% by weight up to about 50% by weight.
Claim 19
Dependent Claim
21 words
A primary alkaline cell in accordance with claim 15 in which the alkaline electrolyte is an aqueous solution of potassium hydroxide.
Claim 20
Dependent Claim
27 words
A primary alkaline cell in accordance with claim 16 in which the polymeric binder is polytetrafluoroethylene and the separator comprises an absorbent component and a barrier material.
Claim 21
Dependent Claim
27 words
A primary alkaline cell in accordance with claim 17 in which the barrier material comprises a layer of polyethylene grafted with methacrylic acid between layers of cellophane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-22 | 1980-08-23 | 1981-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-22 | 1984-08-23 | 1985-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-22 | 1988-08-23 | 1989-02-22 | $7700.00 | Window Closed / Lapsed |