Process for the production of tungsten carbide or mixed metal carbides
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1975-09-02
•
Granted: 1977-02-15
•
Expires: 1995-09-02
Abstract
Abstract A process for the production of tungsten carbide or mixed metal carbides, which comprises mixing tungsten oxide powder of mixed high melting point metal oxide powders with carbon powder in an amount sufficient to form the corresponding carbide, heating the mixture at a temperature of higher than 1000 DEG C in an inert atmosphere or in vacuum to reduce the oxygen content and then heating at a temperature of higher than 1400 DEG C in hydrogen atmosphere, thereby to form tungsten carbide or mixed metal carbides directly from the corresponding oxide.
Inventors
- 👤 Masaya Miyake
- 👤 Akio Hara
- 👤 Noriyuki Ayano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:13
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/5626; C01; C01B; C01B32/00; C01B32/90; C01B32/907; C01B32/914; C01B32/949; C04B35/5611; C04B35/622; C04B35/64; C04B35/65; C01P; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/80; C01P2004/82; C01P2004/84; C01P2006/00; C01P2006/60; C01P2006/80; C01P2006/90
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
110 words
A process for the production of tungsten carbide, which consists essentially of mixing tungsten oxide powder with three to four equivalents of carbon powder, subjecting the resulting mixture to pelletization, heating the pelletized mixture under movement in a rotary furnace at a temperature of from 1000° to 1600° C in a nitrogen or argon atmosphere to reduce the oxygen content of the oxide to less than 0.5% and then heating the intermediate product under movement in a rotary furnace at a temperature of from 1400° C to 2000° C in a hydrogen atmosphere, the temperature of the second heating being about 200° C higher than that of the first heating.
Claim 2
Dependent Claim
110 words
A process for the production of tungsten carbide, which consists essentially of mixing tungsten oxide powder with three to four equivalents of carbon powder, subjecting the resulting mixture to pelletization, heating the pelletized mixture under movement in a rotary furnace at a temperature of from 1000° to 1600° C in a nitrogen or argon atmosphere to reduce the oxygen content of the oxide to less than 0.5% and then heating the intermediate product under movement in a rotary furnace at a temperature of from 1400° C to 2000° C in a hydrogen atmosphere, the temperature of the second heating being about 200° C higher than that of the first heating.
Claim 3
Dependent Claim
26 words
The process of claim 1 wherein the tungsten oxide is formed in situ by first mixing the carbon with tungsten compounds which oxidize during the reaction.
Claim 4
Dependent Claim
23 words
The process of claim 2 wherein at least one compound selected from the group consisting of tungstic acid and ammonium paratungstate is used.
Claim 5
Dependent Claim
151 words
A process for the production of tungsten carbide containing-mixed metal carbides selected from the group consisting of titanium carbide, tantalum carbide, columbium carbide and mixtures thereof, which consists essentially of mixing tungsten oxide powder-containing high melting point metal oxide powders selected from the group consisting of titanium oxides, tantalum oxides, columbium oxides and mixtures thereof, with carbon power in an amount sufficient to give the theoretical quantity of combined carbon, subjecting the resulting mixture to pelletization, heating the pelletized mixture under movement in a rotary furnace at a temperature of from 1000° to 1600° C in nitrogen to reduce the oxygen content of the oxide to less than 5% and then heating the intermediate product under movement in a rotary furnace at a temperature of from 1600° to 2000° C in a hydrogen atmosphere, the temperature of the second heating being about 200° C higher than that of the first heating.
Claim 6
Dependent Claim
151 words
A process for the production of tungsten carbide containing-mixed metal carbides selected from the group consisting of titanium carbide, tantalum carbide, columbium carbide and mixtures thereof, which consists essentially of mixing tungsten oxide powder-containing high melting point metal oxide powders selected from the group consisting of titanium oxides, tantalum oxides, columbium oxides and mixtures thereof, with carbon power in an amount sufficient to give the theoretical quantity of combined carbon, subjecting the resulting mixture to pelletization, heating the pelletized mixture under movement in a rotary furnace at a temperature of from 1000° to 1600° C in nitrogen to reduce the oxygen content of the oxide to less than 5% and then heating the intermediate product under movement in a rotary furnace at a temperature of from 1600° to 2000° C in a hydrogen atmosphere, the temperature of the second heating being about 200° C higher than that of the first heating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-15 | 1980-08-16 | 1981-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-15 | 1984-08-16 | 1985-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-15 | 1988-08-16 | 1989-02-15 | $7700.00 | Window Closed / Lapsed |