Process for the production of nonwoven cellulose acetate laminate cured with phenolic resin
Assignee: Daicel Corp
•
Filing: 1975-01-22
•
Granted: 1977-02-15
•
Expires: 1995-01-22
Abstract
Abstract A nonwoven cellulose acetate laminate is made from a base material mainly composed of a cellulose acetate fiber web, in a short time, by the steps of: impregnating a liquid initial condensate of phenol-formaldehyde into the web or spraying a powdery condensate of phenol-formaldehyde onto the web, and then penetrating superheated steam through the resultant cellulose acetate laminate sheet. The sheet possesses good mechanical properties and excellent sound-absorbing and heat-insulating characteristics.
Inventors
- 👤 Katsuharu Arisaka
- 👤 Hideo Sawada
- 👤 Kozo Shimoguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:19
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/40; D04H1/58; D04H1/64; D04H1/42; D04H1/425; D04H1/4258; D04H1/587
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
212 words
A process for manufacturing a molded article made of a non-woven cellulose acetate fiber web, which consists essentially of the steps of: a. impregnating substantially uniformly a nonwoven web of fibers consisting essentially of from 50 to 100 weight percent of cellulose acetate fibers, the balance being another fiber selected from the group consisting of polyvinyl chloride fibers, polyethylene glycol terephthalate fibers, polyacrylonitrile fibers and mixtures thereof, with a liquid composition consisting of 35 to 100 weight percent of liquid resol resin, the balance being a plasticizer for cellulose acetate, said impregnated web containing from 5 to 40 weight percent of said liquid resol, based on the total weight of the impregnated web; b. placing said web between molding surfaces defining a mold cavity; c. pressing said web to conform same to the shape of said cavity; d. injecting, simultaneously with step (c), superheated steam at a pressure of from 0.05 to 3.0 kg/cm 2 and a temperature of from 80° to 150° C through said web at a rate that is effective to prevent condensation of water in said web and for a period of time effective to cure said resol resin; e. terminating the injection of said steam; and f. removing the cured cellulose acetate fiber web from said mold.
Claim 2
Dependent Claim
212 words
A process for manufacturing a molded article made of a non-woven cellulose acetate fiber web, which consists essentially of the steps of: a. impregnating substantially uniformly a nonwoven web of fibers consisting essentially of from 50 to 100 weight percent of cellulose acetate fibers, the balance being another fiber selected from the group consisting of polyvinyl chloride fibers, polyethylene glycol terephthalate fibers, polyacrylonitrile fibers and mixtures thereof, with a liquid composition consisting of 35 to 100 weight percent of liquid resol resin, the balance being a plasticizer for cellulose acetate, said impregnated web containing from 5 to 40 weight percent of said liquid resol, based on the total weight of the impregnated web; b. placing said web between molding surfaces defining a mold cavity; c. pressing said web to conform same to the shape of said cavity; d. injecting, simultaneously with step (c), superheated steam at a pressure of from 0.05 to 3.0 kg/cm 2 and a temperature of from 80° to 150° C through said web at a rate that is effective to prevent condensation of water in said web and for a period of time effective to cure said resol resin; e. terminating the injection of said steam; and f. removing the cured cellulose acetate fiber web from said mold.
Claim 3
Dependent Claim
26 words
A process in accordance with claim 1 wherein said cellulose acetate fibers have an acetyl value of 38 to 41 percent and are soluble in acetone.
Claim 4
Dependent Claim
30 words
A process in accordance with claim 1 wherein the liquid composition consists of from 35 to 98 weight percent of said liquid resol resin and the balance is said plasticizer.
Claim 5
Dependent Claim
26 words
A process in accordance with claim 3 in which said plasticizer is selected from the group consisting of phthalic acid esters and fire retardant phosphoric esters.
Claim 6
Dependent Claim
31 words
A process in accordance with claim 4 in which said plasticizer is selected from the group consisting of dimethyl phthalate, dibutyl phthalate, dioctyl phthalate, tris(β-monochloroethyl) phosphate, tris(2,3-dichloropropyl) phosphate and tris(2,3-dibromopropyl phosphate.
Claim 7
Dependent Claim
196 words
A process for manufacturing a molded article made of a non-woven cellulose acetate fiber web, which consists essentially of the steps of: a. impregnating substantially uniformly a nonwoven web of fibers consisting essentially of from 50 to 100 weight percent of cellulose acetate fibers, the balance being another fiber selected from the group consisting of polyvinyl chloride fibers, polyethylene glycol terephthalate fibers, polyacrylonitrile fibers and mixtures thereof, with a powder of a novolak resin, said impregnated web containing from 5 to 40 weight percent of said novolak resin, based on the total weight of said impregnated web; b. placing said web between molding surfaces defining a mold cavity; c. pressing said web to conform same to the shape of said cavity; d. injecting, simultaneously with step c., superheated steam at a pressure of from 0.05 to 3.0 kg/cm 2 and a temperature of from 80° to 150° C through said web at a rate that is effective to prevent condensation of water in said web and for a period of time effective to cure said novolak resin; e. terminating the injection of said steam; and f. removing the cured cellulose acetate fiber web from said mold.
Claim 8
Dependent Claim
196 words
A process for manufacturing a molded article made of a non-woven cellulose acetate fiber web, which consists essentially of the steps of: a. impregnating substantially uniformly a nonwoven web of fibers consisting essentially of from 50 to 100 weight percent of cellulose acetate fibers, the balance being another fiber selected from the group consisting of polyvinyl chloride fibers, polyethylene glycol terephthalate fibers, polyacrylonitrile fibers and mixtures thereof, with a powder of a novolak resin, said impregnated web containing from 5 to 40 weight percent of said novolak resin, based on the total weight of said impregnated web; b. placing said web between molding surfaces defining a mold cavity; c. pressing said web to conform same to the shape of said cavity; d. injecting, simultaneously with step c., superheated steam at a pressure of from 0.05 to 3.0 kg/cm 2 and a temperature of from 80° to 150° C through said web at a rate that is effective to prevent condensation of water in said web and for a period of time effective to cure said novolak resin; e. terminating the injection of said steam; and f. removing the cured cellulose acetate fiber web from said mold.
Claim 9
Dependent Claim
27 words
A process in accordance with claim 6 wherein said cellulose acetate fibers have an acetyl value of from 38 to 41 percent and are soluble in acetone.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-15 | 1980-08-16 | 1981-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-15 | 1984-08-16 | 1985-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-15 | 1988-08-16 | 1989-02-15 | $7700.00 | Window Closed / Lapsed |