US4007055A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Preparation of stoichiometric titanium disulfide
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1975-05-09
•
Granted: 1977-02-08
•
Expires: 1995-05-09
Abstract
Abstract Stoichiometric titanium disulfide having a high degree of crystalline perfection and particularly suited for use as an active cathode material is prepared by heating particulate metallic titanium to a reaction temperature between about 475° and 600° C., contacting the heated titanium with an atmosphere having a sulfur partial pressure substantially equal to the equilibrium sulfur partial pressure at the reaction temperature to form titanium disulfide, and maintaining the reactants at the reaction temperature sufficiently to insure complete reaction. The reaction is advantageously conducted in an evacuated tube which is differentially heated to establish a hot zone where the reaction occurs and a cooler zone which controls the sulfur partial pressure within the tube so that the rate of reaction can in turn be controlled to minimize overheating, and also prevents the formation of titanium trisulfide.
Inventors
- 👤 M. Stanley Whittingham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:07
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/05; C; C01; C01G; C01G23/00; C01G23/007; H01M4/00; H01M4/02; H01M4/36; H01M4/58; H01M4/581; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/81; Y10S505/815; Y10S505/824
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
87 words
A process for producing stoichiometric titanium disulfide and having a small aspect ratio which comprises heating particulate titanium to a reaction temperature of between about 475° C. and about 600° C. and contacting the heated titanium with an atmosphere having a sulfur partial pressure substantially equal to the equilibrium sulfur partial pressure over titanium disulfide at the reaction temperature to form titanium disulfide, said titanium and sulfur being used in substantially stoichiometric amounts, and holding the heated titanium at the reaction temperature to homogenize the titanium disulfide.
Claim 2
Dependent Claim
87 words
A process for producing stoichiometric titanium disulfide and having a small aspect ratio which comprises heating particulate titanium to a reaction temperature of between about 475° C. and about 600° C. and contacting the heated titanium with an atmosphere having a sulfur partial pressure substantially equal to the equilibrium sulfur partial pressure over titanium disulfide at the reaction temperature to form titanium disulfide, said titanium and sulfur being used in substantially stoichiometric amounts, and holding the heated titanium at the reaction temperature to homogenize the titanium disulfide.
Claim 3
Dependent Claim
14 words
The process as described in claim 1 wherein the particulate titanium is titanium sponge.
Claim 4
Dependent Claim
28 words
The process as described in claim 1 wherein the particulate titanium has a particle size distribution of about 100% minus 4 mesh and about 100% plus 40 mesh.
Claim 5
Dependent Claim
24 words
The process as described in claim 1 wherein the heated titanium is contacted incrementally with sulfur to minimize temperature increases above the reaction temperature.
Claim 6
Dependent Claim
94 words
The process as described in claim 1 wherein substantially stoichiometric amounts of elemental sulfur and particulate titanium are placed in an elongated reaction vessel which is evacuated and differentially heated to establish a hot zone that is heated to the reaction temperature and a cold zone that is maintained at a temperature between about 50° and about 300° C. cooler than the hot zone so that sulfur partial pressure can be controlled which in turn controls the rate of reaction between the titanium and the sulfur so that the reaction temperature can be controlled.
Claim 7
Dependent Claim
53 words
The process as described in claim 1 wherein the titanium and sulfur are placed in separate interconnected vessels and the vessel containing the titanium is heated to the reaction temperature while the temperature of the vessel holding the sulfur is controlled to maintain the sulfur partial pressure in the vessel containing the titanium.
Claim 8
Dependent Claim
32 words
The process as described in claim 5 wherein the hot zone is gradually heated from about 350° C. to the reaction temperature at a rate between about 10° C./hr. and 100° C./hr.
Claim 9
Dependent Claim
19 words
The process as described in claim 7 wherein the reaction temperature is between about 500° C. and 550° C.
References Cited (Backward Citations)
US3079229A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-08 | 1980-08-09 | 1981-02-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-08 | 1984-08-09 | 1985-02-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-08 | 1988-08-09 | 1989-02-08 | $7700.00 | Window Closed / Lapsed |