Shaped heat insulating articles

Claim 2

In a shaped heat insulating article for forming a molten-metal contacting lining for metallurgical moulds or the like which comprises a refractory composite having a high infra-red radiation opacity and consisting essentially of an inorganic fibrous refractory material and a granular refractory filler material, an exothermic mixture of a fuel and an oxidising agent, and a binder; the improvement wherein said fibrous refractory material is a material selected from the group consisting essentially of aluminosilicate, zircon and alumina fibres and said shaped article has a density of about 0.25 to 0.55 grams per cubic centimeter.

Claim 3

A shaped heat insulating article according to claim 1 wherein the binder comprises an organic binder and an inorganic binder.

Claim 4

A shaped heat insulating article according to claim 2 wherein the organic binder is a material selected from the group consisting essentially of phenolic resins, furan resins and starch and the inorganic binder is a material selected from the group consisting essentially of colloidal silica sol, colloidal alumina, and mono aluminium orthophosphate.

Claim 5

A shaped heat insulating article according to claim 1 comprising a fluoride catalyst for the exothermic mixture.

Claim 6

A shaped heat insulating article according to claim 4 wherein the fluoride catalyst is selected from the group consisting essentially of cryolite, fluorspar and sodium silico-fluoride.

Claim 7

A shaped heat insulating article according to claim 1 preceding claims comprising the following composition by weight: ______________________________________ Refractory material 20 to 80% Fuel 10 to 40% Oxidising agent 0.2 to 20% Fluoride catalyst 0.1 to 20% Colloidal silica sol 0 to 20% Organic binder 0 to 10% The organic binder and colloidal silica sol having a combined proportion in the range of 2 to 30%. ______________________________________ The organic binder and colloidal silica sol having a combined proportion in the range of 2 to 30%.

Claim 8

A shaped heat insulating article according to claim 6 comprising the following composition by weight: ______________________________________ Refractory material 50 to 67.5% Fuel 12.5 to 30% Oxidising agent 2 to 4% Colloidal silica sol 2 to 15% Organic binder 5 to 8.5% ______________________________________

Claim 9

A shaped heat insulating article according to claim 1 wherein the density thereof lies in the range of 0.28 to 0.35 grams per cubic centimeter.

Claim 10

A shaped heat insulating article according to claim 8 wherein the density thereof lies in the range of 0.32 to 0.34 grams per cubic centimeter.

Claim 11

The article defined in claim 1, wherein said granular material is one or more materials selected from the group consisting essentially of alumina, magnesia, chromite, titania and zirconia.

Claim 12

The article defined in claim 1, wherein the fuel is one or more materials selected from the group consisting essentially of aluminum, ferro-silicon, magnesium and zirconium powders.

Claim 13

The article defined in claim 11, wherein the oxidising agent is one or more materials selected from the group consisting essentially of barium sulfate, iron oxide, manganese dioxide and barium nitrate.